AC9144
PC RESIN
Ultra-low Temp Resistance Copolymer
|
Mobile phone / tablet / laptop / 3C products case, sports equipment / protective gear.
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | 13 | 300℃×1.2kg | g/10 min |
|
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | |
|
| 75 | 23℃, 3.2mm, Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | 1.18 | 23℃ | - |
|
|
| Tensile Strength |
ASTM D-638 | | 600 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | | 1000 | 23 ℃, 2mm/min | kg/cm² |
|
|
| Flexural Modulus |
ASTM D-790 | | 21000 | 23 ℃, 2mm/min | kg/cm² |
|
|
| Rockwell Hardness |
ASTM D-785 | R-120 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | 120 | Unannealed, 18.6kg/cm², 3.2mm, 120℃/h | ℃ |
|
|
|
|
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | | 0.6 ~
0.8 | - | % |
|
|
| Combustibility |
UL-94 |
v-2 2 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
v-2 2 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Translucency,
Mid flow,
Low temperature impact property, UV resistance,
|
|
|
AG10NP-N
ABS RESIN
Extrusion Grade
|
MI(220℃×10kg):6
Izod (ASTM,1/4"):47
FM(ASTM):18000
TS(ASTM):355
Extrusion products,Crash helmets,Pipes, Shoe heels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Extrusion molding, Super high impact, High rigid |
|
|
K1011
Homopolymer PP RESIN
Injection Molding Grade
|
General purpose, Foodcontainers, Electrical appliances, Housewares meets the requirements of USP Plastic Class VI
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 15 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 2.8 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 2.8 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 350 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 14500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 15 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 27 | 23 ℃，1/8"，Notched | kJ/m² |
| 27 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 34 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1421 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-100 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Good stiffness,
Good luster
|
|
|
|
AG100H
|
Helmets,
Shoe heels,
Pipe fittings,
Products of low-temp usage
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 8 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 41 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | | 370 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 620 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 19000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-95 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 95 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 93 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 83 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 8 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 40 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | 1.04 | 23℃ | - |
|
| Tensile Strength |
ISO 527 | 38 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 55 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1800 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-95 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 95 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 87 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Super high impact
|
|
|
|
AG15E1
|
Toys, Calculators, Phone,Clock housing,Stereo housing, Suitcase
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 25 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 2.4 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 19 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 480 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 840 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 26000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-111 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 95 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 86 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 2.4 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 25 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 16 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Tensile Strength |
ISO 527 | 46 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 70 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2500 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-111 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 95 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 91 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High gloss,
High rigid
|
|
|
GP5250
PS RESIN
General Purpose Grade
|
Food containers, Stationery, Toys, Clothing hangers, Lamp decoration, CD, Cosmetic cases
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 6.7 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 1.7 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 430 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 31000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 850 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 32000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 95 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 86 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 6.7 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 7.4 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 41 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3300 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 70 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3200 | 23 ℃，2mm/min | Mpa |
|
| Vicat Softening Point |
ISO 306 | |
| 95 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 91 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Injection molding
|
|
|
|
AG15E3
|
Toys, Calculators, Phone,Clock housing,Stereo housing, Suitcase
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 18 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 1.6 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 18 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | 0 | 23℃ | - |
|
|
| Tensile Strength |
ASTM D-638 | | 500 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 860 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 26000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-111 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 95 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 85 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 1.6 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 18 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 18 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Tensile Strength |
ISO 527 | 49 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 72 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2500 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-111 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High gloss, High rigid |
|
|
|
AG15A3
|
Toys, Calculators, Phone,Clock housing,Stereo housing, Suitcase
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 22 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 2.2 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 24 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 470 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 820 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 25000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-109 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 95 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 85 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1 ~ 1.65 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 2.2 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 22 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 26 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 41 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 60 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1 ~ 1.65 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High gloss, Medium impact |
|
|
|
AG15A1-H
|
Toys, Calculators, Phone,Clock housing,Stereo housing, Suitcase
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 21 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 2.2 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 24 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 460 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 810 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 26000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-110 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 95 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 85 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Combustibility |
UL-94 |
HB 1 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 2.2 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 21 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 23 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 45 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 68 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-110 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High gloss, Medium impact |
|
|
|
AG12A3
|
Shoe heels, Toys, Clock housing,
Stereo housing, Suitcase,
The plate-like products
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 18 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 1.6 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 32 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 430 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 730 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 23000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-106 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 94 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 84 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 1.6 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 18 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 31 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 44 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 64 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2200 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-106 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 88 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact |
|
|
|
AG12A0
|
Helmets,
Shoe heels,
Pipe fittings,
Products of low-temp usage
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 19 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 1.6 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 30 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 420 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 740 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 24000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-105 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 95 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 94 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 84 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 1.6 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 19 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 30 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 44 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 66 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2300 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-105 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Super high impact |
|
|
|
AG12A1-H
|
Shoe heels, Toys, Clock housing,Stereo housing, Suitcase, The plate-like products |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(220℃×10kg):21
Izod (ASTM,1/4"):30
FM(ASTM):23000
TS(ASTM):420
High impact, High gloss
|
|
|
GP535N
PS RESIN
General Purpose Grade
|
Kitchen ware, Lamp covers, Decorated sheets, Toys |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 3.5 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 1.8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 450 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 32000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 890 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 32000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 98 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 93 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 4.5 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 10.8 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 44 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3300 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 76 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3100 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 100 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 95 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Heat resistance |
|
|
K1023
Homopolymer PP RESIN
Injection Molding Grade
|
Thin wall parts,Housewares,Toys,meets the requirements of USP Plastic Class VI
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 23 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 2.6 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 2.6 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 340 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 14000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 25 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 25 | 23 ℃，1/8"，Notched | kJ/m² |
| 25 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 33 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1372 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-100 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High fluidity,
Good Stiffness,
Good luster
|
|
|
|
HP9450
|
HP sheets, Disposable dishware,Electronic Packaging, Cable reels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 3.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 15 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 250 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 22000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 52 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 470 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 22000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 100 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 90 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 3 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 12.2 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 9.8 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 25 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 2200 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 39 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 44 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 99 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 94 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Super high impact |
|
|
GP525N
PS RESIN
General Purpose Grade
|
Food containers, Stationery, Toys, Clothing hangers, Lamp decoration, CD, Cosmetic cases
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 6.7 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 430 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 31000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 870 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 32000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 95 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 87 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 6.7 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 7.4 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 41 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3300 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 70 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3200 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 7000 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 95 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 91 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Injection molding
|
|
|
|
AG15A1-H
|
Toys, Caculators, Phone, Clock housing, Stereo housing, Suitcase
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 22 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 2.2 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 24 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 460 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 810 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 26000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-110 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 95 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 85 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Combustibility |
UL-94 |
HB 1 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 2.2 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 21 | 220℃ × 10kg | g/10 min |
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 45 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 68 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-110 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High gloss,
Medium impact
|
|
|
HP9450
PS RESIN
High Impact Grade
|
HP sheets, Disposable dishware,Electronic Packaging, Cable reels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 3.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 15 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 250 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 22000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 52 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 470 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 22000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 100 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 90 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 3 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 12.2 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Tensile Strength |
ISO 527 | |
| 25 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 2200 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 39 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 44 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 99 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 94 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Super high impact |
|
|
K1035
Homopolymer PP RESIN
Injection Molding Grade
|
Thin wall parts , Housewares , Toys
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 38 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 2 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 2 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 340 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >50 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 14000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-102 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | | 0 | 300℃ × 1.2kg | g/10 min |
|
|
|
|
| 38 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 2 | 23 ℃，1/8"，Notched | kJ/m² |
| 2 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 33 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >50 | 23 ℃，50mm/min | % |
| Flexural Strength |
ISO 178 | 0 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | | 14000 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-102 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High fluidity,
Good Stiffness,
Good luster
|
|
|
|
MP6500
|
Stationery, Toys,Parts for home electrical appliances, Clothing hangers, Clock housing, FRP blending
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 3.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 290 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 24000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 40 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 560 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 25000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 100 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 91 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 7 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 5.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 5.8 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 30 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 2600 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 27 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 51 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 98 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 94 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Medium impact |
|
|
GP5350
PS RESIN
General Purpose Grade
|
Kitchen ware, Lamp covers, Decorated sheets, Toys |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 4.5 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 1.8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 450 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 32000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 900 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 32000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 98 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 90 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 4.5 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 10.8 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 44 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3300 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 76 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3100 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 100 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 95 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High heat resistance |
|
|
AE8000-H
ABS RESIN
Extrusion Grade
|
Extrusion products,Crash helmets,Pipes, Shoe heels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 6.0 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 45 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | 1.04 | 23℃ | - |
|
|
| Tensile Strength |
ASTM D-638 | | 440 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 740 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 22000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-103 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 87 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(220℃×10kg):5.4
Izod (ASTM,1/4"):42
FM(ASTM):21000
TS(ASTM):434
Extrusion molding, Super high impact, High rigid |
|
|
|
AF3535
|
Housing of stereos, Large toys, Chairs, Motorcycles, OA machines |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 40 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 4.2 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 23 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 440 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 750 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 23000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-105 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 94 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 86 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Combustibility |
UL-94 |
HB 0.8 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 4.2 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 40 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 26 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 42 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 56 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1700 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-105 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 92 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 0.8 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High flow,High impact
|
|
|
AF3560
ABS RESIN
High Flow Grade
|
Housing of stereos, Large toys, Chairs, Motorcycles, OA machines |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 53 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 5.2 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 12 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 460 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 790 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 24000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-109 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 84 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 5.2 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 53 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 14 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Tensile Strength |
ISO 527 | 43 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 58 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1700 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-109 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 91 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High flow,High impact
|
|
|
AF3500
ABS RESIN
High Flow Grade
|
Housing of stereos, Large toys, Chairs, Motorcycles, OA machines |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 47 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 5.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 32 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 390 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 670 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 20000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-102 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 92 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 94 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 83 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 5 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 47 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 31 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 38 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 50 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1500 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-102 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 92 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High flow,High impact
|
|
|
MP6500
PS RESIN
High Impact Grade
|
Stationery, Toys,Parts for home electrical appliances, Clothing hangers, Clock housing, FRP blending
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 7.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 290 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 24000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 40 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 560 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 25000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 100 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 91 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 7 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 5.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 5.8 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 30 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 2600 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 27 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 51 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 98 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 94 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Medium impact |
|
|
AC9140
PC RESIN
Ultra-low Temp Resistance Copolymer
|
Mobile phone / tablet / laptop / 3C products case, sports equipment / protective gear.
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | 13 | 300℃×1.2kg | g/10 min |
|
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | |
|
| 65 | 23℃, 3.2mm, Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | 1.18 | 23℃ | - |
|
|
| Tensile Strength |
ASTM D-638 | | 600 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | | 1000 | 23 ℃, 2mm/min | kg/cm² |
|
|
| Flexural Modulus |
ASTM D-790 | | 21000 | 23 ℃, 2mm/min | kg/cm² |
|
|
| Rockwell Hardness |
ASTM D-785 | R-120 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | 120 | Unannealed, 18.6kg/cm², 3.2mm, 120℃/h | ℃ |
|
|
|
|
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | | 0.6 ~
0.8 | - | % |
|
|
| Transmissin |
ASTM D-1003 | > 87 | 3.2mm | % |
| Haze |
ASTM D-1003 | < 1.0 | 3.2mm | % |
| Flammability |
UL94 / UL746B / UL746C | 2.0mm V2
RTI 80℃
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
v-2 2 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | | 13 | 300℃ × 1.2kg | g/10 min |
|
|
|
|
|
|
| Charpy Impact Strength |
ISO 179 | |
|
| 60 | 23℃, 4mm, Notched | kJ/m² |
| Specific Gravity |
ISO 1183 | 1.18 | 23℃ | - |
|
| Tensile Strength |
ISO 527 | 60 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 98 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2060 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-120 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
|
| 120 | Unannealed, 1.8Mpa, 4mm, 120℃/h | ℃ |
|
|
|
|
| Molding Shrinkage |
ISO 2577 | 0.6 ~
0.8 | - | % |
|
| Transmissin |
ISO 13468/1 | > 87 | 3.2mm | % |
| Haze |
ISO 14782 | < 1.0 | 3.2mm | % |
| Combustibility |
UL-94 |
v-2 2 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Transparency,
Mid flow,
Low temperature impact property, UV resistance,
|
|
|
AC9144
PC RESIN
Ultra-low Temp Resistance Copolymer
|
Mobile phone / tablet / laptop / 3C products case, sports equipment / protective gear.
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | 13 | 300℃×1.2kg | g/10 min |
|
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | |
|
| 75 | 23℃, 3.2mm, Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | 1.18 | 23℃ | - |
|
|
| Tensile Strength |
ASTM D-638 | | 600 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | | 1000 | 23 ℃, 2mm/min | kg/cm² |
|
|
| Flexural Modulus |
ASTM D-790 | | 21000 | 23 ℃, 2mm/min | kg/cm² |
|
|
| Rockwell Hardness |
ASTM D-785 | R-120 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | 120 | Unannealed, 18.6kg/cm², 3.2mm, 120℃/h | ℃ |
|
|
|
|
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | | 0.6 ~
0.8 | - | % |
|
|
| Combustibility |
UL-94 |
v-2 2 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | | 13 | 300℃ × 1.2kg | g/10 min |
|
|
|
|
|
|
| Specific Gravity |
ISO 1183 | 1.18 | 23℃ | - |
|
| Tensile Strength |
ISO 527 | 60 | 23 ℃，50mm/min | Mpa |
|
| 0 | 23 ℃，20mm/min | Mpa |
| Flexural Strength |
ISO 178 | 98 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2060 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-120 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
|
| 120 | Unannealed, 1.8Mpa, 4mm, 120℃/h | ℃ |
|
|
|
|
| Molding Shrinkage |
ISO 2577 | 0.6 ~
0.8 | - | % |
|
| Combustibility |
UL-94 |
v-2 2 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Translucency,
Mid flow,
Low temperature impact property, UV resistance,
|
|
|
AG10NP
ABS RESIN
Extrusion Grade
|
Extrusion products,Crash helmets,Pipes, Shoe heels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 5.5 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 44 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 430 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 730 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 22000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-102 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 98 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 88 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 ~ 1.76 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 5.5 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 45 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 42 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 58 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1900 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-102 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 93 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.6 ~ 1.76 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Extrusion molding, Super high impact, High rigid |
|
|
AE8000
ABS RESIN
Extrusion Grade
|
Extrusion products,Crash helmets,Pipes, Shoe heels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 4.5 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 45 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 440 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 740 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 22000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-103 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 87 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 4.5 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 47 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 42 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 51 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1500 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-103 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 92 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Extrusion molding, Super high impact, High rigid |
|
|
K1080
Homopolymer PP RESIN
Injection Molding Grade
|
Thin wall parts , Housewares , Toys
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 80 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 2 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 2 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 350 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >50 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 14000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-102 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 80 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 20 | 23 ℃，1/8"，Notched | kJ/m² |
| 20 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 34 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >50 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1372 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-102 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Ultra high fluidity, Good stiffness, Good luster
|
|
|
AG10AP
ABS RESIN
Extrusion Grade
|
Extrusion products,Crash helmets,Pipes, Shoe heels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 4.0 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 51 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 370 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 640 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 19000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-93 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 91 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 94 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 84 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 4 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 50 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 37 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 46 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1500 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-93 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 91 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 92 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Extrusion molding, Super high impact, High rigid |
|
|
K1108
Homopolymer PP RESIN
Injection Molding Grade
|
General purpose, Foodcontainers, Electrical appliances, Housewares
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 10 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 3 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 3 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 360 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 15000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 115 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 10 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 29 | 23 ℃，1/8"，Notched | kJ/m² |
| 29 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 35 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1470 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-100 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 115 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Good stiffness, Good luster
|
|
|
|
K8003
|
Baby-car parts, Paint drum,Sport appliances, Base of Luggage
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 25 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
|
|
|
| 2.6 | 23℃ 1/8"bar | kg-cm/cm |
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | |
| 343 | 23 ℃ | kg/cm² |
|
| Tensile Elongation at break |
ASTM D-638 | | >200 | 23℃ | % |
| Flexural Modulus |
ASTM D-790 | |
| 14500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.52 ~
| 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Hight impact strength, Good Stiffness
|
|
|
|
K8003
|
Baby-car parts, Paint drum,Sport appliances, Base of Luggage
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 31-37 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
|
|
|
| 4.0 | 23℃ 1/8"bar | kg-cm/cm |
|
|
|
| 4.0(38) | 23℃ 1/8"bar | kg-cm/cm (J/m) |
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Elongation at break |
ASTM D-638 | | >200 | 23℃ | % |
| Flexural Modulus |
ASTM D-790 | |
| 18000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-105 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 125 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | |
|
| 1.4 ~
1.8 | 23℃ | ％ |
| Tensile Strength at Yield |
ASTM D-638 | 380(37) | 23℃ | kg/cm2 (Mpa) |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Hight impact strength, Good Stiffness
|
|
|
K2051
Homopolymer PP RESIN
Injection Molding Grade
|
Thinner Wall Parts, Microwave containers, House wares,Toys |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 51 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 4 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 4 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 400 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >50 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 20000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-110 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 135 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 50 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 39 | 23 ℃，1/8"，Notched | kJ/m² |
| 39 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 39 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >50 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1960 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-110 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 135 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Super high fluidity,
High stiffness, Good luster, Nucleating Agent, Low warpage
|
|
|
K8003
Impact Copolymer PP RESIN
Injection Molding Grade
|
Baby-car parts, Paint drum,Sport appliances, Base of Luggage
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 60 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 9.5 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 260 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-80 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 3 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 93 | 0℉，4mm，Notched | kJ/m² |
| 588 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 25 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1078 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-80 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Hight impact strength, Good Stiffness
|
|
|
K8003AN
Impact Copolymer PP RESIN
Injection Molding Grade
|
Paint drum,Sport appliances, Base of Luggage |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 60 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 9 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 260 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 12000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-83 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 115 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Excellent impact strength, High stiffness, Excellent anti-static
|
|
|