Extrusion & Blow Molding

PP resin (TAIRIPRO® PP resin) using the state of art Gas-Phase processing technologies granted by Chisso, Japan, the high efficient catalyst and the comprehensive quality control system, its yearly capacity is 510,000MTS. The Tairipro product classification contains homo polymer, random and impact copolymer which can be processed by injection, extrusion, blow and vacuum thermoforming. Their application is versatile and adopted in the field of home appliance, AUTO parts, food packages, toys and daily necessities. The R&D center & the full range pilot plant well equipped will be supportive of our new grade development and the setup of the relevant processing guide as well. All production facilities are operated in accordance with strict environmental protection regulation, and waste gases treated by high-heat combustion, then heat recovered. No waste water arises in the polymerization process.

Storage and Validity suggestion

ISO 9001

ISO 14001

TAF ISO IEC 17025_2017_EN

TAF ISO IEC 17025_2017_ZN-TW

Extrusion & Blow Molding

Model

Applications

Physical

Features

Attach

Operating

B1101

Homopolymer PP RESIN

Extrusion & Blow Molding

Thermoforming Sheet, PP-H pipe, Tray, Blow molding

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238

		0.5	230℃ × 2.16kg	g/10 min




IZOD Impact Strength	ASTM D-256
		7	23 ℃，1/8"，Notched	kg-cm/cm
		7	23 ℃，4mm，Notched	kg-cm/cm











Specific Gravity	ASTM D-792
		0.9	23℃/23℃	-

Tensile Strength	ASTM D-638
		360	23 ℃，50mm/min	kg/cm²
		0	23 ℃	kg/cm²

Tensile Elongation at break	ASTM D-638	>200	23 ℃，50mm/min	%
Tensile Elongation at break	ASTM D-638
Flexural Modulus	ASTM D-790

		14500	23 ℃	kg/cm²

Rockwell Hardness	ASTM D-785	R-102	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648




		110	Unannealed，1/4" bar	℃





Molding Shrinkage	FCFC Method	1.5 ~ 1.9	23 ℃	%
Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133





		0.5	230℃ × 2.16kg	g/10 min

IZOD Impact Strength	ISO 180
		69	23 ℃，1/8"，Notched	kJ/m²
		69	23 ℃，4mm，Notched	kJ/m²





Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	0.9	23℃/23℃	-
Tensile Strength	ISO 527	35	23 ℃，50mm/min	Mpa


Tensile Elongation at break	ISO 527	>200	23 ℃，50mm/min	%
Flexural Modulus	ISO 178
Flexural Modulus	ISO 178	1421	23 ℃	Mpa
Rockwell Hardness	ISO 2039-2	R-102	23℃	R-scale
Heat Deflection Temperature	ISO 75/A

		110	Unannealed，0.455Mpa 1/4" 厚，120℃/h	℃





Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

Excellent melt strength,
Deep drawing

T1002

Homopolymer PP RESIN

Extrusion & Blow Molding

Corrugated sheet, Strapping, Bottles

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238

		1.7	230℃ × 2.16kg	g/10 min




IZOD Impact Strength	ASTM D-256
		5	23 ℃，1/8"，Notched	kg-cm/cm
		5	23 ℃，4mm，Notched	kg-cm/cm











Specific Gravity	ASTM D-792
		0.9	23℃/23℃	-

Tensile Strength	ASTM D-638
		360	23 ℃，50mm/min	kg/cm²


Tensile Elongation at break	ASTM D-638	>200	23 ℃，50mm/min	%
Tensile Elongation at break	ASTM D-638
Flexural Strength	ASTM D-790
		0	23 ℃, 2mm/min	kg/cm²


Flexural Modulus	ASTM D-790

		15000	23 ℃	kg/cm²

Rockwell Hardness	ASTM D-785	R-100	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648




		110	Unannealed，1/4" bar	℃





Molding Shrinkage	FCFC Method	1.5 ~ 1.9	23 ℃	%
Flammability	UL-94	1.5-1.65mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94	HB 1.5 ~ 1.65 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133





		1.7	230℃ × 2.16kg	g/10 min

IZOD Impact Strength	ISO 180
		49	23 ℃，1/8"，Notched	kJ/m²
		49	23 ℃，4mm，Notched	kJ/m²





Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	0.9	23℃/23℃	-
Tensile Strength	ISO 527	35	23 ℃，50mm/min	Mpa


Tensile Elongation at break	ISO 527	>200	23 ℃，50mm/min	%
Flexural Modulus	ISO 178
Flexural Modulus	ISO 178	1470	23 ℃	Mpa
Rockwell Hardness	ISO 2039-2	R-100	23℃	R-scale
Heat Deflection Temperature	ISO 75/A

		110	Unannealed，0.455Mpa 1/4" 厚，120℃/h	℃





Molding Shrinkage	FCFC Method	1.5 ~ 1.9	23 ℃	%
Combustibility	UL-94	HB 1.5 ~ 1.65 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

Excellent tensile strength

T1202

Homopolymer PP RESIN

Extrusion & Blow Molding

Blow molding

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238

		1.6	230℃ × 2.16kg	g/10 min




IZOD Impact Strength	ASTM D-256
		4.5	23 ℃，1/8"，Notched	kg-cm/cm
		4.5	23 ℃，4mm，Notched	kg-cm/cm











Specific Gravity	ASTM D-792
		0.9	23℃/23℃	-

Tensile Strength	ASTM D-638

		380	23 ℃	kg/cm²

Tensile Elongation at break	ASTM D-638	>200	23 ℃，50mm/min	%
Tensile Elongation at break	ASTM D-638
Flexural Modulus	ASTM D-790

		18000	23 ℃	kg/cm²

Rockwell Hardness	ASTM D-785	R-108	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648




		135	Unannealed，1/4" bar	℃





Molding Shrinkage	FCFC Method	1.5 ~ 1.9	23 ℃	%
Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133





		1.6	230℃ × 2.16kg	g/10 min

IZOD Impact Strength	ISO 180
		44	23 ℃，1/8"，Notched	kJ/m²
		44	23 ℃，4mm，Notched	kJ/m²





Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

high stiffness, heat resistance, clarity

MI(230℃×2.16kg):1.6

Izod(ASTM,1/8"):4.5

FM(ASTM):18000

TS(ASTM):380

T2502

Homopolymer PP RESIN

Extrusion & Blow Molding

Transparency pressure forming sheet,Portfolio, Bottles

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238

		1.8	230℃ × 2.16kg	g/10 min




IZOD Impact Strength	ASTM D-256
		6	23 ℃，1/8"，Notched	kg-cm/cm
		6	23 ℃，4mm，Notched	kg-cm/cm











Specific Gravity	ASTM D-792
		0.9	23℃/23℃	-

Tensile Strength	ASTM D-638
		360	23 ℃，50mm/min	kg/cm²


Tensile Elongation at break	ASTM D-638	>200	23 ℃，50mm/min	%
Tensile Elongation at break	ASTM D-638
Flexural Modulus	ASTM D-790

		15500	23 ℃	kg/cm²

Rockwell Hardness	ASTM D-785	R-100	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648




		117	Unannealed，1/4" bar	℃





Molding Shrinkage	FCFC Method	1.5 ~ 1.9	23 ℃	%
Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133





		1.8	230℃ × 2.16kg	g/10 min

IZOD Impact Strength	ISO 180
		59	23 ℃，1/8"，Notched	kJ/m²
		59	23 ℃，4mm，Notched	kJ/m²





Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	0.9	23℃/23℃	-
Tensile Strength	ISO 527	35	23 ℃，50mm/min	Mpa


Tensile Elongation at break	ISO 527	>200	23 ℃，50mm/min	%
Flexural Modulus	ISO 178
Flexural Modulus	ISO 178	1519	23 ℃	Mpa
Rockwell Hardness	ISO 2039-2	R-100	23℃	R-scale
Heat Deflection Temperature	ISO 75/A

		117	Unannealed，0.455Mpa 1/4" 厚，120℃/h	℃





Molding Shrinkage	FCFC Method	1.5 ~ 1.9	23 ℃	%
Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

High stiffiness, Good transparency, Good heat resistance