GP550N
|
PSP sheets, XPS sheets, OPS,Medicine containers
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 1.9 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 1.8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 510 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 32000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 1060 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 33000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 104 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 95 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 2.6 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 9.5 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 48 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3400 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 84 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3000 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 103 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 98 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High molecular weight |
|
|
T3002
Random Copolymer PP RESIN
Extrusion & Blow Molding
|
Blow Molding, USP CLASS VI Approved
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 2 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 8 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 8 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 260 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 8500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-85 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 85 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 1.6 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 78 | 23 ℃，1/8"，Notched | kJ/m² |
| 78 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 25 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 833 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-85 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | 0 | Unannealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
| 85 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Good transparency, Good resistance to chemical
|
|
|
K4515
Random Copolymer PP RESIN
Injection Molding Grade
|
High transparency container, Transparency housewares, USP Class VI approved |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 6 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 6 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 310 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-95 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 95 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5-1.65mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 18 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 59 | 23 ℃，1/8"，Notched | kJ/m² |
| 59 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 30 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1127 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-95 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 95 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High Clarity, Anti-static,Good resistance to chemical
|
|
|
GP5250
PS RESIN
General Purpose Grade
|
Food containers, Stationery, Toys, Clothing hangers, Lamp decoration, CD, Cosmetic cases
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 6.7 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 1.7 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 430 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 31000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 850 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 32000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 95 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 86 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 6.7 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 7.4 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 41 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3300 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 70 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3200 | 23 ℃，2mm/min | Mpa |
|
| Vicat Softening Point |
ISO 306 | |
| 95 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 91 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Injection molding
|
|
|
K4535
Random Copolymer PP RESIN
Injection Molding Grade
|
High transparency container, Transparency housewares, USP Class VI approved |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 5 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 5 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 310 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-95 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 95 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5-1.65mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 35 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 49 | 23 ℃，1/8"，Notched | kJ/m² |
| 49 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 30 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1127 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-95 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 95 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High fluidity, High Clarity, Anti-static, Good resistance to chemical
|
|
|
F4007
Random Copolymer PP RESIN
Film Grade
|
Blow Molding, USP CLASS VI Approved
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 7 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 6.5 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 6.5 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 260 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
| 0 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 8500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-85 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 85 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 7.5 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 64 | 23 ℃，1/8"，Notched | kJ/m² |
| 64 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 25 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 833 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-85 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 85 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Good transparency
|
|
|
K1023
Homopolymer PP RESIN
Injection Molding Grade
|
Thin wall parts,Housewares,Toys,meets the requirements of USP Plastic Class VI
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 23 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 2.6 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 2.6 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 340 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 14000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 25 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 25 | 23 ℃，1/8"，Notched | kJ/m² |
| 25 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 33 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1372 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-100 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High fluidity,
Good Stiffness,
Good luster
|
|
|
GP525N
PS RESIN
General Purpose Grade
|
Food containers, Stationery, Toys, Clothing hangers, Lamp decoration, CD, Cosmetic cases
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 6.7 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 430 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 31000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 870 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 32000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 95 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 87 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 6.7 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 7.4 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 41 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3300 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 70 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3200 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 7000 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 95 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 91 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Injection molding
|
|
|
K4650
Random Copolymer PP RESIN
Injection Molding Grade
|
High transparency container& housewares,
meets the requirements of USP Plastic Class VI
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 50 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 4.5 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 4.5 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 310 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-95 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 95 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 50 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 44 | 23 ℃，1/8"，Notched | kJ/m² |
| 44 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 30 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1127 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-95 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 95 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High fluidity, High clarity, anti-static
|
|
|
K4715
Random Copolymer PP RESIN
Injection Molding Grade
|
Super high transparency container& housewares,
meets the requirements of USP Plastic Class VI
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 15 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 6 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 6 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 310 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-95 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 95 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 18 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 59 | 23 ℃，1/8"，Notched | kJ/m² |
| 59 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 30 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1127 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-95 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 95 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Super High Clarity, Anti-static
|
|
|
GP535A
PS RESIN
General Purpose Grade
|
Kitchen ware, Lamp covers, Decorated sheets, Toys |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 4.3 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 1.8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 480 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 35000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 930 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 32000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 100 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 89 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 4.3 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 7.2 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 43 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3300 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 74 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3100 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 98 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 94 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High heat resistance |
|
|
GP5500
PS RESIN
General Purpose Grade
|
PSP sheets, OPS,Medicine containers
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 2.6 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 1.8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 500 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 32000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 1050 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 34000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 104 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 95 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 2.6 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 9.5 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 47 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3400 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 85 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3100 | 23 ℃，2mm/min | Mpa |
|
| Vicat Softening Point |
ISO 306 | |
| 103 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 98 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High molecular weight |
|
|
GP550N
PS RESIN
General Purpose Grade
|
PSP sheets, XPS sheets, OPS,Medicine containers
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 2.6 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 1.8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 510 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 32000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 1060 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 33000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 104 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 95 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 2.6 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 9.5 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 48 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3400 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 84 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3000 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 103 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 98 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High molecular weight |
|
|