AF3535
|
Housing of stereos, Large toys, Chairs,
Motorcycles, OA machines |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 16 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 14 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Density |
ASTM D-792 | 1.04-1.07 | 23 ℃ | g/cm3 |
| Tensile Strength |
ASTM D-638 | |
| 400 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 700 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 22000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
|
|
|
|
| 84 | 1.8 MPa, 1/4”bar Unannealed | ℃ |
| Molding Shrinkage |
ASTM D-955 | |
|
| 0.4 ~
0.7 | 23℃ | ％ |
| Relative Temp Index |
UL746B | 60 | Elec | ℃ |
| 60 | Imp | ℃ |
| 60 | Str | ℃ |
| Combustibility |
UL-94 |
HB 1.5 ~ 2.99 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 ~ 2.99 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(220℃×10kg):39
Izod (ASTM,1/4"):23
FM(ASTM):23000
TS(ASTM):440
High flow
High impact
|
|
|
|
AF3535
|
Housing of stereos, Large toys, Chairs,
Motorcycles, OA machines |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 21 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 12 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Density |
ASTM D-792 | 1.04-1.07 | 23 ℃ | g/cm3 |
| Tensile Strength |
ASTM D-638 | |
| 390 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 690 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 22000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Molding Shrinkage |
ASTM D-955 | |
|
| 0.4 ~
0.7 | 23℃ | ％ |
| Relative Temp Index |
UL746B | 60 | Elec | ℃ |
| 60 | Imp | ℃ |
| 60 | Str | ℃ |
| Combustibility |
UL-94 |
HB 1.5 ~ 2.99 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 ~ 2.99 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(220℃×10kg):39
Izod (ASTM,1/4"):23
FM(ASTM):23000
TS(ASTM):440
High flow
High impact
|
|
|
|
AF3535
|
Housing of stereos, Large toys, Chairs,
Motorcycles, OA machines |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 28 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 14 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Density |
ASTM D-792 | 1.04-1.07 | 23 ℃ | g/cm3 |
| Tensile Strength |
ASTM D-638 | |
| 400 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 700 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 24000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-103 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
|
|
|
|
| 83 | 1.8 MPa, 1/4”bar Unannealed | ℃ |
| Molding Shrinkage |
ASTM D-955 | |
|
| 0.4 ~
0.7 | 23℃ | ％ |
| Relative Temp Index |
UL746B | 60 | Elec | ℃ |
| 60 | Imp | ℃ |
| 60 | Str | ℃ |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(220℃×10kg):39
Izod (ASTM,1/4"):23
FM(ASTM):23000
TS(ASTM):440
High flow
High impact
|
|
|
|
AF3535
|
Housing of stereos, Large toys, Chairs,
Motorcycles, OA machines |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 19 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 15 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Density |
ASTM D-792 | 1.04-1.07 | 23 ℃ | g/cm3 |
| Tensile Strength |
ASTM D-638 | |
| 410 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 730 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 23000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-103 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
|
|
|
|
| 84 | 1.8 MPa, 1/4”bar Unannealed | ℃ |
| Molding Shrinkage |
ASTM D-955 | |
|
| 0.4 ~
0.7 | 23℃ | ％ |
| Relative Temp Index |
UL746B | 60 | Elec | ℃ |
| 60 | Imp | ℃ |
| 60 | Str | ℃ |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(220℃×10kg):39
Izod (ASTM,1/4"):23
FM(ASTM):23000
TS(ASTM):440
High flow
High impact
|
|
|
|
AF3535
|
Housing of stereos, Large toys, Chairs,
Motorcycles, OA machines |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 23 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 17 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Density |
ASTM D-792 | 1.04-1.07 | 23 ℃ | g/cm3 |
| Tensile Strength |
ASTM D-638 | |
| 440 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 770 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 24000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-105 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
|
|
|
|
| 86 | 1.8 MPa, 1/4”bar Unannealed | ℃ |
| Molding Shrinkage |
ASTM D-955 | |
|
| 0.4 ~
0.7 | 23℃ | ％ |
| Relative Temp Index |
UL746B | 60 | Elec | ℃ |
| 60 | Imp | ℃ |
| 60 | Str | ℃ |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(220℃×10kg):39
Izod (ASTM,1/4"):23
FM(ASTM):23000
TS(ASTM):440
High flow
High impact
|
|
|
AF3535
ABS RESIN
High Flow Grade
|
Housing of stereos, Large toys, Chairs,
Motorcycles, OA machines |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 29 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 17 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Density |
ASTM D-792 | 1.04-1.07 | 23 ℃ | g/cm3 |
| Tensile Strength |
ASTM D-638 | |
| 420 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 730 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 24000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-106 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
|
|
|
|
| 86 | 1.8 MPa, 1/4”bar Unannealed | ℃ |
| Molding Shrinkage |
ASTM D-955 | |
|
| 0.4 ~
0.7 | 23℃ | ％ |
| Relative Temp Index |
UL746B | 60 | Elec | ℃ |
| 60 | Imp | ℃ |
| 60 | Str | ℃ |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(220℃×10kg):39
Izod (ASTM,1/4"):23
FM(ASTM):23000
TS(ASTM):440
High flow
High impact
|
|
|