K4038
Random Copolymer PP RESIN
Injection Molding Grade
Transparency containers,Thin wall products
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 38 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 5 23 ℃，1/8"，Notched kg-cm/cm
5 23 ℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 290 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 11000 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-90 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 95 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.5 ~
2 23 ℃ %
Combustibility
UL-94
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 38 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 49 23 ℃，1/8"，Notched kJ/m²
49 23 ℃，4mm，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 28 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1078 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-90 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 95 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.5 ~
2 23 ℃ %
Combustibility
UL-94
File No. E162823
-
To print, please click on the attached standard physical properties table.
High fluidity, Anti-static, Good Transparency
Please choose
K4515
Random Copolymer PP RESIN
Injection Molding Grade
High transparency container, Transparency housewares, USP Class VI approved
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 6 23 ℃，1/8"，Notched kg-cm/cm
6 23 ℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 310 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 11500 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-95 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 95 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.5 ~
2 23 ℃ %
Flammability
UL-94 1.5-1.65mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 ~ 1.65 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 18 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 59 23 ℃，1/8"，Notched kJ/m²
59 23 ℃，4mm，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 30 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1127 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-95 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 95 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Combustibility
UL-94
HB 1.5 ~ 1.65 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
High Clarity, Anti-static,Good resistance to chemical
Please choose
K4535
Random Copolymer PP RESIN
Injection Molding Grade
High transparency container, Transparency housewares, USP Class VI approved
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 5 23 ℃，1/8"，Notched kg-cm/cm
5 23 ℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 310 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 11500 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-95 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 95 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.5 ~
2 23 ℃ %
Flammability
UL-94 1.5-1.65mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 ~ 1.65 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 35 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 49 23 ℃，1/8"，Notched kJ/m²
49 23 ℃，4mm，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 30 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1127 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-95 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 95 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.5 ~
2 23 ℃ %
Combustibility
UL-94
HB 1.5 ~ 1.65 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
High fluidity, High Clarity, Anti-static, Good resistance to chemical
Please choose
K4650
Random Copolymer PP RESIN
Injection Molding Grade
High transparency container& housewares,
meets the requirements of USP Plastic Class VI
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 50 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 4.5 23 ℃，1/8"，Notched kg-cm/cm
4.5 23 ℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 310 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 11500 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-95 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 95 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.5 ~
2 23 ℃ %
Combustibility
UL-94
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 50 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 44 23 ℃，1/8"，Notched kJ/m²
44 23 ℃，4mm，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 30 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1127 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-95 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 95 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.5 ~
2 23 ℃ %
Combustibility
UL-94
File No. E162823
-
To print, please click on the attached standard physical properties table.
High fluidity, High clarity, anti-static
Please choose
K4715
Random Copolymer PP RESIN
Injection Molding Grade
Super high transparency container& housewares,
meets the requirements of USP Plastic Class VI
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 15 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 6 23 ℃，1/8"，Notched kg-cm/cm
6 23 ℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 310 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 11500 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-95 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 95 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.5 ~
2 23 ℃ %
Flammability
UL-94 1.5mm HB
3.0mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 18 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 59 23 ℃，1/8"，Notched kJ/m²
59 23 ℃，4mm，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 30 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1127 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-95 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 95 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.5 ~
2 23 ℃ %
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
Please choose
K4750
Random Copolymer PP RESIN
Injection Molding Grade
Super high transparency container& housewares
×
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ASTM D-1238 50 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ASTM D-256 4.5 23 ℃，1/8"，Notched kg-cm/cm
4.5 23 ℃，4mm，Notched kg-cm/cm
Specific Gravity
ASTM D-792 0.9 23℃/23℃ -
Tensile Strength
ASTM D-638 310 23 ℃，50mm/min kg/cm²
Tensile Elongation at break
ASTM D-638 >200 23 ℃，50mm/min %
Flexural Modulus
ASTM D-790 1127 23 ℃ kg/cm²
Rockwell Hardness
ASTM D-785 R-95 23 ℃ R-scale
Heat Deflection Temperature
ASTM D-648 95 Unannealed，1/4" bar ℃
Molding Shrinkage
FCFC Method 1.5 ~
2 23 ℃ %
Flammability
UL-94 1.5mm HB
3.0mm HB
All Color FILE NO. E162823 -
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
Property
Test Method
Value
Test Condition
Unit
Melt Flow Index
ISO 1133 50 230℃ × 2.16kg g/10 min
IZOD Impact Strength
ISO 180 44 23 ℃，1/8"，Notched kJ/m²
44 23 ℃，4mm，Notched kJ/m²
Specific Gravity
ISO 1183 0.9 23℃/23℃ -
Tensile Strength
ISO 527 30 23 ℃，50mm/min Mpa
Tensile Elongation at break
ISO 527 >200 23 ℃，50mm/min %
Flexural Modulus
ISO 178 1127 23 ℃ Mpa
Rockwell Hardness
ISO 2039-2 R-95 23℃ R-scale
Heat Deflection Temperature
ISO 75/A 95 Unannealed，0.455Mpa 1/4" 厚，120℃/h ℃
Molding Shrinkage
FCFC Method 1.5 ~
2 23 ℃ %
Combustibility
UL-94
HB 1.5 ~ 3 mm
File No. E162823
-
To print, please click on the attached standard physical properties table.
Super High Clarity, Anti-static
Please choose
Storage and Validity suggestion