TAIRILAC ABS Resin - Acrylonitrile Butadiene Styrene

ABS Resin(Taiwan)

FCFC ABS Resin （TAIRILAC® ABS Resin）, there are two plants in production, which is HSIN-KANG and MAI-LIAO, its yearly capacity is 410,000MTS, the major ingredients come from our own sixth naphtha cracking project, this will ensure the stability of quality with competitive price. FCFC ABS Resin product diversification contains general purpose, extrusion, jet black, high flow, heat resistance, flame retardant, transparent and metal plating that can fulfill the needs of. All production facilities are operated in accordance with strict environmental protection regulation, and waste gases treated by high-heat combustion, then heat recovered.

Hsin-Kang PABS Plant ISO 9001 、 ISO 14001

Mai-Liao PABS Plant ISO 9001 、 ISO 14001

Jet Black Extrusion Grade
General Grade
Jet Black General Grade
High Flow Grade
Heat Resistant Grade
Metal Plating Grade
Extrusion Grade
Self Extinguishing Grade
Health Care Grade
20%GF Reinforced Grade

Model

Applications

Physical

Features

Attach

Operating

AE10EP

ABS RESIN

Jet Black Extrusion Grade

Pipes

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		5	220℃ × 10kg	g/10 min





IZOD Impact Strength	ASTM D-256	48	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792	1.05	23℃	-


Tensile Strength	ASTM D-638
		392	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	660	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	21000	23 ℃，15mm/min	kg/cm²



Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133






		4.9	220℃ × 10kg	g/10 min
IZOD Impact Strength	ISO 180	48	23℃, 4mm	kJ/m²







Tensile Strength	ISO 527
		37	23 ℃	Mpa

Flexural Strength	ISO 178
Flexural Strength	ISO 178	51	23 ℃	Mpa
Flexural Modulus	ISO 178
Flexural Modulus	ISO 178	21000	23 ℃	Mpa
Rockwell Hardness	ISO 2039-2	R-97	23℃	R-scale
Heat Deflection Temperature	ISO 75/A	86	Unannealed，1.8Mpa 4mm厚，120℃/h	℃







Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

MI(220℃×10kg): 5.7

Izod (ASTM,1/4"): 41

FM(ASTM): 20000

TS(ASTM): 370

Extrusion molding,

Super high impact,

High rigid

Model

Applications

Physical

Features

Attach

Operating

AG100H

ABS RESIN

General Grade

Helmets, Shoe heels, Pipe fittings, Products of low-temp usage

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		8	220℃ × 10kg	g/10 min





IZOD Impact Strength	ASTM D-256	41	23 ℃，1/4"，Notched	kg-cm/cm













Tensile Strength	ASTM D-638
		370	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	620	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	19000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-95	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	95	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		93	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		83	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133






		8	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	40	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183	1.04	23℃	-
Specific Gravity	ISO 1183
Tensile Strength	ISO 527	38	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	55	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	1800	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-95	23℃	R-scale
Vicat Softening Point	ISO 306	95	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		87	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

Super high impact

AG15E1

ABS RESIN

General Grade

Toys, Calculators, Phone,Clock housing,Stereo housing, Suitcase

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		25	220℃ × 10kg	g/10 min




		2.4	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	19	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.05	23℃/23℃	-

Tensile Strength	ASTM D-638
		480	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	840	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	26000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-111	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	95	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		96	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		86	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Combustibility	UL-94	HB 1.6 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		2.4	200℃ × 5kg	g/10 min




		25	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	16	23 ℃，4mm厚，Notched	kJ/m²



Tensile Strength	ISO 527	46	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	70	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2500	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-111	23℃	R-scale
Vicat Softening Point	ISO 306	95	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		91	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.6 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

High gloss,
High rigid

AG15E3

ABS RESIN

General Grade

Toys, Calculators, Phone,Clock housing,Stereo housing, Suitcase

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		18	220℃ × 10kg	g/10 min




		1.6	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	18	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792	0	23℃	-


Tensile Strength	ASTM D-638
		500	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	860	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	26000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-111	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	93	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		95	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		85	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		1.6	200℃ × 5kg	g/10 min




		18	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	18	23 ℃，4mm厚，Notched	kJ/m²



Tensile Strength	ISO 527	49	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	72	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2500	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-111	23℃	R-scale
Vicat Softening Point	ISO 306	93	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		90	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

High gloss, High rigid

AG15A3

ABS RESIN

General Grade

Toys, Calculators, Phone,Clock housing,Stereo housing, Suitcase

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		22	220℃ × 10kg	g/10 min




		2.2	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	24	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.05	23℃/23℃	-

Tensile Strength	ASTM D-638
		470	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	820	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	25000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-109	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	94	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		95	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		85	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Combustibility	UL-94	HB 1 ~ 1.65 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		2.2	200℃ × 5kg	g/10 min




		22	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	26	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.05	23℃/23℃	-
Tensile Strength	ISO 527	41	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	60	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2400	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Vicat Softening Point	ISO 306	94	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		90	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1 ~ 1.65 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

High gloss, Medium impact

AG15A1-H

ABS RESIN

General Grade

Toys, Calculators, Phone,Clock housing,Stereo housing, Suitcase

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		21	220℃ × 10kg	g/10 min




		2.2	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	24	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.05	23℃/23℃	-

Tensile Strength	ASTM D-638
		460	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	810	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	26000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-110	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	94	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		95	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		85	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Combustibility	UL-94	HB 1 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		2.2	200℃ × 5kg	g/10 min




		21	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	23	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.05	23℃/23℃	-
Tensile Strength	ISO 527	45	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	68	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2400	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-110	23℃	R-scale
Vicat Softening Point	ISO 306	94	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		90	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

High gloss, Medium impact

AG12A3

ABS RESIN

General Grade

Shoe heels, Toys, Clock housing, Stereo housing, Suitcase, The plate-like products

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		18	220℃ × 10kg	g/10 min




		1.6	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	32	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.04	23℃/23℃	-

Tensile Strength	ASTM D-638
		430	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	730	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	23000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-106	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	93	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		94	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		84	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Combustibility	UL-94	HB 1.5 ~ 1.65 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		1.6	200℃ × 5kg	g/10 min




		18	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	31	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.04	23℃/23℃	-
Tensile Strength	ISO 527	44	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	64	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2200	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-106	23℃	R-scale
Vicat Softening Point	ISO 306	93	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		88	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.5 ~ 1.65 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

High impact

AG12A0

ABS RESIN

General Grade

Helmets, Shoe heels, Pipe fittings, Products of low-temp usage

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		19	220℃ × 10kg	g/10 min




		1.6	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	30	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.04	23℃/23℃	-

Tensile Strength	ASTM D-638
		420	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	740	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	24000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-105	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	95	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		94	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		84	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Flammability	UL-94	1.5mm HB 3.0mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		1.6	200℃ × 5kg	g/10 min




		19	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	30	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.04	23℃/23℃	-
Tensile Strength	ISO 527	44	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	66	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2300	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-105	23℃	R-scale
Vicat Softening Point	ISO 306	93	Annealed，50N，50℃/h	℃



Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

Super high impact

Model

Applications

Physical

Features

Attach

Operating

AG15AJ

ABS RESIN

Jet Black General Grade

Black purpose parts, LED-TV housing,All-in-one PC housing

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
			220℃ × 10kg	g/10 min




			200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	23	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.05	23℃/23℃	-

Tensile Strength	ASTM D-638
		440	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	770	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	25000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-108	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	95	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		96	Annealed，1.8Mpa 1/4"厚，120℃/h	℃







Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		2.4	200℃ × 5kg	g/10 min




		25	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	24	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.05	23℃/23℃	-
Tensile Strength	ISO 527	44	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	66	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2300	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-108	23℃	R-scale
Vicat Softening Point	ISO 306	95	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		92	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

Jet black

AG15AB

ABS RESIN

Jet Black General Grade

Black purpose parts, LED-TV housing,All-in-one PC housing

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
			220℃ × 10kg	g/10 min




			200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	19	23 ℃，1/4"，Notched	kg-cm/cm




			23 ℃，1/4"，Notched	kg-cm/cm








Specific Gravity	ASTM D-792
		1.05	23℃/23℃	-

Tensile Strength	ASTM D-638
		470	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	830	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	25000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-109	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	96	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		96	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		86	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		2.4	200℃ × 5kg	g/10 min




		24	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	21	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.05	23℃/23℃	-
Tensile Strength	ISO 527	47	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	69	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2400	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-109	23℃	R-scale
Vicat Softening Point	ISO 306	96	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		94	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

Jet black, High gloss

AG12AJ

ABS RESIN

Jet Black General Grade

Black purpose parts, LED-TV housing,All-in-one PC housing

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
			220℃ × 10kg	g/10 min




			200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	34	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.05	23℃/23℃	-

Tensile Strength	ASTM D-638
		400	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	680	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	21000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-103	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	95	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		96	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		84	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Combustibility	UL-94	HB 1.6 ~ 1.76 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		1.9	200℃ × 5kg	g/10 min




		20	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	34	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.05	23℃/23℃	-
Tensile Strength	ISO 527	40	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	58	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2000	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-103	23℃	R-scale
Vicat Softening Point	ISO 306	95	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		91	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.6 ~ 1.76 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

Jet black

Model

Applications

Physical

Features

Attach

Operating

AF3530

Housing of stereos, Large toys, Chairs, Motorcycles, OA machines

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		27	220℃ × 10kg	g/10 min




		3.0	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	27	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.04	23℃/23℃	-

Tensile Strength	ASTM D-638
		420	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	720	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	22000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-105	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	93	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		93	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		85	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Flammability	UL-94	0.8mm HB 1.5mm HB 3.0mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94	HB 0.8 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Combustibility	UL-94	HB 0.8 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

High flow,
High impact,
Chemical resistant

AF3530

ABS RESIN

High Flow Grade

Housing of stereos, Large toys, Chairs, Motorcycles, OA machines

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		27	220℃ × 10kg	g/10 min




		3.0	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	27	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.04	23℃/23℃	-

Tensile Strength	ASTM D-638
		420	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	720	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	22000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-105	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	93	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		93	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		85	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Combustibility	UL-94	HB 0.8 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		3	200℃ × 5kg	g/10 min




		27	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	30	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.04	23℃/23℃	-
Tensile Strength	ISO 527	40	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	52	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	1600	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-105	23℃	R-scale
Vicat Softening Point	ISO 306	93	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		91	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 0.8 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

High flow,
High impact,
Chemical resistant

AF3535

Housing of stereos, Large toys, Chairs, Motorcycles, OA machines

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		40	220℃ × 10kg	g/10 min




		4.2	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	23	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.04	23℃/23℃	-

Tensile Strength	ASTM D-638
		440	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	750	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	23000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-105	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	93	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		94	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		86	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Combustibility	UL-94	HB 0.8 ~ 1.7 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		4.2	200℃ × 5kg	g/10 min




		40	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	26	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.04	23℃/23℃	-
Tensile Strength	ISO 527	42	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	56	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	1700	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-105	23℃	R-scale
Vicat Softening Point	ISO 306	93	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		92	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 0.8 ~ 1.7 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

High flow,High impact

AF3560

ABS RESIN

High Flow Grade

Housing of stereos, Large toys, Chairs, Motorcycles, OA machines

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		53	220℃ × 10kg	g/10 min




		5.2	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	12	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.04	23℃/23℃	-

Tensile Strength	ASTM D-638
		460	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	790	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	24000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-109	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	93	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		96	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		84	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		5.2	200℃ × 5kg	g/10 min




		53	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	14	23 ℃，4mm厚，Notched	kJ/m²



Tensile Strength	ISO 527	43	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	58	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	1700	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-109	23℃	R-scale
Vicat Softening Point	ISO 306	93	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		91	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

High flow,High impact

AF3500

ABS RESIN

High Flow Grade

Housing of stereos, Large toys, Chairs, Motorcycles, OA machines

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		47	220℃ × 10kg	g/10 min




		5.0	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	32	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.04	23℃/23℃	-

Tensile Strength	ASTM D-638
		390	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	670	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	20000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-102	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	92	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		94	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		83	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		5	200℃ × 5kg	g/10 min




		47	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	31	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.04	23℃/23℃	-
Tensile Strength	ISO 527	38	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	50	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	1500	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-102	23℃	R-scale
Vicat Softening Point	ISO 306	92	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		90	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

High flow,High impact

Model

Applications

Physical

Features

Attach

Operating

AX4300

ABS RESIN

Heat Resistant Grade

Parts of cars, Electrical appliances, Hair dryer, Heat resistant parts

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		4.0	220℃ × 10kg	g/10 min





IZOD Impact Strength	ASTM D-256	29	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.05	23℃/23℃	-

Tensile Strength	ASTM D-638
		450	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	780	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	22000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-106	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	99	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		104	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		94	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.3 ~ 0.6	3.2mm	%



Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133






		4	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	28	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.05	23℃/23℃	-
Tensile Strength	ISO 527	42	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	62	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2000	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-106	23℃	R-scale
Vicat Softening Point	ISO 306	99	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		96	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.3 ~ 0.6	3.2mm	%
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

Medium high heat, Extrusion blow molding

AX4100

ABS RESIN

Heat Resistant Grade

Parts of cars, Electrical appliances, Hair dryer, Heat resistant parts

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		4.5	220℃ × 10kg	g/10 min





IZOD Impact Strength	ASTM D-256	15	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.05	23℃/23℃	-

Tensile Strength	ASTM D-638
		400	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	740	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	24000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-110	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	106	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		112	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		102	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.3 ~ 0.6	3.2mm	%



Combustibility	UL-94	HB 1.5 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133






		4.5	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	16	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.05	23℃/23℃	-
Tensile Strength	ISO 527	38	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	61	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2100	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-110	23℃	R-scale
Vicat Softening Point	ISO 306	106	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		102	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.3 ~ 0.6	3.2mm	%
Combustibility	UL-94	HB 1.5 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

Super high heat

AX4000

ABS RESIN

Heat Resistant Grade

Parts of cars, Electrical appliances, Hair dryer, Heat resistant parts

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		9.0	220℃ × 10kg	g/10 min





IZOD Impact Strength	ASTM D-256	20	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.05	23℃/23℃	-

Tensile Strength	ASTM D-638
		420	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	770	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	24000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-109	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	100	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		104	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		93	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.3 ~ 0.6	3.2mm	%



Combustibility	UL-94	HB 1.5 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133






		9	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	21	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.05	23℃/23℃	-
Tensile Strength	ISO 527	41	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	63	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2100	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-109	23℃	R-scale
Vicat Softening Point	ISO 306	100	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		96	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.3 ~ 0.6	3.2mm	%
Combustibility	UL-94	HB 1.5 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

Medium high heat

Model

Applications

Physical

Features

Attach

Operating

AG23AT

ABS RESIN

Metal Plating Grade

Wheel cover, Knobs, Tags,Door handle, Plating products

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		20	220℃ × 10kg	g/10 min




		2.0	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	32	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.04	23℃/23℃	-

Tensile Strength	ASTM D-638
		440	23 ℃，50mm/min	kg/cm²


Flexural Modulus	ASTM D-790	23000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-106	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	94	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		96	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		86	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		2	200℃ × 5kg	g/10 min




		20	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	33	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.04	23℃/23℃	-
Tensile Strength	ISO 527	44	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	62	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2000	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-106	23℃	R-scale
Vicat Softening Point	ISO 306	94	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		93	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

High impact,Electro plating

Model

Applications

Physical

Features

Attach

Operating

AE8700

ABS RESIN

Extrusion Grade

Extrusion products, Crash helmet, Pipes, Shoe heels

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		3.5	220℃ × 10kg	g/10 min





IZOD Impact Strength	ASTM D-256	35	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.04	23℃/23℃	-

Tensile Strength	ASTM D-638
		480	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	820	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	25000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-109	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	95	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		99	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		90	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133






		3.5	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	40	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.04	23℃/23℃	-
Tensile Strength	ISO 527	46	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	69	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2300	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-109	23℃	R-scale
Vicat Softening Point	ISO 306	95	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		87	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

Extrusion molding,
Super high impact,
High rigid

AG10NP

ABS RESIN

Extrusion Grade

Extrusion products,Crash helmets,Pipes, Shoe heels

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		5.5	220℃ × 10kg	g/10 min





IZOD Impact Strength	ASTM D-256	44	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.04	23℃/23℃	-

Tensile Strength	ASTM D-638
		430	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	730	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	22000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-102	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	94	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		98	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		88	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Combustibility	UL-94	HB 1.6 ~ 1.76 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133






		5.5	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	45	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.04	23℃/23℃	-
Tensile Strength	ISO 527	42	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	58	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	1900	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-102	23℃	R-scale
Vicat Softening Point	ISO 306	94	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		93	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.6 ~ 1.76 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

Extrusion molding, Super high impact, High rigid

AE8000

ABS RESIN

Extrusion Grade

Extrusion products,Crash helmets,Pipes, Shoe heels

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		4.5	220℃ × 10kg	g/10 min





IZOD Impact Strength	ASTM D-256	45	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.04	23℃/23℃	-

Tensile Strength	ASTM D-638
		440	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	740	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	22000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-103	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	94	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		96	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		87	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Combustibility	UL-94	HB 1.6 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133






		4.5	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	47	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.04	23℃/23℃	-
Tensile Strength	ISO 527	42	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	51	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	1500	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-103	23℃	R-scale
Vicat Softening Point	ISO 306	94	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		92	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.6 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

Extrusion molding, Super high impact, High rigid

AG10AP

ABS RESIN

Extrusion Grade

Extrusion products,Crash helmets,Pipes, Shoe heels

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		4.0	220℃ × 10kg	g/10 min





IZOD Impact Strength	ASTM D-256	51	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.04	23℃/23℃	-

Tensile Strength	ASTM D-638
		370	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	640	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	19000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-93	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	91	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		94	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		84	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Combustibility	UL-94	HB 1.6 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133






		4	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	50	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.04	23℃/23℃	-
Tensile Strength	ISO 527	37	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	46	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	1500	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-93	23℃	R-scale
Vicat Softening Point	ISO 306	91	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		92	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.6 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

Extrusion molding, Super high impact, High rigid

Model

Applications

Physical

Features

Attach

Operating

ANC120

ABS RESIN

Self Extinguishing Grade

Flame retardant materials;Housing of LCD monitor, LCD-TVcomputers & OA machine

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238





		5.5	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	26	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.19	23℃/23℃	-

Tensile Strength	ASTM D-638
		400	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	690	23 ℃，15mm/min	kg/cm²


		0	23 ℃，1.2mm/min	kg/cm²
Flexural Modulus	ASTM D-790	23000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-100	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	83	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		84	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		74	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Combustibility	UL-94	v-0 2.3 ~ 3 mm 5VB 2.3 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		5.5	200℃ × 5kg	g/10 min





Charpy Impact Strength	ISO 179	18	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.19	23℃/23℃	-
Tensile Strength	ISO 527	39	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	59	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2000	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-100	23℃	R-scale
Vicat Softening Point	ISO 306	83	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		79	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.3 ~ 0.6	3.2mm	%
Combustibility	UL-94	v-0 2.3 ~ 3 mm 5VB 2.3 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

Flame retardant

ANC100

ABS RESIN

Heat Resistant Grade

Flame retardant materials;Housing of LCD monitor, LCD-TV,computers & OA machine

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238





		6.0	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	22	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792	0	23℃	-


Tensile Strength	ASTM D-638
		420	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	720	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	24000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-101	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	80	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		90	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		76	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.3 ~ 0.6	3.2mm	%



Combustibility	UL-94	v-0 1.5 ~ 3 mm 5VA 2.3 ~ 2.5 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		6	200℃ × 5kg	g/10 min





Charpy Impact Strength	ISO 179	17	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.21	23℃/23℃	-
Tensile Strength	ISO 527	40	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	59	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178	0	23 ℃	Mpa
Flexural Modulus	ISO 178	2000	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-101	23℃	R-scale
Vicat Softening Point	ISO 306	80	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		76	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.3 ~ 0.6	3.2mm	%
Combustibility	UL-94	v-0 1.5 ~ 3 mm 5VA 2.3 ~ 2.5 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

Flame retardant

Model

Applications

Physical

Features

Attach

Operating

AG16A1

ABS RESIN

Health Care Grade

Scalpel shank, Asthma inhaler Meets the requirements of USP Plastic Class VI

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		11	220℃ × 10kg	g/10 min




		1.0	200℃ × 5kg	g/10 min
IZOD Impact Strength	ASTM D-256	28	23 ℃，1/4"，Notched	kg-cm/cm













Specific Gravity	ASTM D-792
		1.04	23℃/23℃	-

Tensile Strength	ASTM D-638
		510	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	880	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	26000	23 ℃，15mm/min	kg/cm²



Vicat Softening Point	ASTM D-1525	94	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648


		94	Annealed，1.8Mpa 1/4"厚，120℃/h	℃
		88	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133

		1	200℃ × 5kg	g/10 min




		11	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	33	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.04	23℃/23℃	-
Tensile Strength	ISO 527	47	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	72	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2300	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-111	23℃	R-scale
Vicat Softening Point	ISO 306	94	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		88	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

High rigid,
Medium impact

Model

Applications

Physical

Features

Attach

Operating

AG20GF

ABS RESIN

20%GF Reinforced Grade

Printer parts

ASTM Data Sheet
ISO Data Sheet

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		20	220℃ × 10kg	g/10 min





IZOD Impact Strength	ASTM D-256	8.7	23 ℃，1/4"，Notched	kg-cm/cm













Tensile Strength	ASTM D-638

		1100	23 ℃	kg/cm²

Flexural Strength	ASTM D-790

		69510	23 ℃	kg/cm²

Combustibility	UL-94		File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Combustibility	UL-94		File No. E162823	-

To print, please click on the attached standard physical properties table.

MI(220℃×10kg):15

Izod (ASTM,1/4"):8.7

FM(ASTM):69510

TS(ASTM):1100

Dimensional stability
High heat resistant