Ultra-low Temp resistance copolymer

FCFC PC resin (TAIRILITE® PC Resin) and FIPC PC resin (TARFLON® PC Resin), using the state of phosgene polymerization process from IDEMITSU, JAPAN, with good quality management system. The product had supplied to inject, blow, extrusion molding and other processing industries, due to PC with high physical strength and high transparency, etc. Thus the end product can be widely utilized in home appliances, vehicle lamps and components, food containers, equipment housing, outdoor visor and optics parts. The R&D center & the full laboratory equipment and testing equipment well equipped will be supportivetoour new grade development and the setup ofrelevant processing guideas well. The factory production equipment adopted strict environmental standards, and the production technology is mature and stable, non-polluting theenvironmentconcerns.

PDF Download

ISO 9001 ISO 14001

Ultra-low Temp resistance copolymer

Model

Applications

Features

Attachments

Physical

Comparison

Contact

AC9144

PC RESIN

Ultra-low Temp Resistance Copolymer

Mobile phone / tablet / laptop / 3C products case, sports equipment / protective gear.

Translucency,
Mid flow,
Low temperature impact property, UV resistance,

ASTM Physical
ISO Physical

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238	13	300℃×1.2kg	g/10 min






IZOD Impact Strength	ASTM D-256


		75	23℃, 3.2mm, Notched	kg-cm/cm










Specific Gravity	ASTM D-792	1.18	23℃	-


Tensile Strength	ASTM D-638
		600	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790
		1000	23 ℃, 2mm/min	kg/cm²


Flexural Modulus	ASTM D-790
		21000	23 ℃, 2mm/min	kg/cm²


Rockwell Hardness	ASTM D-785	R-120	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648	120	Unannealed, 18.6kg/cm², 3.2mm, 120℃/h	℃










Molding Shrinkage	ASTM D-955
		0.6 ~ 0.8	-	%


Combustibility	UL-94	v-2 2 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Combustibility	UL-94	v-2 2 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

AC9140

PC RESIN

Ultra-low Temp Resistance Copolymer

Mobile phone / tablet / laptop / 3C products case, sports equipment / protective gear.

Transparency,
Mid flow,
Low temperature impact property, UV resistance,

ASTM Physical
ISO Physical

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238	13	300℃×1.2kg	g/10 min






IZOD Impact Strength	ASTM D-256


		65	23℃, 3.2mm, Notched	kg-cm/cm










Specific Gravity	ASTM D-792	1.18	23℃	-


Tensile Strength	ASTM D-638
		600	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790
		1000	23 ℃, 2mm/min	kg/cm²


Flexural Modulus	ASTM D-790
		21000	23 ℃, 2mm/min	kg/cm²


Rockwell Hardness	ASTM D-785	R-120	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648	120	Unannealed, 18.6kg/cm², 3.2mm, 120℃/h	℃










Molding Shrinkage	ASTM D-955
		0.6 ~ 0.8	-	%


Transmissin	ASTM D-1003	> 87	3.2mm	%
Haze	ASTM D-1003	< 1.0	3.2mm	%
Flammability	UL94 / UL746B / UL746C	2.0mm V2 RTI 80℃ All Color	FILE NO. E162823	-
Combustibility	UL-94	v-2 2 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133
		13	300℃ × 1.2kg	g/10 min






Charpy Impact Strength	ISO 179


		60	23℃, 4mm, Notched	kJ/m²
Specific Gravity	ISO 1183	1.18	23℃	-
Specific Gravity	ISO 1183
Tensile Strength	ISO 527	60	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	98	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2060	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-120	23℃	R-scale
Heat Deflection Temperature	ISO 75/A


		120	Unannealed, 1.8Mpa, 4mm, 120℃/h	℃




Molding Shrinkage	ISO 2577	0.6 ~ 0.8	-	%
Molding Shrinkage	ISO 2577
Transmissin	ISO 13468/1	> 87	3.2mm	%
Haze	ISO 14782	< 1.0	3.2mm	%
Combustibility	UL-94	v-2 2 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

AC9144

PC RESIN

Ultra-low Temp Resistance Copolymer

Mobile phone / tablet / laptop / 3C products case, sports equipment / protective gear.

Translucency,
Mid flow,
Low temperature impact property, UV resistance,

ASTM Physical
ISO Physical

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238	13	300℃×1.2kg	g/10 min






IZOD Impact Strength	ASTM D-256


		75	23℃, 3.2mm, Notched	kg-cm/cm










Specific Gravity	ASTM D-792	1.18	23℃	-


Tensile Strength	ASTM D-638
		600	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790
		1000	23 ℃, 2mm/min	kg/cm²


Flexural Modulus	ASTM D-790
		21000	23 ℃, 2mm/min	kg/cm²


Rockwell Hardness	ASTM D-785	R-120	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648	120	Unannealed, 18.6kg/cm², 3.2mm, 120℃/h	℃










Molding Shrinkage	ASTM D-955
		0.6 ~ 0.8	-	%


Combustibility	UL-94	v-2 2 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133
		13	300℃ × 1.2kg	g/10 min






Specific Gravity	ISO 1183	1.18	23℃	-
Specific Gravity	ISO 1183
Tensile Strength	ISO 527	60	23 ℃，50mm/min	Mpa

		0	23 ℃，20mm/min	Mpa
Flexural Strength	ISO 178	98	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2060	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-120	23℃	R-scale
Heat Deflection Temperature	ISO 75/A


		120	Unannealed, 1.8Mpa, 4mm, 120℃/h	℃




Molding Shrinkage	ISO 2577	0.6 ~ 0.8	-	%
Molding Shrinkage	ISO 2577
Combustibility	UL-94	v-2 2 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

AC9830

PC RESIN

Ultra-low Temp Resistance Copolymer

Mobile equipment housing, Connectors, Switches, Outdoor equipment component, Battery pack.

Translucency,
Mid flow,
Flame retardant,
Low temperature impact property, UV resistance,

ASTM Physical
ISO Physical

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238	12	300℃×1.2kg	g/10 min






IZOD Impact Strength	ASTM D-256


		75	23℃, 3.2mm, Notched	kg-cm/cm










Specific Gravity	ASTM D-792	1.2	23℃	-


Tensile Strength	ASTM D-638
		680	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790
		1000	23 ℃, 2mm/min	kg/cm²


Flexural Modulus	ASTM D-790
		21000	23 ℃, 2mm/min	kg/cm²


Rockwell Hardness	ASTM D-785	R-120	23 ℃	R-scale
Heat Deflection Temperature	ASTM D-648	125	Unannealed, 18.6kg/cm², 3.2mm, 120℃/h	℃










Molding Shrinkage	ASTM D-955
		0.4 ~ 0.8	-	%


Combustibility	UL-94	v-0 1.5 mm 5VA 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133
		12	300℃ × 1.2kg	g/10 min






Charpy Impact Strength	ISO 179


		70	23℃, 4mm, Notched	kJ/m²
Specific Gravity	ISO 1183	1.2	23℃	-
Specific Gravity	ISO 1183
Tensile Strength	ISO 527	67	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	98	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2058	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-120	23℃	R-scale
Heat Deflection Temperature	ISO 75/A


		125	Unannealed, 1.8Mpa, 4mm, 120℃/h	℃




Molding Shrinkage	ISO 2577	0.4 ~ 0.8	-	%
Molding Shrinkage	ISO 2577
Combustibility	UL-94	v-0 1.5 mm 5VA 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.