General Grade

FCFC SAN Resin (TAIRISAN® SAN Resin), in additional to ABS production use, providing a diversity of products for sale such as lighters, cosmetic cases, water filter, battery housing and other needs transparency and resistance to chemical products.

PDF Download

Hsin-Kang PABS Plant: ISO 9001 ISO 14001

Mai-Liao PABS Plant: ISO 9001 ISO 14001

General Grade

Model

Applications

Features

Attachments

Physical

Comparison

Contact

NF2100

SAN RESIN

General Grade

Cassettes, Trash cans, Toothbrush handles, Lamp covers, Pen tube, Cup with cover, Cosmetic cases

MI(220℃×10kg):50

Izod (ASTM,1/4"):1.5

FM(ASTM):35000

TS(ASTM):700

High flow,

Injection grade

ASTM Physical
ISO Physical

Property	Test Method	Value	Test Condition	Unit
IZOD Impact Strength	ASTM D-256




		<2	23 ℃，1/4"，Notched	kg-cm/cm








Specific Gravity	ASTM D-792
		1.06	23℃/23℃	-

Tensile Strength	ASTM D-638

		700	23 ℃	kg/cm²

Flexural Modulus	ASTM D-790

		35000	23 ℃	kg/cm²

Rockwell Hardness	ASTM D-785	M-78	23℃	M-scale
Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		5	200℃ × 5kg	g/10 min




		50	220℃ × 10kg	g/10 min
CHARPY IMPACT STRENGTH	ISO 179	<2	23℃, 4mm, Notched	kJ/m2
Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.06	23℃/23℃	-
Flexural Strength	ISO 178
Flexural Strength	ISO 178	118	23 ℃	Mpa
Flexural Modulus	ISO 178
Flexural Modulus	ISO 178	69	23 ℃	Mpa
Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

NF2200

SAN RESIN

General Grade

Trash cans, Toothbrush handles, Lamp covers, Pen tube, Cup with cover, Cosmetic cases

High flow , Injection grade

ASTM Physical
ISO Physical

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		29	220℃ × 10kg	g/10 min




		2.9	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	<2	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.06	23℃/23℃	-

Tensile Strength	ASTM D-638
		720	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	1200	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	35000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	M-78	23℃	M-scale
Vicat Softening Point	ASTM D-1525	101	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648



		94	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Flammability	UL-94	1.5mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94	HB 1.5 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		2.9	200℃ × 5kg	g/10 min




		29	220℃ × 10kg	g/10 min
CHARPY IMPACT STRENGTH	ISO 179	<2	23℃, 4mm, Notched	kJ/m2
Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.06	23℃/23℃	-
Tensile Strength	ISO 527	73	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	117	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	3600	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-78	23℃	R-scale
Vicat Softening Point	ISO 306	101	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		102	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.5 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.