K1011
Homopolymer PP RESIN
Injection Molding Grade
General purpose, Foodcontainers, Electrical appliances, Housewares meets the requirements of USP Plastic Class VI
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 15 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 2.8 23 ℃，1/8"，Notched kg-cm/cm
2.8 23 ℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 350 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 14500 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-100 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 110 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
HB 1.5 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 15 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 27 23 ℃，1/8"，Notched kJ/m²
27 23 ℃，4mm，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 34 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1421 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-100 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 110 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
HB 1.5 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
Good stiffness,
Please choose
K1011AG
Homopolymer PP RESIN
Injection Molding Grade
Electric appliance parts,RTI=125℃
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 15 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 3.6 23 ℃，1/8"，Notched kg-cm/cm
3.6 23 ℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 380 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 16500 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-107 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 125 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Flammability
UL-94 1.5mm HB
3.0mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 15 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 35 23 ℃，1/8"，Notched kJ/m²
35 23 ℃，4mm，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 37 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1617 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-107 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 125 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
Long term heat resistance,High stiffness,Good luster
Please choose
K1023
Homopolymer PP RESIN
Injection Molding Grade
Thin wall parts,Housewares,Toys,meets the requirements of USP Plastic Class VI
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 23 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 2.6 23 ℃，1/8"，Notched kg-cm/cm
2.6 23 ℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 340 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 14000 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-100 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 110 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Flammability
UL-94 1.5mm HB
3.0mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 25 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 25 23 ℃，1/8"，Notched kJ/m²
25 23 ℃，4mm，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 33 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1372 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-100 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 110 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
High fluidity,
Please choose
K1035
Homopolymer PP RESIN
Injection Molding Grade
Thin wall parts , Housewares , Toys
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 38 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 2 23 ℃，1/8"，Notched kg-cm/cm
2 23 ℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 340 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >50 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 14000 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-102 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 110 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Flammability
UL-94 1.5mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 0 300℃ × 1.2kg g/10 min
38 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 2 23 ℃，1/8"，Notched kJ/m²
2 23 ℃，4mm，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 33 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >50 23 ℃，50mm/min %
Flexural Strength
ISO 178 0 23 ℃，2mm/min Mpa
Flexural Modulus
ISO 178 14000 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-102 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 110 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
HB 1.5 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
High fluidity,
Please choose
K1080
Homopolymer PP RESIN
Injection Molding Grade
Thin wall parts , Housewares , Toys
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 80 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 2 23 ℃，1/8"，Notched kg-cm/cm
2 23 ℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 350 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >50 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 14000 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-102 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 110 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 80 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 20 23 ℃，1/8"，Notched kJ/m²
20 23 ℃，4mm，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 34 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >50 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1372 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-102 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 110 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
File No. E162823
-
To print, please click on the attached standard physical properties table.
Ultra high fluidity, Good stiffness, Good luster
Please choose
K1108
Homopolymer PP RESIN
Injection Molding Grade
General purpose, Foodcontainers, Electrical appliances, Housewares
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 10 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 3 23 ℃，1/8"，Notched kg-cm/cm
3 23 ℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 360 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 15000 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-100 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 115 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Flammability
UL-94 1.5mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 10 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 29 23 ℃，1/8"，Notched kJ/m²
29 23 ℃，4mm，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 35 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1470 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-100 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 115 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
HB 1.5 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
Good stiffness, Good luster
Please choose
K1525
Homopolymer PP RESIN
Injection Molding Grade
microwave containers, Food containers
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 25 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 2.6 23 ℃，1/8"，Notched kg-cm/cm
2.6 23 ℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 360 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >50 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 18000 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-108 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 125 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Flammability
UL-94 1.5mm HB
3.0mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 25 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 25 23 ℃，1/8"，Notched kJ/m²
25 23 ℃，4mm，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 35 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >50 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1764 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-108 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 125 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
High fluidity, High Stiffness , Good luster, Good
Please choose
K2051
Homopolymer PP RESIN
Injection Molding Grade
Thinner Wall Parts, Microwave containers, House wares,Toys
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 51 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 4 23 ℃，1/8"，Notched kg-cm/cm
4 23 ℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 400 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >50 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 20000 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-110 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 135 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.4 ~
1.8 23 ℃ %
Combustibility
UL-94
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 50 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 39 23 ℃，1/8"，Notched kJ/m²
39 23 ℃，4mm，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 39 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >50 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1960 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-110 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 135 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Combustibility
UL-94
File No. E162823
-
To print, please click on the attached standard physical properties table.
Super high fluidity,
Please choose
Storage and Validity suggestion