AC2300
|
Auto parts, household appliances, 3C electronic products and household goods casings such as wheel covers, handles, Portable storage device
|
Metal plating
|
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
| 7 | 240℃ × 5kg | g/10 min |
|
| 17 | 260℃ × 5kg | g/10 min |
|
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
|
|
|
|
| 60 | 23 ℃ | kg-cm/cm |
|
|
|
|
| Specific Gravity |
ASTM D-792 | |
| 1.14 | 23 ℃ | g/cm3 |
| Tensile Strength |
ASTM D-638 | |
| 560 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 920 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 23000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-116 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
|
|
| 112 | Unannealed 6.4mm, 1.8 MPa | ℃ |
|
|
| Molding Shrinkage |
ASTM D-955 | |
| 0.4 ~
0.6 | Flow dir.料流方向 | % |
|
| Flammability |
UL-94 | 1.5mm HB | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
|
|
|
AC2300
|
Auto parts, household appliances, 3C electronic products and household goods casings such as wheel covers, handles, Portable storage device
|
Metal plating
|
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
| 37 | 240℃ × 5kg | g/10 min |
| 27 | 260℃ × 2.16kg | g/10 min |
|
|
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
|
|
|
|
| 45 | 23 ℃ | kg-cm/cm |
| 15 | -30 ℃ | kg-cm/cm |
|
|
|
| Specific Gravity |
ASTM D-792 | |
| 1.18 | 23 ℃ | g/cm3 |
| Tensile Elongation |
ASTM D-638 | | 600 | 23 ℃ | kg/cm2 |
| Flexural Strength |
ASTM D-790 | |
| 1000 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 26000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-117 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
|
|
| 87 | Unannealed 6.4mm, 1.8 MPa | ℃ |
|
|
| Molding Shrinkage |
ASTM D-955 | |
| 0.4 ~
0.6 | Flow dir.料流方向 | % |
|
| Flammability |
UL-94 | 1.5mm V-0
1.5mm 5V-B | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
|
|
|
AC2300
|
Auto parts, household appliances, 3C electronic products and household goods casings such as wheel covers, handles, Portable storage device
|
Metal plating
|
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
| 25 | 240℃ × 5kg | g/10 min |
|
|
|
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
|
|
|
|
| 60 | 23 ℃ | kg-cm/cm |
| -- | -30 ℃ | kg-cm/cm |
|
|
|
| Specific Gravity |
ASTM D-792 | |
| 1.18 | 23 ℃ | g/cm3 |
| Tensile Strength |
ASTM D-638 | |
| 600 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 1000 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 25000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-116 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
|
|
| 88 | Unannealed 6.4mm, 1.8 MPa | ℃ |
|
|
| Molding Shrinkage |
ASTM D-955 | |
| 0.4 ~
0.6 | Flow dir.料流方向 | % |
|
| Flammability |
UL-94 | 1.5mm V0 | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
|
|
|
AC2300
|
Auto parts, household appliances, 3C electronic products and household goods casings such as wheel covers, handles, Portable storage device
|
Metal plating
|
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
| 9 | 240℃ × 5kg | g/10 min |
|
| 21 | 260℃ × 5kg | g/10 min |
|
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
|
|
|
|
| 50 | 23 ℃ | kg-cm/cm |
|
|
|
|
| Specific Gravity |
ASTM D-792 | 1.08 | 23℃ | - |
|
|
| Tensile Strength |
ASTM D-638 | |
| 480 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 840 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 23000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-107 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
|
|
| 95 | Unannealed 6.4mm, 1.8 MPa | ℃ |
|
|
| Molding Shrinkage |
ASTM D-955 | | 0.4 ~
0.6 | - | % |
|
|
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
| 27 | 260℃ × 2.16kg | g/10 min |
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
| 510 | 23 ℃ 3.2mm | J/m |
|
|
|
|
| Charpy Impact Strength |
ISO 179 | |
| 35 | 23 ℃ 4mm | kJ/m² |
|
| Tensile Strength |
ISO 527 | | 47 | 23 ℃ | Mpa |
|
| Flexural Strength |
ISO 178 | | 82 | 23 ℃ | Mpa |
| Flexural Modulus |
ISO 178 | | 2250 | 23 ℃ | Mpa |
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
| 84 | Unannealed 18.6 kg/cm² (1.8MPa)(6.4mm) | ℃ |
|
|
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
|
|
AC2300
PC/ABS Alloy
General Grade
|
Auto parts, household appliances, 3C electronic products and household goods casings such as wheel covers, handles, Portable storage device
|
Metal plating
|
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
| 9.0 | 240℃ × 5kg | g/10 min |
|
| 21 | 260℃ × 5kg | g/10 min |
|
| IZOD Impact Strength |
ASTM D-256 | |
|
| 55 | 23℃, 3.2mm, Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.08 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | |
| 510 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 880 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 24000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-110 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | |
|
| 117 | VICAT(10N ℃) | ℃ |
|
| Heat Deflection Temperature |
ASTM D-648 | |
| 96 | Unannealed 18.6 kg/cm² (1.8Mpa)(6.4mm) | ℃ |
|
|
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.6 | 3.2mm | % |
|
|
|
| Flammability |
UL-94 | 1.5-1.65mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
| 9 | 240℃ × 5kg | g/10 min |
|
| 21 | 260℃ × 5kg | g/10 min |
|
|
| IZOD Impact Strength |
ISO 180 | |
|
| 540 | 23 ℃ 3.2mm | J/m |
|
|
|
|
| Charpy Impact Strength |
ISO 179 | |
| 40 | 23 ℃ 4mm | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 1.08 | 23℃/23℃ | - |
| Flexural Strength |
ISO 178 | | 86 | 23 ℃ | Mpa |
| Flexural Modulus |
ISO 178 | | 2350 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-110 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | |
|
| 117 | VICAT(10N ℃) | ℃ |
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
| 0 | Unannealed 18.6 kg/cm² (1.8MPa)(6.4mm) | ℃ |
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.6 | 3.2mm | % |
| Symbol |
ISO 1043 | >ABS+PC< | - | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
|
|