Extrusion

PP resin (TAIRIPRO® PP resin) using the state of art Gas-Phase processing technologies granted by Chisso, Japan, the high efficient catalyst and the comprehensive quality control system, its yearly capacity is 510,000MTS. The Tairipro product classification contains homo polymer, random and impact copolymer which can be processed by injection, extrusion, blow and vacuum thermoforming. Their application is versatile and adopted in the field of home appliance, AUTO parts, food packages, toys and daily necessities. The R&D center & the full range pilot plant well equipped will be supportive of our new grade development and the setup of the relevant processing guide as well. All production facilities are operated in accordance with strict environmental protection regulation, and waste gases treated by high-heat combustion, then heat recovered. No waste water arises in the polymerization process.

Storage and Validity suggestion

ISO 9001

ISO 14001

TAF ISO IEC 17025_2017_EN

TAF ISO IEC 17025_2017_ZN-TW

Extrusion

Model

Applications

Physical

Features

Attach

Operating

B8001

Impact Copolymer PP RESIN

Extrusion Grade

PP Pipe, Thermoforming sheet, Blow molding

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238

		1	230℃ × 2.16kg	g/10 min




IZOD Impact Strength	ASTM D-256
		80	23 ℃，1/8"，Notched	kg-cm/cm




			-20℃，4mm，Notched	kg-cm/cm







Specific Gravity	ASTM D-792
		0.9	23℃/23℃	-

Tensile Strength	ASTM D-638
		270	23 ℃，50mm/min	kg/cm²


Tensile Elongation at break	ASTM D-638	>200	23 ℃，50mm/min	%
Tensile Elongation at break	ASTM D-638
Flexural Modulus	ASTM D-790

		11000	23 ℃	kg/cm²

Rockwell Hardness	ASTM D-785	R-80	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648




		105	Unannealed，1/4" bar	℃





Molding Shrinkage	FCFC Method	1.5 ~ 1.9	23 ℃	%
Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133





		0.3	230℃ × 2.16kg	g/10 min

IZOD Impact Strength	ISO 180




		108	0℉，4mm，Notched	kJ/m²
		734	73℉，1/8"，Notched	kJ/m²

Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	0.9	23℃/23℃	-
Tensile Strength	ISO 527	26	23 ℃，50mm/min	Mpa


Flexural Modulus	ISO 178
Flexural Modulus	ISO 178	1178	23 ℃	Mpa
Rockwell Hardness	ISO 2039-2	R-80	23℃	R-scale
Heat Deflection Temperature	ISO 75/A

		105	Unannealed，0.455Mpa 1/4" 厚，120℃/h	℃





Molding Shrinkage	FCFC Method	1.5 ~ 1.9	23 ℃	%
Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

Hight impact strength, Excellent resistance to low temp. Brittleness,Good luster

B8001A3

Impact Copolymer PP RESIN

Extrusion Grade

PP-B pipe, Thermoforming sheet,Blow molding

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238

		1	230℃ × 2.16kg	g/10 min




IZOD Impact Strength	ASTM D-256
		80	23 ℃，1/8"，Notched	kg-cm/cm




		11	-20℃，4mm，Notched	kg-cm/cm







Specific Gravity	ASTM D-792
		0.9	23℃/23℃	-

Tensile Strength	ASTM D-638
		270	23 ℃，50mm/min	kg/cm²


Tensile Elongation at break	ASTM D-638	>200	23 ℃，50mm/min	%
Tensile Elongation at break	ASTM D-638
Flexural Modulus	ASTM D-790

		11000	23 ℃	kg/cm²

Rockwell Hardness	ASTM D-785	R-80	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648



		105	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955
		1.5 ~ 1.9	-	%


Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133





		0.3	230℃ × 2.16kg	g/10 min

IZOD Impact Strength	ISO 180
		80	23 ℃，1/8"，Notched	kJ/m²



		11	0℉，4mm，Notched	kJ/m²


Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	0.9	23℃/23℃	-
Tensile Strength	ISO 527	26	23 ℃，50mm/min	Mpa


Tensile Elongation at break	ISO 527	>200	23 ℃，50mm/min	%
Flexural Modulus	ISO 178
Flexural Modulus	ISO 178	1178	23 ℃	Mpa
Rockwell Hardness	ISO 2039-2	R-80	23℃	R-scale
Heat Deflection Temperature	ISO 75/A

		105	Unannealed，0.455Mpa 1/4" 厚，120℃/h	℃





Molding Shrinkage	ISO 2577	1.5 ~ 1.9	-	%
Molding Shrinkage	ISO 2577
Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

Excellent impact strength, Excellent resistance to low temp. brittleness

MI(230℃×2.16kg):0.3

Izod(ASTM,1/8"):80

FM(ASTM):11000

TS(ASTM):270

T8002

Impact Copolymer PP RESIN

Extrusion Grade

Corrugated sheet, Bottles, Thermo-forming sheet

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238

		2	230℃ × 2.16kg	g/10 min




IZOD Impact Strength	ASTM D-256
		75	23 ℃，1/8"，Notched	kg-cm/cm




		10.8	-20℃，4mm，Notched	kg-cm/cm







Specific Gravity	ASTM D-792
		0.9	23℃/23℃	-

Tensile Strength	ASTM D-638
		270	23 ℃，50mm/min	kg/cm²


Tensile Elongation at break	ASTM D-638	>200	23 ℃，50mm/min	%
Tensile Elongation at break	ASTM D-638
Flexural Modulus	ASTM D-790

		11000	23 ℃	kg/cm²

Rockwell Hardness	ASTM D-785	R-80	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648




		105	Unannealed，1/4" bar	℃





Molding Shrinkage	FCFC Method	1.5 ~ 1.9	23 ℃	%
Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133





		1	230℃ × 2.16kg	g/10 min

IZOD Impact Strength	ISO 180




		106	0℉，4mm，Notched	kJ/m²
		735	73℉，1/8"，Notched	kJ/m²

Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	0.9	23℃/23℃	-
Tensile Strength	ISO 527	26	23 ℃，50mm/min	Mpa


Tensile Elongation at break	ISO 527	>200	23 ℃，50mm/min	%
Flexural Modulus	ISO 178
Flexural Modulus	ISO 178	1078	23 ℃	Mpa
Rockwell Hardness	ISO 2039-2	R-80	23℃	R-scale
Heat Deflection Temperature	ISO 75/A

		105	Unannealed，0.455Mpa 1/4" 厚，120℃/h	℃





Molding Shrinkage	FCFC Method	1.5 ~ 1.9	23 ℃	%
Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

Hight impact strength,
Excellent resistance to low temp. Brittleness,
Good luster