WE8300

FCFC ASA Resin (TAIRILAC® ASA Resin) has excellent weather resistance and a stain ability, which is self-developed production technology and gain the Republic of China 229680 patent. Production process fully by existing ABS devices to convert capacity adjusts supply to meet market demand. The major ingredients come from our own sixth naphtha cracking project, this will ensure the stability of quality with competitive price. The factory has lab and testing equipment, product development can be based on market demand, in addition to the general purpose and high flow grade, developing of building materials and automotive in response to the environmental protection and new energy material. The future product development will gradually replace specialty ABS, to comply with the environmental protection technology of spraying and electroplating.

ISO 9001 、 ISO 14001

Model

Applications

Physical

Features

Attachments

Operating

WE8300

ASA RESIN

Suitable for plastic roof tile modified use.

ASTM Physical
ISO Physical

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ASTM D-1238
		8.0	220℃ × 10kg	g/10 min





IZOD Impact Strength	ASTM D-256
		15	23 ℃，1/8"，Notched	kg-cm/cm












Specific Gravity	ASTM D-792
		1.05	23℃/23℃	-

Tensile Strength	ASTM D-638
		440	23 ℃，50mm/min	kg/cm²


Flexural Strength	ASTM D-790	750	23 ℃，15mm/min	kg/cm²



Flexural Modulus	ASTM D-790	22000	23 ℃，15mm/min	kg/cm²



Rockwell Hardness	ASTM D-785	R-101	23 ℃	R-scale
Vicat Softening Point	ASTM D-1525	93	Annealed，50N，50℃/h	℃




Heat Deflection Temperature	ASTM D-648



		85	Unannealed，1.8Mpa 1/4" 厚，120℃/h	℃






Molding Shrinkage	ASTM D-955	0.4 ~ 0.7	3.2mm	%



Flammability	UL-94	1.5mm HB 3.0mm HB All Color	FILE NO. E162823	-
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

Property	Test Method	Value	Test Condition	Unit
Melt Flow Index	ISO 1133






		8	220℃ × 10kg	g/10 min
Charpy Impact Strength	ISO 179	16	23 ℃，4mm厚，Notched	kJ/m²



Specific Gravity	ISO 1183
Specific Gravity	ISO 1183	1.05	23℃/23℃	-
Tensile Strength	ISO 527	39	23 ℃，50mm/min	Mpa


Flexural Strength	ISO 178	59	23 ℃，2mm/min	Mpa
Flexural Strength	ISO 178
Flexural Modulus	ISO 178	2000	23 ℃，2mm/min	Mpa
Flexural Modulus	ISO 178
Rockwell Hardness	ISO 2039-2	R-101	23℃	R-scale
Vicat Softening Point	ISO 306	93	Annealed，50N，50℃/h	℃



Heat Deflection Temperature	ISO 75/A
		91	Annealed，1.8Mpa 4mm厚，120℃/h	℃






Molding Shrinkage	ISO 2577
Molding Shrinkage	ISO 2577	0.4 ~ 0.7	3.2mm	%
Combustibility	UL-94	HB 1.5 ~ 3 mm	File No. E162823	-

To print, please click on the attached standard physical properties table.

Excellent weather resistance, Suitable for plastic roof tile modified use.