Special Grade

FCFC SAN Resin (TAIRISAN® SAN Resin), in additional to ABS production use, providing a diversity of products for sale such as lighters, cosmetic cases, water filter, battery housing and other needs transparency and resistance to chemical products.

PDF Download

Hsin-Kang PABS Plant: ISO 9001 ISO 14001

Mai-Liao PABS Plant: ISO 9001 ISO 14001

Special Grade

Model

Applications

Features

Attachments

Physical

Comparison

Contact

NX3200

SAN RESIN

Special grade

Blade of fan, Batteries housing

High heat,
Chemical resistance

ASTM Physical
ISO Physical

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		15	220℃ × 10kg	g/10 min




		1.5	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	<2	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.06	23℃/23℃	-

Tensile Strength	ASTM D-638
		800	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	1200	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	37000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	M-79	23℃	M-scale
Vicat Softening Point	ASTM D-1525	102	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648



		96	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Combustibility	UL-94	HB 1.5 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		1.5	200℃ × 5kg	g/10 min




		15	220℃ × 10kg	g/10 min
CHARPY IMPACT STRENGTH	ISO 179	<2	23℃, 4mm, Notched	kJ/m2
Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.06	23℃/23℃	-
Tensile Strength	ISO 527	82	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	118	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	3600	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-79	23℃	R-scale
Vicat Softening Point	ISO 306	102	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		103	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.5 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

NX3400

SAN RESIN

Special grade

Blade of fan, Batteries housing

High heat,
Chemical resistance

ASTM Physical
ISO Physical

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		10	220℃ × 10kg	g/10 min




		1.0	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	<2	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.06	23℃/23℃	-

Tensile Strength	ASTM D-638
		820	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	1200	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	37000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	M-79	23℃	M-scale
Vicat Softening Point	ASTM D-1525	102	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648



		97	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Flammability	UL-94	1.6-1.8mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94	HB 1.6 ~ 1.8 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		1	200℃ × 5kg	g/10 min




		10	220℃ × 10kg	g/10 min
CHARPY IMPACT STRENGTH	ISO 179	<2	23℃, 4mm, Notched	kJ/m2
Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.06	23℃/23℃	-
Tensile Strength	ISO 527	83	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	121	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	3600	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-79	23℃	R-scale
Vicat Softening Point	ISO 306	102	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		104	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.6 ~ 1.8 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.