TAIRILAC ASA Resin - Self-Developed

ASA Resin

FCFC ASA Resin (TAIRILAC® ASA Resin) has excellent weather resistance and a stain ability, which is self-developed production technology and gain the Republic of China 229680 patent. Production process fully by existing ABS devices to convert capacity adjusts supply to meet market demand. The major ingredients come from our own sixth naphtha cracking project, this will ensure the stability of quality with competitive price. The factory has lab and testing equipment, product development can be based on market demand, in addition to the general purpose and high flow grade, developing of building materials and automotive in response to the environmental protection and new energy material. The future product development will gradually replace specialty ABS, to comply with the environmental protection technology of spraying and electroplating.

PDF Download

ISO 9001 ISO 14001

ASA Resin

Model

Applications

Features

Attachments

Physical

Comparison

Contact

WG1500

ASA RESIN

Outdoor Products、junction box、Auto parts

Weather resistance is excellent,
Color stable, Suitable for outdoor use

ASTM Physical
ISO Physical

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		20	220℃ × 10kg	g/10 min





IZOD Impact Strength	ASTM D-256
		13	23 ℃，1/8"，Notched	kg-cm/cm












Specific Gravity	ASTM D-792
		1.05	23℃/23℃	-

Tensile Strength	ASTM D-638
		440	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	770	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	23000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-103	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	88	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648



		83	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133






		18	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	15	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.05	23℃/23℃	-
Tensile Strength	ISO 527	40	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	61	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2000	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-103	23℃	R-scale
Vicat Softening Point	ISO 306	88	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		88	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

WG1800

ASA RESIN

Fans of air-conditioner, Housings of motorbike, Outside applications

Weather resistance is excellent,
Color stable, Suitable for outdoor use

ASTM Physical
ISO Physical

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		19	220℃ × 10kg	g/10 min





IZOD Impact Strength	ASTM D-256
		18	23 ℃，1/8"，Notched	kg-cm/cm












Specific Gravity	ASTM D-792
		1.05	23℃/23℃	-

Tensile Strength	ASTM D-638
		430	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	710	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	21000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-100	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648



		86	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Flammability	UL-94	1.5mm HB 3.0mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133






		18	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	23	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.05	23℃/23℃	-
Tensile Strength	ISO 527	40	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	57	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	1900	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-100	23℃	R-scale
Vicat Softening Point	ISO 306	90	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		90	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

WF3301

ASA RESIN

Fans of air-conditioner, Parts of car, Outside pipes

Weather resistance is excellent,
Color stable, Suitable for outdoor use

ASTM Physical
ISO Physical

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		26	220℃ × 10kg	g/10 min





IZOD Impact Strength	ASTM D-256
		20	23 ℃，1/8"，Notched	kg-cm/cm












Specific Gravity	ASTM D-792
		1.05	23℃/23℃	-

Tensile Strength	ASTM D-638
		410	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	670	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	21000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-96	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	89	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648



		83	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Flammability	UL-94	1.5mm HB 3.0mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133






		30	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	24	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.05	23℃/23℃	-
Tensile Strength	ISO 527	38	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	53	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	1700	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-96	23℃	R-scale
Vicat Softening Point	ISO 306	89	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		90	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

WE8303

ASA RESIN

Outdoor Products、junction box、Auto parts

Excellent weather resistance, Extrusion products

ASTM Physical
ISO Physical

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		3.0	220℃ × 10kg	g/10 min





IZOD Impact Strength	ASTM D-256
		33	23 ℃，1/8"，Notched	kg-cm/cm












Specific Gravity	ASTM D-792
		1.05	23℃/23℃	-

Tensile Strength	ASTM D-638
		450	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	610	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	22000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-102	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	93	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648



		88	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Flammability	UL-94	1.5mm HB 3.0mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133






		3	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	34	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.05	23℃/23℃	-
Tensile Strength	ISO 527	41	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	45	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	1950	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-102	23℃	R-scale
Vicat Softening Point	ISO 306	93	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		94	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

WE8300

ASA RESIN

Suitable for plastic roof tile modified use.

Excellent weather resistance, Suitable for plastic roof tile modified use.

ASTM Physical
ISO Physical

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		8.0	220℃ × 10kg	g/10 min





IZOD Impact Strength	ASTM D-256
		15	23 ℃，1/8"，Notched	kg-cm/cm












Specific Gravity	ASTM D-792
		1.05	23℃/23℃	-

Tensile Strength	ASTM D-638
		440	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	750	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	22000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-101	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	93	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648



		85	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Flammability	UL-94	1.5mm HB 3.0mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133






		8	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	16	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.05	23℃/23℃	-
Tensile Strength	ISO 527	39	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	59	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2000	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-101	23℃	R-scale
Vicat Softening Point	ISO 306	93	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		91	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

WE830M

ASA RESIN

Suitable for plastic roof tile modified use.

Excellent weather resistance, Suitable for plastic roof tile modified use.

ASTM Physical
ISO Physical

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		9.0	220℃ × 10kg	g/10 min





IZOD Impact Strength	ASTM D-256
		11	23 ℃，1/8"，Notched	kg-cm/cm












Specific Gravity	ASTM D-792
		1.05	23℃/23℃	-

Tensile Strength	ASTM D-638
		330	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	550	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	15000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-85	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	87	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648



		82	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		10	200℃ × 5kg	g/10 min





Charpy Impact Strength	ISO 179	11	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.05	23℃/23℃	-
Tensile Strength	ISO 527	29	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	41	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	1400	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Vicat Softening Point	ISO 306	87	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		88	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

WX1805

ASA RESIN

Outdoor Products、junction box、Auto parts

Parts of cars, Electrical appliances, Heat resistant parts

ASTM Physical
ISO Physical

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		6.5	220℃ × 10kg	g/10 min





IZOD Impact Strength	ASTM D-256
		9	23 ℃，1/8"，Notched	kg-cm/cm












Specific Gravity	ASTM D-792
		1.05	23℃/23℃	-

Tensile Strength	ASTM D-638
		500	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	870	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	25000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-109	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	99	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648



		94	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Flammability	UL-94	1.5mm HB 3.0mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133






		5	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	16	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.05	23℃/23℃	-
Tensile Strength	ISO 527	46	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	71	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2300	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-109	23℃	R-scale
Vicat Softening Point	ISO 306	99	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		100	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

WE9100

ASA RESIN

Outdoor Products、junction box、Auto parts

Suitable for plastic roof tile modified use.

ASTM Physical
ISO Physical

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		1.5	220℃ × 10kg	g/10 min





IZOD Impact Strength	ASTM D-256
		60	23 ℃，1/8"，Notched	kg-cm/cm












Specific Gravity	ASTM D-792
		1.05	23℃/23℃	-

Tensile Strength	ASTM D-638
		230	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	380	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	11000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-53	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	83	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648



		77	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133






		1.8	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	65	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.05	23℃/23℃	-
Tensile Strength	ISO 527	18	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	22	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	1000	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-53	23℃	R-scale
Vicat Softening Point	ISO 306	83	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		84	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.