AG10NP-N
ABS RESIN
Extrusion Grade
|
MI(220℃×10kg):6
Izod (ASTM,1/4"):47
FM(ASTM):18000
TS(ASTM):355
Extrusion products,Crash helmets,Pipes, Shoe heels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Extrusion molding, Super high impact, High rigid |
|
|
|
GP550N
|
PSP sheets, XPS sheets, OPS,Medicine containers
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 1.9 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 1.8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 510 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 32000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 1060 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 33000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 104 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 95 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 2.6 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 9.5 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 48 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3400 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 84 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3000 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 103 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 98 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High molecular weight |
|
|
B1101
Homopolymer PP RESIN
Extrusion & Blow Molding
|
Thermoforming Sheet, PP-H pipe, Tray, Blow molding |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 0.5 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 7 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 7 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 360 | 23 ℃，50mm/min | kg/cm² |
| 0 | 23 ℃ | kg/cm² |
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 14500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-102 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
1.9 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 0.5 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 69 | 23 ℃，1/8"，Notched | kJ/m² |
| 69 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 35 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1421 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-102 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Excellent melt strength,
Deep drawing
|
|
|
IV2500(<380 nm cut)
PC RESIN
Weatherability Grade
|
IV grade is mainly used for safety glasses, sun glasses and daylight roof. |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(ISO 1133):7
Charpy (ISO 179-1):80 kJ/m2
FM(ISO 179):2.2 GPa
TS(ISO 527-1,2):65 MPa
UV-stabilized PC with UV cut-off under 380 nm, iced-clear color.
|
|
|
B8001A3
Impact Copolymer PP RESIN
Extrusion Grade
|
PP-B pipe, Thermoforming sheet,Blow molding
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 1 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 80 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 11 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 270 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-80 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
| 105 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | | 1.5 ~
1.9 | - | % |
|
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 0.3 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 80 | 23 ℃，1/8"，Notched | kJ/m² |
|
|
|
| 11 | 0℉，4mm，Notched | kJ/m² |
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 26 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1178 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-80 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 105 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | 1.5 ~
1.9 | - | % |
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Excellent impact strength, Excellent resistance to low temp. brittleness
MI(230℃×2.16kg):0.3
Izod(ASTM,1/8"):80
FM(ASTM):11000
TS(ASTM):270
|
|
|
VT2500(<400 nm cut)
PC RESIN
Weatherability Grade
|
VT grade is also mainly used for safety glasses, sun glasses and daylight roof. |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(ISO 1133):7
Charpy (ISO 179-1):80 kJ/m2
FM(ISO 179):2.2 GPa
TS(ISO 527-1,2):65 MPa
UV-stabilized PC with UV cut-off under 400 nm, iced-clear color and good mold release property.
|
|
|
T8002
Impact Copolymer PP RESIN
Extrusion Grade
|
Corrugated sheet, Bottles, Thermo-forming sheet
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 2 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 75 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 10.8 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 270 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-80 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 105 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
1.9 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 1 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 106 | 0℉，4mm，Notched | kJ/m² |
| 735 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 26 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1078 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-80 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 105 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
1.9 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Hight impact strength,
Excellent resistance to low temp. Brittleness,
Good luster
|
|
|
AE8000-H
ABS RESIN
Extrusion Grade
|
Extrusion products,Crash helmets,Pipes, Shoe heels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 6.0 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 45 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | 1.04 | 23℃ | - |
|
|
| Tensile Strength |
ASTM D-638 | | 440 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 740 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 22000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-103 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 87 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(220℃×10kg):5.4
Izod (ASTM,1/4"):42
FM(ASTM):21000
TS(ASTM):434
Extrusion molding, Super high impact, High rigid |
|
|
AG10NP
ABS RESIN
Extrusion Grade
|
Extrusion products,Crash helmets,Pipes, Shoe heels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 5.5 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 44 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 430 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 730 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 22000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-102 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 98 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 88 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 ~ 1.76 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 5.5 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 45 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 42 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 58 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1900 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-102 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 93 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.6 ~ 1.76 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Extrusion molding, Super high impact, High rigid |
|
|
AE8000
ABS RESIN
Extrusion Grade
|
Extrusion products,Crash helmets,Pipes, Shoe heels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 4.5 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 45 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 440 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 740 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 22000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-103 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 87 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 4.5 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 47 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 42 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 51 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1500 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-103 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 92 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Extrusion molding, Super high impact, High rigid |
|
|
AG10AP
ABS RESIN
Extrusion Grade
|
Extrusion products,Crash helmets,Pipes, Shoe heels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 4.0 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 51 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 370 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 640 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 19000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-93 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 91 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 94 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 84 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 4 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 50 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 37 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 46 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1500 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-93 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 91 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 92 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Extrusion molding, Super high impact, High rigid |
|
|
GP550N
PS RESIN
General Purpose Grade
|
PSP sheets, XPS sheets, OPS,Medicine containers
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 2.6 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 1.8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 510 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 32000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 1060 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 31000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 104 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 95 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 2.6 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 9.5 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 48 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3400 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 84 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3000 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 103 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 98 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High molecular weight |
|
|