Multi- Filament

PP resin (TAIRIPRO® PP resin) using the state of art Gas-Phase processing technologies granted by Chisso, Japan, the high efficient catalyst and the comprehensive quality control system, its yearly capacity is 510,000MTS. The Tairipro product classification contains homo polymer, random and impact copolymer which can be processed by injection, extrusion, blow and vacuum thermoforming. Their application is versatile and adopted in the field of home appliance, AUTO parts, food packages, toys and daily necessities. The R&D center & the full range pilot plant well equipped will be supportive of our new grade development and the setup of the relevant processing guide as well. All production facilities are operated in accordance with strict environmental protection regulation, and waste gases treated by high-heat combustion, then heat recovered. No waste water arises in the polymerization process.

Storage and Validity suggestion

ISO 9001

ISO 14001

TAF ISO IEC 17025_2017_EN

TAF ISO IEC 17025_2017_ZN-TW

Multi- Filament

Model

Applications

Physical

Features

Attach

Operating

S1019

Homopolymer PP RESIN

Multi-Filament Grade

Staple fiber, ES fiber & PP staple fiber

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238

		19	230℃ × 2.16kg	g/10 min




IZOD Impact Strength	ASTM D-256
		2.8	23 ℃，1/8"，Notched	kg-cm/cm
		2.8	23 ℃，4mm，Notched	kg-cm/cm











Specific Gravity	ASTM D-792
		0.9	23℃/23℃	-

Tensile Strength	ASTM D-638
		340	23 ℃，50mm/min	kg/cm²


Tensile Elongation at break	ASTM D-638	>200	23 ℃，50mm/min	%
Tensile Elongation at break	ASTM D-638
Flexural Modulus	ASTM D-790

		14000	23 ℃	kg/cm²

Rockwell Hardness	ASTM D-785	R-100	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648




		110	Unannealed，1/4" bar	℃





Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133





		19	230℃ × 2.16kg	g/10 min

IZOD Impact Strength	ISO 180
		27	23 ℃，1/8"，Notched	kJ/m²
		27	23 ℃，4mm，Notched	kJ/m²





Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	0.9	23℃/23℃	-
Tensile Strength	ISO 527	33	23 ℃，50mm/min	Mpa


Tensile Elongation at break	ISO 527	>200	23 ℃，50mm/min	%
Flexural Modulus	ISO 178
Flexural Modulus	ISO 178	1372	23 ℃	Mpa
Rockwell Hardness	ISO 2039-2	R-100	23℃	R-scale
Heat Deflection Temperature	ISO 75/A

		110	Unannealed，0.455Mpa 1/4" 厚，120℃/h	℃





Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

Controlled rheology, Good softness, Anti gas fading

S1040

Homopolymer PP RESIN

Multi-Filament Grade

Nonwoven, Fine Denier staple fiber　

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238

		40	230℃ × 2.16kg	g/10 min




IZOD Impact Strength	ASTM D-256
		2.3	23 ℃，1/8"，Notched	kg-cm/cm
		2.3	23 ℃，4mm，Notched	kg-cm/cm











Specific Gravity	ASTM D-792
		0.9	23℃/23℃	-

Tensile Strength	ASTM D-638
		350	23 ℃，50mm/min	kg/cm²


Tensile Elongation at break	ASTM D-638	>50	23 ℃，50mm/min	%
Tensile Elongation at break	ASTM D-638
Flexural Modulus	ASTM D-790

		15000	23 ℃	kg/cm²

Rockwell Hardness	ASTM D-785	R-103	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648




		110	Unannealed，1/4" bar	℃





Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133





		34	230℃ × 2.16kg	g/10 min

IZOD Impact Strength	ISO 180
		23	23 ℃，1/8"，Notched	kJ/m²
		23	23 ℃，4mm，Notched	kJ/m²





Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	0.9	23℃/23℃	-
Tensile Strength	ISO 527	34	23 ℃，50mm/min	Mpa


Tensile Elongation at break	ISO 527	>50	23 ℃，50mm/min	%
Flexural Modulus	ISO 178
Flexural Modulus	ISO 178	1470	23 ℃	Mpa
Rockwell Hardness	ISO 2039-2	R-103	23℃	R-scale
Heat Deflection Temperature	ISO 75/A

		110	Unannealed，0.455Mpa 1/4" 厚，120℃/h	℃





Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

Controlled rheology, Compact Spinning, Anti gas fading