K3029
Impact Copolymer PP RESIN
Injection Molding Grade
Bumper, Automotive parts, Thin wall products
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 15 23 ℃，1/8"，Notched kg-cm/cm
7 -20℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 210 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >100 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 10000 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-75 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 108 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Flammability
UL-94 1.5mm HB
3.0mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 32 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 69 0℉，4mm，Notched kJ/m²
147 73℉，1/8"，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 21 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >100 23 ℃，50mm/min %
Flexural Modulus
ISO 178 980 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-75 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 108 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
High fluidity, High impact strength
Please choose
K7005AG
Impact Copolymer PP RESIN
Injection Molding Grade
Automotive parts, Furniture,Appliances, Pallet , Crate containers
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 40 23 ℃，1/8"，Notched kg-cm/cm
-20℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 270 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 14000 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-93 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 120 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Flammability
UL-94 1.5mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 5 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 4.9 0℉，4mm，Notched kJ/m²
392 73℉，1/8"，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 26 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1372 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-93 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 120 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
HB 1.5 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
Hight impact strength, High Stiffness, Goog light stability
Please choose
K7005AN
Impact Copolymer PP RESIN
Injection Molding Grade
Automotive parts, Furniture,Appliances
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 40 23 ℃，1/8"，Notched kg-cm/cm
-20℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 270 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 14000 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-93 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 120 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Flammability
UL-94 1.5mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 5 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 49 0℉，4mm，Notched kJ/m²
392 73℉，1/8"，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 26 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1372 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-93 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 120 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
HB 1.5 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
Hight impact strength, High Stiffness
Please choose
K8003
Baby-car parts, Paint drum,Sport appliances, Base of Luggage
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 25 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 2.6 23℃ 1/8"bar kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 343 23 ℃ kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23℃ %
Flexural Modulus
ASTM D-790 14500 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-100 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 110 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.52 ~
23 ℃ %
Combustibility
UL-94
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Combustibility
UL-94
File No. E162823
-
To print, please click on the attached standard physical properties table.
Hight impact strength, Good Stiffness
Please choose
K7009
Impact Copolymer PP RESIN
Injection Molding Grade
Automotive parts, Furniture,Appliances
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 11 23 ℃，1/8"，Notched kg-cm/cm
4.6 -20℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 260 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 13500 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-94 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 120 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Flammability
UL-94 1.5mm HB
3.0mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 9 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 45 0℉，4mm，Notched kJ/m²
108 73℉，1/8"，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 25 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1323 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-94 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 120 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
High stiffness,Good impact strength
Please choose
K8003
Baby-car parts, Paint drum,Sport appliances, Base of Luggage
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 31-37 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 4.0 23℃ 1/8"bar kg-cm/cm
4.0(38) 23℃ 1/8"bar kg-cm/cm (J/m)
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Elongation at break
ASTM D-638 >200 23℃ %
Flexural Modulus
ASTM D-790 18000 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-105 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 125 Unannealed，1/4" bar ℃
Molding Shrinkage
ASTM D-955 1.4 ~
1.8 23℃ ％
Tensile Strength at Yield
ASTM D-638 380(37) 23℃ kg/cm2 (Mpa)
Combustibility
UL-94
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Combustibility
UL-94
File No. E162823
-
To print, please click on the attached standard physical properties table.
Hight impact strength, Good Stiffness
Please choose
K7009AH
Impact Copolymer PP RESIN
Injection Molding Grade
Electric appliance parts, Automotive parts,RTI=125℃
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 11 23 ℃，1/8"，Notched kg-cm/cm
4.6 -20℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 260 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 13500 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-94 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 120 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Flammability
UL-94 1.5mm HB
3.0mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 9 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 45 0℉，4mm，Notched kJ/m²
108 73℉，1/8"，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 25 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1323 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-94 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 120 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
Long term thermal aging, High stiffness, Good impact strength
Please choose
K7025
Impact Copolymer PP RESIN
Injection Molding Grade
Washing machine cylinder, Appliances
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 8 23 ℃，1/8"，Notched kg-cm/cm
4.5 -20℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 270 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 14000 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-93 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 120 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Flammability
UL-94 1.5mm HB
3.0mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 27 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 44 0℉，4mm，Notched kJ/m²
78 73℉，1/8"，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 26 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1372 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-93 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 120 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
High fluidity, High impact strength,
Please choose
K8003
Impact Copolymer PP RESIN
Injection Molding Grade
Baby-car parts, Paint drum,Sport appliances, Base of Luggage
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 60 23 ℃，1/8"，Notched kg-cm/cm
9.5 -20℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 260 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 11000 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-80 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 110 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Flammability
UL-94 1.5mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 3 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 93 0℉，4mm，Notched kJ/m²
588 73℉，1/8"，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 25 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1078 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-80 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 110 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
HB 1.5 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
Hight impact strength, Good Stiffness
Please choose
K8003AN
Impact Copolymer PP RESIN
Injection Molding Grade
Paint drum,Sport appliances, Base of Luggage
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 60 23 ℃，1/8"，Notched kg-cm/cm
9 -20℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 260 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 12000 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-83 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 115 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Flammability
UL-94 1.5mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Combustibility
UL-94
HB 1.5 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
Excellent impact strength, High stiffness, Excellent anti-static
Please choose
K8009
Impact Copolymer PP RESIN
Injection Molding Grade
Automotive parts, Battery case,Electrical appliances, Furniture
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 40 23 ℃，1/8"，Notched kg-cm/cm
7.4 -20℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 230 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 11000 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-80 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 110 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Flammability
UL-94 1.5mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 9 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 73 0℉，4mm，Notched kJ/m²
392 73℉，1/8"，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 22 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1078 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-80 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 110 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
HB 1.5 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
High impact strength, Good fluidity
Please choose
K8009
Automotive parts, Battery case,Electrical appliances, Furniture
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 9 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 40 23 ℃，1/8"，Notched kg-cm/cm
7.4 -20℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 230 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 11000 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-80 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 110 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Flammability
UL-94 1.5mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 9 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 73 0℉，4mm，Notched kJ/m²
392 73℉，1/8"，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 22 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1078 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-80 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 110 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
File No. E162823
-
To print, please click on the attached standard physical properties table.
High impact strength, Good fluidity
Please choose
K8025
Impact Copolymer PP RESIN
Injection Molding Grade
Automotive parts, Washing machine parts, Tool boxes,
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 25 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 12.5 23 ℃，1/8"，Notched kg-cm/cm
6.2 -20℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 230 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 11000 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-80 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 110 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Flammability
UL-94 1.5mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 28 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 61 0℉，4mm，Notched kJ/m²
123 73℉，1/8"，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 22 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1078 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-80 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 110 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
HB 1.5 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
High impact strength, High fluidity
Please choose
K8025
Automotive parts, Washing machine parts, Tool boxes,
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 25 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 12.5 23 ℃，1/8"，Notched kg-cm/cm
6.2 -20℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 230 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Rockwell Hardness
ASTM D-785 R-80 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 110 Unannealed，1/4" bar ℃
Molding Shrinkage
ASTM D-955 1.4 ~
1.8 23℃ ％
Flammability
UL-94 HB 1.5 mm FILE NO. E162823 -
Combustibility
UL-94
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 28 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 61 0℉，4mm，Notched kJ/m²
123 73℉，1/8"，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 22 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1078 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-80 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 110 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Combustibility
UL-94
File No. E162823
-
To print, please click on the attached standard physical properties table.
High impact strength, High fluidity
Please choose
K8050
Impact Copolymer PP RESIN
Injection Molding Grade
Washing machine,Storage boxes,Thin wall products
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 10 23 ℃，1/8"，Notched kg-cm/cm
5 -20℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 240 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >100 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 12500 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-85 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 115 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Flammability
UL-94 1.5-1.65mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 ~ 1.65 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 50 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 49 0℉，4mm，Notched kJ/m²
98 73℉，1/8"，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 23 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >100 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1225 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-85 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 115 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
HB 1.5 ~ 1.65 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
High fluidity, Good impact strength, High Stiffness,Low warpage
Please choose
K8065
Impact Copolymer PP RESIN
Injection Molding Grade
Washing machine,Storage boxes,Thin wall products
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 9 23 ℃，1/8"，Notched kg-cm/cm
4.8 -20℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 240 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >100 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 12500 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-85 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 115 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 65 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 47 0℉，4mm，Notched kJ/m²
88 73℉，1/8"，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 23 23 ℃，50mm/min Mpa
0 23 ℃ Mpa
Tensile Elongation at break
ISO 527 >100 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1225 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-85 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 115 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
File No. E162823
-
To print, please click on the attached standard physical properties table.
High fluidity, Good impact strength, High Stiffness,Low warpage
Please choose
K8095
Impact Copolymer PP RESIN
Injection Molding Grade
Automotive parts
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 7 23 ℃，1/8"，Notched kg-cm/cm
4.5 -20℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 210 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >50 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 10000 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-78 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 108 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 95 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 44 0℉，4mm，Notched kJ/m²
69 73℉，1/8"，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 21 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >50 23 ℃，50mm/min %
Flexural Modulus
ISO 178 980 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-78 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 108 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
File No. E162823
-
To print, please click on the attached standard physical properties table.
High fluidity, Good impact strength, Good Stiffness
Please choose
K8802
Impact Copolymer PP RESIN
Injection Molding Grade
Suitcase Parts
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 70 23 ℃，1/8"，Notched kg-cm/cm
10 -20℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 270 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 11000 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-80 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 105 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.5 ~
1.9 23 ℃ %
Flammability
UL-94 1.5mm HB
3.0mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 2 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 98 0℉，4mm，Notched kJ/m²
686 73℉，1/8"，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 26 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1078 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-80 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 105 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.5 ~
1.9 23 ℃ %
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
Hight impact strength,
Please choose
K9010
Impact Copolymer PP RESIN
Injection Molding Grade
Automotive parts
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 50 23 ℃，1/8"，Notched kg-cm/cm
8.5 -20℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 220 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 10000 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-78 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 110 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Flammability
UL-94 1.5mm HB
3.0mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 9 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 83 0℉，4mm，Notched kJ/m²
490 73℉，1/8"，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 22 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Strength
ISO 178 0 23 ℃，2mm/min Mpa
Flexural Modulus
ISO 178 980 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-78 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 110 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
High impact strength, Good fluidity
Please choose
K9017
Impact Copolymer PP RESIN
Injection Molding Grade
Automotive parts
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 45 23 ℃，1/8"，Notched kg-cm/cm
8.3 -20℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 210 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 9000 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-76 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 98 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Flammability
UL-94 1.5mm HB
3.0mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.3 ~ 3 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 17 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 81 0℉，4mm，Notched kJ/m²
441 73℉，1/8"，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 21 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 882 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-76 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 98 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
HB 1.3 ~ 3 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
High impact strength, Good fluidity, Anti-UV added,
Please choose
K9030
Impact Copolymer PP RESIN
Injection Molding Grade
Bumper,Automotive parts, Thin wall products
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 50 23 ℃，1/8"，Notched kg-cm/cm
8 -20℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 200 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 8500 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-66 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 100 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 32 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 78 0℉，4mm，Notched kJ/m²
490 73℉，1/8"，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 20 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 833 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-66 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 100 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
File No. E162823
-
To print, please click on the attached standard physical properties table.
High fluidity, Hight impact strength
Please choose
KP03B
Impact Copolymer PP RESIN
Injection Molding Grade
Automotive parts, Storage boxes, Thin wall products
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 5 23 ℃，1/8"，Notched kg-cm/cm
3.7 -20℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 260 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >100 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 13500 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-94 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 115 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Flammability
UL-94 1.5mm HB
3.0mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 30 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 0 23 ℃，4mm，Unnotched kJ/m²
36 0℉，4mm，Notched kJ/m²
49 73℉，1/8"，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 25 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >100 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1323 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-94 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 115 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
High fluidity, Good impact strength
Please choose