AE8700
ABS Resin
Extrusion Grade
|
Extrusion products, Crash helmet, Pipes, Shoe heels |
Extrusion molding,
Super high impact,
High rigid
|
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 3.5 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 35 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 480 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 820 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 25000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-109 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 95 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 99 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 90 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 3.5 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 40 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 46 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 69 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2300 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-109 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 95 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 87 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
|
|
AG10NP
ABS Resin
Extrusion Grade
|
Extrusion products,Crash helmets,Pipes, Shoe heels
|
Extrusion molding, Super high impact, High rigid |
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 5.5 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 44 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 430 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 730 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 22000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-102 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 98 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 88 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 ~ 1.76 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 5.5 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 45 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 42 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 58 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1900 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-102 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 93 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.6 ~ 1.76 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
|
|
AE8000
ABS Resin
Extrusion Grade
|
Extrusion products,Crash helmets,Pipes, Shoe heels
|
Extrusion molding, Super high impact, High rigid |
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 4.5 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 45 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 440 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 740 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 22000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-103 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 87 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 4.5 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 47 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 42 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 51 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1500 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-103 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 92 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
|
|
AG10AP
ABS Resin
Extrusion Grade
|
Extrusion products,Crash helmets,Pipes, Shoe heels
|
Extrusion molding, Super high impact, High rigid |
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 4.0 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 51 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 370 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 640 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 19000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-93 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 91 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 94 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 84 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 4 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 50 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 37 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 46 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1500 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-93 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 91 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 92 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
|
|