HP835G
PS Resin
High Impact Grade
|
Housing for electrical appliances, Baby car parts,Housings of LCD Monitor,Exercise appliances
|
High impact, Normal flow |
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 3.7 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 11 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 280 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 22000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 55 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 550 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 23000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 101 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 89 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Combustibility |
UL-94 |
HB 1 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 3.7 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 10.8 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 8 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 28 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 2400 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 38 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 54 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2300 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 101 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 94 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
|
|
HP8250
PS Resin
High Impact Grade
|
Housing for electrical appliances, Baby car parts,Housings of LCD Monitor,Exercise appliances
|
High impact, Normal flow |
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 5.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 13 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 240 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 23000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 49 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 450 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 23000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 99 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 90 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 0.8mm HB
1.0mm HB
1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 5 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 13 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 9 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 24 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 2100 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 29 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 42 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2100 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 99 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 90 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
|
|
HP825F
PS Resin
High Impact Grade
|
Housing for electrical appliances, Baby car parts,Housings of LCD Monitor,Exercise appliances
|
High flow |
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 9.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 12 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 250 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 24000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 45 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 460 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 23000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 100 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 90 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 9 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 10 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 9.6 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 26 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 2300 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 33 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 46 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 99 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 96 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
|
|
HP9450
PS Resin
High Impact Grade
|
HP sheets, Disposable dishware,Electronic Packaging, Cable reels
|
Super high impact |
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 3.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 14 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 250 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 22000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 52 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 470 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 21000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 100 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 90 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 3 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 10.2 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Tensile Strength |
ISO 527 | |
| 25 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 2000 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 39 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 40 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1800 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 100 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 90 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
|
|
MP6500
PS Resin
High Impact Grade
|
Stationery, Toys,Parts for home electrical appliances, Clothing hangers, Clock housing, FRP blending
|
Medium impact |
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 6.4 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 7 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 290 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 24000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 37 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 550 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 23000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 98 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 90 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 6.4 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 6.5 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 5.6 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 29 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 2600 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 27 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 50 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2300 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 98 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 90 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
|
|