PCR PP RESIN

Formosa Chemicals & Fibre Corporation (FCFC) TAIRIPRO PCR PP resin is an environmentally friendly polypropylene (PP) material containing post-consumer recycled (PCR) content. By combining FCFC’s expertise in PP production with advanced recycling technology, TAIRIPRO PCR PP delivers performance comparable to virgin PP, including excellent heat resistance, outstanding impact strength, and dimensional stability.

TAIRIPRO PCR PP is widely applicable in household storage products, precision instruments, sporting goods, and hygiene products. By incorporating PCR PP, it effectively reduces reliance on fossil-based resources while promoting plastic circularity, achieving both waste reduction and sustainability goals.

Furthermore, TAIRIPRO PCR PP complies with RoHS, SVHC, and international environmental standards, demonstrating FCFC’s commitment to green materials and environmental sustainability.

Our rPP has obtained the FDA No Objection Letter (NOL). Please see the attached document for your reference.

PCR PP RESIN

Model

Applications

Physical

Features

Attach

Operating

K8003

Baby-car parts, Paint drum,Sport appliances, Base of Luggage

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238

		13.5-18.0	230℃ × 2.16kg	g/10 min




IZOD Impact Strength	ASTM D-256







		3.0	23℃ 1/8"bar	kg-cm/cm





Specific Gravity	ASTM D-792	0.9	23℃	-


Tensile Strength	ASTM D-638

		362	23 ℃	kg/cm²

Tensile Elongation at break	ASTM D-638
Tensile Elongation at break	ASTM D-638	>200	23℃	%
Flexural Strength	ASTM D-790

		15000	23 ℃	kg/cm²

Rockwell Hardness	ASTM D-785	R-101	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648




		115	Unannealed，1/4" bar	℃





Molding Shrinkage	ASTM D-955
		1.4 ~ 1.8	-	%


FDA Compliance		Yes	-	-
Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
IZOD Impact Strength	ISO 180






		29	23℃ 1/8"bar	kJ/m2
Tensile Strength	ISO 527
		35	23 ℃	Mpa

Flexural Modulus	ISO 178
Flexural Modulus	ISO 178	1470	23 ℃	Mpa
Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

Hight impact strength, Good Stiffness

K8003

Baby-car parts, Paint drum,Sport appliances, Base of Luggage

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238

		3.6	230℃ × 2.16kg	g/10 min




IZOD Impact Strength	ASTM D-256
		45	23 ℃，1/8"，Notched	kg-cm/cm












Specific Gravity	ASTM D-792
		0.9	23℃/23℃	-

Tensile Strength	ASTM D-638

		260	23 ℃	kg/cm²

Tensile Elongation at break	ASTM D-638	>200	23 ℃，50mm/min	%
Tensile Elongation at break	ASTM D-638
Flexural Strength	ASTM D-790

		11500	23 ℃	kg/cm²

Rockwell Hardness	ASTM D-785	R-83	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648



		115	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955
		1.48 ~ 1.8	-	%


FDA Compliance		Yes	-	-
Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
IZOD Impact Strength	ISO 180
		440	23 ℃，1/8"，Notched	kJ/m²






Tensile Strength	ISO 527
		25	23 ℃	Mpa

Flexural Strength	ISO 178
Flexural Strength	ISO 178	1127	23 ℃	Mpa
Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

Hight impact strength, Good Stiffness

K8003

Baby-car parts, Paint drum,Sport appliances, Base of Luggage

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238

		20-25	230℃ × 2.16kg	g/10 min




IZOD Impact Strength	ASTM D-256











		4.9(48)	23℃ 1/8"bar	kg-cm/cm (J/m)

Specific Gravity	ASTM D-792
		0.9	23℃/23℃	-

Tensile Elongation at break	ASTM D-638
Tensile Elongation at break	ASTM D-638	>200	23℃	%
Rockwell Hardness	ASTM D-785	R-85	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648




		95	Unannealed，1/4" bar	℃





Molding Shrinkage	FCFC Method	1.4 ~ 1.8	23 ℃	%
Tensile Strength at Yield	ASTM D-638	280(27)	23℃	kg/cm2 (Mpa)
Flexural Modulus	ASTM D-790A	11000(1078)	23℃	kgf/cm2
Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

Hight impact strength, Good Stiffness

K8003

Baby-car parts, Paint drum,Sport appliances, Base of Luggage

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238

		35	230℃ × 2.16kg	g/10 min




IZOD Impact Strength	ASTM D-256







		5.0(49)	23℃ 1/8"bar	kg-cm/cm





Specific Gravity	ASTM D-792
		0.9	23℃/23℃	-

Tensile Elongation at break	ASTM D-638
Tensile Elongation at break	ASTM D-638	>200	23℃	%
Rockwell Hardness	ASTM D-785	R-85	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648




		95	Unannealed，1/4" bar	℃





Tensile Strength at Yield	ASTM D-638	280(27)	23℃	kg/cm2 (Mpa)
Flexural Modulus	ASTM D-790A	11500	23℃	kgf/cm2
Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

Hight impact strength, Good Stiffness

K8003

Baby-car parts, Paint drum,Sport appliances, Base of Luggage

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238

		25.0	230℃ × 2.16kg	g/10 min




IZOD Impact Strength	ASTM D-256











		8.0(78)	23℃ 1/8"bar	kg-cm/cm (J/m)
		4.1(40)	-20℃ 1/8"bar	kg-cm/cm (J/m)
Specific Gravity	ASTM D-792
		0.9	23℃/23℃	-

Tensile Elongation at break	ASTM D-638
Tensile Elongation at break	ASTM D-638	>200	23℃	%
Flexural Strength	ASTM D-790

		13121	23 ℃	kg/cm²

Rockwell Hardness	ASTM D-785	R-80	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648




		118	Unannealed，1/4" bar	℃





Molding Shrinkage	FCFC Method	1.4 ~ 1.8	23 ℃	%
Tensile Strength at Yield	ASTM D-638	250 (24)	23℃	kg/cm2 (Mpa)
Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

Hight impact strength, Good Stiffness

K8003

Baby-car parts, Paint drum,Sport appliances, Base of Luggage

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238

		3.0-4.2	230℃ × 2.16kg	g/10 min




IZOD Impact Strength	ASTM D-256







		45	23℃ 1/8"bar	kg-cm/cm





Specific Gravity	ASTM D-792
		0.9	23℃/23℃	-

Tensile Strength	ASTM D-638

		260	23 ℃	kg/cm²

Tensile Elongation at break	ASTM D-638
Tensile Elongation at break	ASTM D-638	>200	23℃	%
Flexural Modulus	ASTM D-790

		11500	23 ℃	kg/cm²

Rockwell Hardness	ASTM D-785	R-83	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648




		115	Unannealed，1/4" bar	℃





Molding Shrinkage	ASTM D-955


		1.4 ~ 1.8	23℃	％
FDA Compliance		YES	-	-
Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
IZOD Impact Strength	ISO 180
		440	23 ℃，1/8"，Notched	kJ/m²






Tensile Strength	ISO 527
		25	23 ℃	Mpa

Flexural Modulus	ISO 178
Flexural Modulus	ISO 178	1127	23 ℃	Mpa
Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

Hight impact strength, Good Stiffness

K8003

Baby-car parts, Paint drum,Sport appliances, Base of Luggage

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238

		25	230℃ × 2.16kg	g/10 min




IZOD Impact Strength	ASTM D-256







		2.6	23℃ 1/8"bar	kg-cm/cm





Specific Gravity	ASTM D-792
		0.9	23℃/23℃	-

Tensile Strength	ASTM D-638

		343	23 ℃	kg/cm²

Tensile Elongation at break	ASTM D-638
Tensile Elongation at break	ASTM D-638	>200	23℃	%
Flexural Modulus	ASTM D-790

		14500	23 ℃	kg/cm²

Rockwell Hardness	ASTM D-785	R-100	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648




		110	Unannealed，1/4" bar	℃





Molding Shrinkage	FCFC Method	1.52 ~	23 ℃	%
Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

Hight impact strength, Good Stiffness

K8003

Baby-car parts, Paint drum,Sport appliances, Base of Luggage

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238

		31-37	230℃ × 2.16kg	g/10 min




IZOD Impact Strength	ASTM D-256







		4.0	23℃ 1/8"bar	kg-cm/cm



		4.0(38)	23℃ 1/8"bar	kg-cm/cm (J/m)

Specific Gravity	ASTM D-792
		0.9	23℃/23℃	-

Tensile Elongation at break	ASTM D-638
Tensile Elongation at break	ASTM D-638	>200	23℃	%
Flexural Modulus	ASTM D-790

		18000	23 ℃	kg/cm²

Rockwell Hardness	ASTM D-785	R-105	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648




		125	Unannealed，1/4" bar	℃





Molding Shrinkage	ASTM D-955


		1.4 ~ 1.8	23℃	％
Tensile Strength at Yield	ASTM D-638	380(37)	23℃	kg/cm2 (Mpa)
Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

Hight impact strength, Good Stiffness