TAIRIREX PS Resin - Polystyrene Resin

PS Resin(Taiwan)

TAIRIREX® PS Resin (Polystyrene), utilizing the techniques from FINA in USA and our own developed improved techniques, there are two plants in production, which is HSIN-KANG and MAI-LIAO, its yearly capacity is 320,000MTS, the major ingredients come from our own sixth naphtha cracking project, this will ensure the stability of quality with competitive price. TAIRIREX® PS Resin diversification contains general purpose (GPPS), which is crystal and easy processing and high impact (HIPS) that has low GEL and residual monomer. All production facilities are operated in accordance with strict environmental protection regulation and non-polluting the environment concerns.

Hsin-Kang PABS Plant ISO 9001 、 ISO 14001

Mai-Liao PABS Plant ISO 9001 、ISO 14001

GPPS (General Purpose PS)
HIPS (High Impact PS)

Model

Applications

Physical

Features

Attach

Operating

GP5000

PS RESIN

General Purpose Grade

TRP blending, Thin sheet injection

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238





		10	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256




		1.6	23 ℃，1/4"，Notched	kg-cm/cm








Tensile Strength	ASTM D-638	410	23 ℃，5mm/min	kg/cm²



Tensile Modulus	ASTM D-638	33000	23 ℃，1mm/min	kg/cm²
Tensile Elongation	ASTM D-638	2	23 ℃，5mm/min	%
Tensile Elongation	ASTM D-638
Flexural Strength	ASTM D-790


		780	23 ℃，1.2mm/min	kg/cm²
Flexural Modulus	ASTM D-790


		31000	23 ℃，1.2mm/min	kg/cm²
Vicat Softening Point	ASTM D-1525

		94	Annealed 80℃*2hr 1/8" ，10N 50℃/h	℃


Reidual Monomer		700	-	ppm max
Heat Deflection Temperature	ASTM D-648





		83	Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8"	℃




Flammability	UL-94	1.5-1.7mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133	10	200℃ × 5kg 49N	g/10min







IZOD Impact Strength	ISO 180



		1.6	23 ℃，4mm，Unnotched	kJ/m²



Charpy Impact Strength	ISO 179
		8.7	23℃，4mm GPPS無缺口，HIPS有缺口	kJ/m²


Tensile Strength	ISO 527

		42	23 ℃，20mm/min	Mpa
Tensile Modulus	ISO 527	3400	23 ℃，1mm/min	Mpa
Tensile Elongation	ISO 527	3	23 ℃，20mm/min	%
Flexural Strength	ISO 178	72	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	3000	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Reidual Monomer		700	-	ppm max
Vicat Softening Point	ISO 306

		94	Annealed 80℃*2hr， 4mm，10N 50℃/h	℃

Heat Deflection Temperature	ISO 75/A





		89	Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm	℃

Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

High flow Injection molding

GP5250

PS RESIN

General Purpose Grade

Food containers, Stationery, Toys, Clothing hangers, Lamp decoration, CD, Cosmetic cases

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238





		6.7	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256




		1.7	23 ℃，1/4"，Notched	kg-cm/cm








Tensile Strength	ASTM D-638	430	23 ℃，5mm/min	kg/cm²



Tensile Modulus	ASTM D-638	31000	23 ℃，1mm/min	kg/cm²
Tensile Elongation	ASTM D-638	2	23 ℃，5mm/min	%
Tensile Elongation	ASTM D-638
Flexural Strength	ASTM D-790


		850	23 ℃，1.2mm/min	kg/cm²
Flexural Modulus	ASTM D-790


		31000	23 ℃，1.2mm/min	kg/cm²
Vicat Softening Point	ASTM D-1525

		95	Annealed 80℃*2hr 1/8" ，10N 50℃/h	℃


Reidual Monomer		700	-	ppm max
Heat Deflection Temperature	ASTM D-648





		86	Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8"	℃




Flammability	UL-94	1.5-1.7mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94	HB 1.5 ~ 1.7 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133	6.7	200℃ × 5kg 49N	g/10min







IZOD Impact Strength	ISO 180



		1.6	23 ℃，4mm，Unnotched	kJ/m²



Charpy Impact Strength	ISO 179
		7.4	23℃，4mm GPPS無缺口，HIPS有缺口	kJ/m²


Tensile Strength	ISO 527

		41	23 ℃，20mm/min	Mpa
Tensile Modulus	ISO 527	3300	23 ℃，1mm/min	Mpa
Tensile Elongation	ISO 527	3	23 ℃，20mm/min	%
Flexural Strength	ISO 178	70	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	3200	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Vicat Softening Point	ISO 306

		95	Annealed 80℃*2hr， 4mm，10N 50℃/h	℃

Heat Deflection Temperature	ISO 75/A





		91	Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm	℃

Combustibility	UL-94	HB 1.5 ~ 1.7 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

Injection molding

GP525N

PS RESIN

General Purpose Grade

Food containers, Stationery, Toys, Clothing hangers, Lamp decoration, CD, Cosmetic cases

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238





		6.7	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256




			23 ℃，1/4"，Notched	kg-cm/cm








Tensile Strength	ASTM D-638	430	23 ℃，5mm/min	kg/cm²



Tensile Modulus	ASTM D-638	31000	23 ℃，1mm/min	kg/cm²
Tensile Elongation	ASTM D-638	2	23 ℃，5mm/min	%
Tensile Elongation	ASTM D-638
Flexural Strength	ASTM D-790


		870	23 ℃，1.2mm/min	kg/cm²
Flexural Modulus	ASTM D-790


		31000	23 ℃，1.2mm/min	kg/cm²
Vicat Softening Point	ASTM D-1525

		95	Annealed 80℃*2hr 1/8" ，10N 50℃/h	℃


Reidual Monomer		700	-	ppm max
Heat Deflection Temperature	ASTM D-648





		87	Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8"	℃




Flammability	UL-94	1.5-1.7mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94	HB 1.5 ~ 1.7 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133	6.7	200℃ × 5kg 49N	g/10min







IZOD Impact Strength	ISO 180



		1.6	23 ℃，4mm，Unnotched	kJ/m²



Charpy Impact Strength	ISO 179
		7.4	23℃，4mm GPPS無缺口，HIPS有缺口	kJ/m²


Tensile Strength	ISO 527

		41	23 ℃，20mm/min	Mpa
Tensile Modulus	ISO 527	3300	23 ℃，1mm/min	Mpa
Tensile Elongation	ISO 527	3	23 ℃，20mm/min	%
Flexural Strength	ISO 178	70	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	3200	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Reidual Monomer		7000	-	ppm max
Vicat Softening Point	ISO 306

		95	Annealed 80℃*2hr， 4mm，10N 50℃/h	℃

Heat Deflection Temperature	ISO 75/A





		91	Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm	℃

Combustibility	UL-94	HB 1.5 ~ 1.7 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

Injection molding

GP5350

PS RESIN

General Purpose Grade

Kitchen ware, Lamp covers, Decorated sheets, Toys

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238





		4.5	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256




		1.8	23 ℃，1/4"，Notched	kg-cm/cm








Tensile Strength	ASTM D-638	450	23 ℃，5mm/min	kg/cm²



Tensile Modulus	ASTM D-638	32000	23 ℃，1mm/min	kg/cm²
Tensile Elongation	ASTM D-638	2	23 ℃，5mm/min	%
Tensile Elongation	ASTM D-638
Flexural Strength	ASTM D-790


		900	23 ℃，1.2mm/min	kg/cm²
Flexural Modulus	ASTM D-790


		31000	23 ℃，1.2mm/min	kg/cm²
Vicat Softening Point	ASTM D-1525

		98	Annealed 80℃*2hr 1/8" ，10N 50℃/h	℃


Reidual Monomer		700	-	ppm max
Heat Deflection Temperature	ASTM D-648





		90	Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8"	℃




Flammability	UL-94	1.5-1.7mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94	HB 1.5 ~ 1.7 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133	4.5	200℃ × 5kg 49N	g/10min







IZOD Impact Strength	ISO 180



		1.6	23 ℃，4mm，Unnotched	kJ/m²



Charpy Impact Strength	ISO 179
		10.8	23℃，4mm GPPS無缺口，HIPS有缺口	kJ/m²


Tensile Strength	ISO 527

		44	23 ℃，20mm/min	Mpa
Tensile Modulus	ISO 527	3300	23 ℃，1mm/min	Mpa
Tensile Elongation	ISO 527	3	23 ℃，20mm/min	%
Flexural Strength	ISO 178	76	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	3100	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Reidual Monomer		700	-	ppm max
Vicat Softening Point	ISO 306

		100	Annealed 80℃*2hr， 4mm，10N 50℃/h	℃

Heat Deflection Temperature	ISO 75/A





		95	Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm	℃

Combustibility	UL-94	HB 1.5 ~ 1.7 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

High heat resistance

GP535A

PS RESIN

General Purpose Grade

Kitchen ware, Lamp covers, Decorated sheets, Toys

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238





		4.3	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256




		1.8	23 ℃，1/4"，Notched	kg-cm/cm








Tensile Strength	ASTM D-638	480	23 ℃，5mm/min	kg/cm²



Tensile Modulus	ASTM D-638	32000	23 ℃，1mm/min	kg/cm²
Tensile Elongation	ASTM D-638	2	23 ℃，5mm/min	%
Tensile Elongation	ASTM D-638
Flexural Strength	ASTM D-790


		930	23 ℃，1.2mm/min	kg/cm²
Flexural Modulus	ASTM D-790


		31000	23 ℃，1.2mm/min	kg/cm²
Vicat Softening Point	ASTM D-1525

		96	Annealed 80℃*2hr 1/8" ，10N 50℃/h	℃


Reidual Monomer		700	-	ppm max
Heat Deflection Temperature	ASTM D-648





		89	Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8"	℃




Flammability	UL-94	1.5-1.7mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94	HB 1.5 ~ 1.7 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133	4.3	200℃ × 5kg 49N	g/10min







IZOD Impact Strength	ISO 180



		1.6	23 ℃，4mm，Unnotched	kJ/m²



Charpy Impact Strength	ISO 179
		7.2	23℃，4mm GPPS無缺口，HIPS有缺口	kJ/m²


Tensile Strength	ISO 527

		43	23 ℃，20mm/min	Mpa
Tensile Modulus	ISO 527	3300	23 ℃，1mm/min	Mpa
Tensile Elongation	ISO 527	3	23 ℃，20mm/min	%
Flexural Strength	ISO 178	74	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	3100	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Reidual Monomer		700	-	ppm max
Vicat Softening Point	ISO 306

		98	Annealed 80℃*2hr， 4mm，10N 50℃/h	℃

Heat Deflection Temperature	ISO 75/A





		94	Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm	℃

Combustibility	UL-94	HB 1.5 ~ 1.7 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

High heat resistance

GP535N

PS RESIN

General Purpose Grade

Kitchen wave, Lamp covers, Decorated sheets, Toys

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238





		4.5	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	1.8	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792	1.04	23℃	-


Tensile Strength	ASTM D-638

		450	23 ℃	kg/cm²

Tensile Modulus	ASTM D-638	32000	23 ℃，1mm/min	kg/cm²
Tensile Elongation	ASTM D-638	2	23 ℃，5mm/min	%
Tensile Elongation	ASTM D-638
Flexural Strength	ASTM D-790

		890	23 ℃	kg/cm²

Flexural Modulus	ASTM D-790

		31000	23 ℃	kg/cm²

Vicat Softening Point	ASTM D-1525

		93	Annealed 80℃*2hr 1/8" ，10N 50℃/h	℃


Reidual Monomer		700	-	ppm max
Heat Deflection Temperature	ASTM D-648





		90	Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8"	℃




Combustibility	UL-94	HB 1.5 ~ 1.7 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		3.5	200℃ × 5kg	g/10 min





Specific Gravity	ISO 1183	1.04	23℃	-
Specific Gravity	ISO 1183
Tensile Modulus	ISO 527	3136	23 ℃，1mm/min	Mpa
Tensile Elongation	ISO 527	2	23 ℃，20mm/min	%
Flexural Strength	ISO 178
Flexural Strength	ISO 178	88	23 ℃	Mpa
Flexural Modulus	ISO 178
Flexural Modulus	ISO 178	3136	23 ℃	Mpa
Reidual Monomer		700	-	ppm max
Vicat Softening Point	ISO 306

		98	Annealed 80℃*2hr， 4mm，10N 50℃/h	℃

Heat Deflection Temperature	ISO 75/A





		93	Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm	℃

Combustibility	UL-94	HB 1.5 ~ 1.7 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

MI(200℃×5kg):3.5

Izod (ASTM,1/4"):1.8

FM(ASTM):32000

TS(ASTM):450

High heat

GP5500

PS RESIN

General Purpose Grade

PSP sheets, OPS,Medicine containers

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238





		2.6	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256




		1.8	23 ℃，1/4"，Notched	kg-cm/cm








Tensile Strength	ASTM D-638	500	23 ℃，5mm/min	kg/cm²



Tensile Modulus	ASTM D-638	32000	23 ℃，1mm/min	kg/cm²
Tensile Elongation	ASTM D-638	2	23 ℃，5mm/min	%
Tensile Elongation	ASTM D-638
Flexural Strength	ASTM D-790


		1050	23 ℃，1.2mm/min	kg/cm²
Flexural Modulus	ASTM D-790


		31000	23 ℃，1.2mm/min	kg/cm²
Vicat Softening Point	ASTM D-1525

		104	Annealed 80℃*2hr 1/8" ，10N 50℃/h	℃


Reidual Monomer		700	-	ppm max
Heat Deflection Temperature	ASTM D-648





		95	Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8"	℃




Flammability	UL-94	1.5-1.7mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94	HB 1.5 ~ 1.7 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133	2.6	200℃ × 5kg 49N	g/10min







IZOD Impact Strength	ISO 180



		1.6	23 ℃，4mm，Unnotched	kJ/m²



Charpy Impact Strength	ISO 179
		9.5	23℃，4mm GPPS無缺口，HIPS有缺口	kJ/m²


Tensile Strength	ISO 527

		47	23 ℃，20mm/min	Mpa
Tensile Modulus	ISO 527	3400	23 ℃，1mm/min	Mpa
Tensile Elongation	ISO 527	3	23 ℃，20mm/min	%
Flexural Strength	ISO 178	85	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	3100	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Vicat Softening Point	ISO 306

		103	Annealed 80℃*2hr， 4mm，10N 50℃/h	℃

Heat Deflection Temperature	ISO 75/A





		98	Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm	℃

Combustibility	UL-94	HB 1.5 ~ 1.7 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

High molecular weight

GP550N

PS RESIN

General Purpose Grade

PSP sheets, XPS sheets, OPS,Medicine containers

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238





		2.6	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256




		1.8	23 ℃，1/4"，Notched	kg-cm/cm








Tensile Strength	ASTM D-638	510	23 ℃，5mm/min	kg/cm²



Tensile Modulus	ASTM D-638	32000	23 ℃，1mm/min	kg/cm²
Tensile Elongation	ASTM D-638	2	23 ℃，5mm/min	%
Tensile Elongation	ASTM D-638
Flexural Strength	ASTM D-790


		1060	23 ℃，1.2mm/min	kg/cm²
Flexural Modulus	ASTM D-790


		31000	23 ℃，1.2mm/min	kg/cm²
Vicat Softening Point	ASTM D-1525

		104	Annealed 80℃*2hr 1/8" ，10N 50℃/h	℃


Reidual Monomer		700	-	ppm max
Heat Deflection Temperature	ASTM D-648





		95	Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8"	℃




Flammability	UL-94	1.5-1.7mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94	HB 1.5 ~ 1.7 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133	2.6	200℃ × 5kg 49N	g/10min







IZOD Impact Strength	ISO 180



		1.6	23 ℃，4mm，Unnotched	kJ/m²



Charpy Impact Strength	ISO 179
		9.5	23℃，4mm GPPS無缺口，HIPS有缺口	kJ/m²


Tensile Strength	ISO 527

		48	23 ℃，20mm/min	Mpa
Tensile Modulus	ISO 527	3400	23 ℃，1mm/min	Mpa
Tensile Elongation	ISO 527	3	23 ℃，20mm/min	%
Flexural Strength	ISO 178	84	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	3000	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Reidual Monomer		700	-	ppm max
Vicat Softening Point	ISO 306

		103	Annealed 80℃*2hr， 4mm，10N 50℃/h	℃

Heat Deflection Temperature	ISO 75/A





		98	Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm	℃

Combustibility	UL-94	HB 1.5 ~ 1.7 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

High molecular weight

Model

Applications

Physical

Features

Attach

Operating

HP835G

PS RESIN

High Impact Grade

Housing for electrical appliances, Baby car parts,Housings of LCD Monitor,Exercise appliances

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238





		3.7	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256




		11	23 ℃，1/4"，Notched	kg-cm/cm








Tensile Strength	ASTM D-638	280	23 ℃，5mm/min	kg/cm²



Tensile Modulus	ASTM D-638	22000	23 ℃，1mm/min	kg/cm²
Tensile Elongation	ASTM D-638	55	23 ℃，5mm/min	%
Tensile Elongation	ASTM D-638
Flexural Strength	ASTM D-790


		550	23 ℃，1.2mm/min	kg/cm²
Flexural Modulus	ASTM D-790


		23000	23 ℃，1.2mm/min	kg/cm²
Vicat Softening Point	ASTM D-1525

		101	Annealed 80℃*2hr 1/8" ，10N 50℃/h	℃


Reidual Monomer		700	-	ppm max
Heat Deflection Temperature	ASTM D-648





		89	Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8"	℃




Combustibility	UL-94	HB 1 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133	3.7	200℃ × 5kg 49N	g/10min







IZOD Impact Strength	ISO 180



		10.8	23 ℃，4mm，Unnotched	kJ/m²



Charpy Impact Strength	ISO 179
		8	23℃，4mm GPPS無缺口，HIPS有缺口	kJ/m²


Tensile Strength	ISO 527

		28	23 ℃，20mm/min	Mpa
Tensile Modulus	ISO 527	2400	23 ℃，1mm/min	Mpa
Tensile Elongation	ISO 527	38	23 ℃，20mm/min	%
Flexural Strength	ISO 178	54	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2300	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Reidual Monomer		700	-	ppm max
Vicat Softening Point	ISO 306

		101	Annealed 80℃*2hr， 4mm，10N 50℃/h	℃

Heat Deflection Temperature	ISO 75/A





		94	Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm	℃

Combustibility	UL-94	HB 1 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

High impact, Normal flow

HP8250

PS RESIN

High Impact Grade

Housing for electrical appliances, Baby car parts,Housings of LCD Monitor,Exercise appliances

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238





		5.5	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256




		13	23 ℃，1/4"，Notched	kg-cm/cm








Tensile Strength	ASTM D-638	240	23 ℃，5mm/min	kg/cm²



Tensile Modulus	ASTM D-638	22000	23 ℃，1mm/min	kg/cm²
Tensile Elongation	ASTM D-638	53	23 ℃，5mm/min	%
Tensile Elongation	ASTM D-638
Flexural Strength	ASTM D-790


		450	23 ℃，1.2mm/min	kg/cm²
Flexural Modulus	ASTM D-790


		21000	23 ℃，1.2mm/min	kg/cm²
Vicat Softening Point	ASTM D-1525

		101	Annealed 80℃*2hr 1/8" ，10N 50℃/h	℃


Reidual Monomer		700	-	ppm max
Heat Deflection Temperature	ASTM D-648





		89	Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8"	℃




Flammability	UL-94	0.8mm HB 1.0mm HB 1.5mm HB 3.0mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133	5.5	200℃ × 5kg 49N	g/10min







IZOD Impact Strength	ISO 180



		11	23 ℃，4mm，Unnotched	kJ/m²



Charpy Impact Strength	ISO 179
		8.5	23℃，4mm GPPS無缺口，HIPS有缺口	kJ/m²


Tensile Strength	ISO 527

		24	23 ℃，20mm/min	Mpa
Tensile Modulus	ISO 527	2200	23 ℃，1mm/min	Mpa
Tensile Elongation	ISO 527	33	23 ℃，20mm/min	%
Flexural Strength	ISO 178	41	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2200	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Reidual Monomer		700	-	ppm max
Vicat Softening Point	ISO 306

		98	Annealed 80℃*2hr， 4mm，10N 50℃/h	℃

Heat Deflection Temperature	ISO 75/A





		96	Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm	℃

Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

High impact, Normal flow

HP825F

PS RESIN

High Impact Grade

Housing for electrical appliances, Baby car parts,Housings of LCD Monitor,Exercise appliances

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238





		9.0	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256




		12	23 ℃，1/4"，Notched	kg-cm/cm








Tensile Strength	ASTM D-638	250	23 ℃，5mm/min	kg/cm²



Tensile Modulus	ASTM D-638	24000	23 ℃，1mm/min	kg/cm²
Tensile Elongation	ASTM D-638	45	23 ℃，5mm/min	%
Tensile Elongation	ASTM D-638
Flexural Strength	ASTM D-790


		460	23 ℃，1.2mm/min	kg/cm²
Flexural Modulus	ASTM D-790


		23000	23 ℃，1.2mm/min	kg/cm²
Vicat Softening Point	ASTM D-1525

		100	Annealed 80℃*2hr 1/8" ，10N 50℃/h	℃


Reidual Monomer		700	-	ppm max
Heat Deflection Temperature	ASTM D-648





		90	Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8"	℃




Flammability	UL-94	1.5mm HB 3.0mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133	9	200℃ × 5kg 49N	g/10min







IZOD Impact Strength	ISO 180



		10	23 ℃，4mm，Unnotched	kJ/m²



Charpy Impact Strength	ISO 179
		9.6	23℃，4mm GPPS無缺口，HIPS有缺口	kJ/m²


Tensile Strength	ISO 527

		26	23 ℃，20mm/min	Mpa
Tensile Modulus	ISO 527	2300	23 ℃，1mm/min	Mpa
Tensile Elongation	ISO 527	33	23 ℃，20mm/min	%
Flexural Strength	ISO 178	46	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2400	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Reidual Monomer		700	-	ppm max
Vicat Softening Point	ISO 306

		99	Annealed 80℃*2hr， 4mm，10N 50℃/h	℃

Heat Deflection Temperature	ISO 75/A





		96	Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm	℃

Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

High flow

HP9450

PS RESIN

High Impact Grade

HP sheets, Disposable dishware,Electronic Packaging, Cable reels

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238





		3.0	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256




		15	23 ℃，1/4"，Notched	kg-cm/cm








Tensile Strength	ASTM D-638	250	23 ℃，5mm/min	kg/cm²



Tensile Modulus	ASTM D-638	22000	23 ℃，1mm/min	kg/cm²
Tensile Elongation	ASTM D-638	52	23 ℃，5mm/min	%
Tensile Elongation	ASTM D-638
Flexural Strength	ASTM D-790


		470	23 ℃，1.2mm/min	kg/cm²
Flexural Modulus	ASTM D-790


		22000	23 ℃，1.2mm/min	kg/cm²
Vicat Softening Point	ASTM D-1525

		100	Annealed 80℃*2hr 1/8" ，10N 50℃/h	℃


Reidual Monomer		700	-	ppm max
Heat Deflection Temperature	ASTM D-648





		90	Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8"	℃




Flammability	UL-94	1.5-1.7mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94	HB 1.5 ~ 1.7 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133	3	200℃ × 5kg 49N	g/10min







IZOD Impact Strength	ISO 180



		12.2	23 ℃，4mm，Unnotched	kJ/m²



Tensile Strength	ISO 527

		25	23 ℃，20mm/min	Mpa
Tensile Modulus	ISO 527	2200	23 ℃，1mm/min	Mpa
Tensile Elongation	ISO 527	39	23 ℃，20mm/min	%
Flexural Strength	ISO 178	44	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2400	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Reidual Monomer		700	-	ppm max
Vicat Softening Point	ISO 306

		99	Annealed 80℃*2hr， 4mm，10N 50℃/h	℃

Heat Deflection Temperature	ISO 75/A





		94	Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm	℃

Combustibility	UL-94	HB 1.5 ~ 1.7 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

Super high impact

MP6500

PS RESIN

High Impact Grade

Stationery, Toys,Parts for home electrical appliances, Clothing hangers, Clock housing, FRP blending

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238





		7.0	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256




		8	23 ℃，1/4"，Notched	kg-cm/cm








Tensile Strength	ASTM D-638	290	23 ℃，5mm/min	kg/cm²



Tensile Modulus	ASTM D-638	24000	23 ℃，1mm/min	kg/cm²
Tensile Elongation	ASTM D-638	40	23 ℃，5mm/min	%
Tensile Elongation	ASTM D-638
Flexural Strength	ASTM D-790


		560	23 ℃，1.2mm/min	kg/cm²
Flexural Modulus	ASTM D-790


		23000	23 ℃，1.2mm/min	kg/cm²
Vicat Softening Point	ASTM D-1525

		100	Annealed 80℃*2hr 1/8" ，10N 50℃/h	℃


Reidual Monomer		700	-	ppm max
Heat Deflection Temperature	ASTM D-648





		91	Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8"	℃




Flammability	UL-94	1.5-1.7mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94	HB 1.5 ~ 1.7 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133	7	200℃ × 5kg 49N	g/10min







IZOD Impact Strength	ISO 180



		5.6	23 ℃，4mm，Unnotched	kJ/m²



Charpy Impact Strength	ISO 179
		5.8	23℃，4mm GPPS無缺口，HIPS有缺口	kJ/m²


Tensile Strength	ISO 527

		30	23 ℃，20mm/min	Mpa
Tensile Modulus	ISO 527	2600	23 ℃，1mm/min	Mpa
Tensile Elongation	ISO 527	27	23 ℃，20mm/min	%
Flexural Strength	ISO 178	51	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2400	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Reidual Monomer		700	-	ppm max
Vicat Softening Point	ISO 306

		98	Annealed 80℃*2hr， 4mm，10N 50℃/h	℃

Heat Deflection Temperature	ISO 75/A





		94	Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm	℃

Combustibility	UL-94	HB 1.5 ~ 1.7 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

Medium impact