AC2108
PC/ABS Alloy
Extrusion Grade
|
Suitcase |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Extrusion
molding，High impact
MI(240℃×5kg):5.0
Izod(ASTM,1/8"):70
FM(ASTM):23000
TS(ASTM):670
|
|
|
IV1900R(<380 nm cut)
PC RESIN
Weatherability Grade
|
IV-R grade is listed in AMECA, can used for car headlamp, lighting equipment and various outdoor applications. |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(ISO 1133):19
Charpy (ISO 179-1):70 kJ/m2
FM(ISO 179):2.3 GPa
TS(ISO 527-1,2):65 MPa
UV-stabilized PC with UV cut-off under 380 nm, iced-clear color, and good mold release property.
|
|
|
F4006
Random Copolymer PP RESIN
Film Grade
|
Excellent resistance to whiteness
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 6 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 6.5 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 6.5 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 260 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 8500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-85 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 85 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 7.5 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 64 | 23 ℃，1/8"，Notched | kJ/m² |
| 64 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 25 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 833 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-85 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 85 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Good Transpar-ency
|
|
|
AG10NP-N
ABS RESIN
Extrusion Grade
|
MI(220℃×10kg):6
Izod (ASTM,1/4"):47
FM(ASTM):18000
TS(ASTM):355
Extrusion products,Crash helmets,Pipes, Shoe heels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Extrusion molding, Super high impact, High rigid |
|
|
|
HP825S
|
Fridge liner, Door liner of fridge |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(200℃×5kg):2.7
Izod (ASTM,1/4"):10
FM(ASTM):15000
TS(ASTM):240
Environmental stress cracking resistance, extrusion with |
|
|
|
NF2100
|
Cassettes, Trash cans, Toothbrush handles, Lamp covers, Pen tube,
Cup with cover, Cosmetic cases |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| <2 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.06 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | |
| 700 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 35000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | M-78 | 23℃ | M-scale |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 5 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 50 | 220℃ × 10kg | g/10 min |
| CHARPY IMPACT STRENGTH |
ISO 179 | <2 | 23℃, 4mm, Notched | kJ/m2 |
| Specific Gravity |
ISO 1183 | | 1.06 | 23℃/23℃ | - |
| Flexural Strength |
ISO 178 | | 118 | 23 ℃ | Mpa |
| Flexural Modulus |
ISO 178 | | 69 | 23 ℃ | Mpa |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(220℃×10kg):50
Izod (ASTM,1/4"):1.5
FM(ASTM):35000
TS(ASTM):700
High flow,
Injection grade |
|
|
K4038
Random Copolymer PP RESIN
Injection Molding Grade
|
Transparency containers,Thin wall products
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 38 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 5 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 5 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 290 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-90 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 95 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 38 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 49 | 23 ℃，1/8"，Notched | kJ/m² |
| 49 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 28 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1078 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-90 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 95 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High fluidity, Anti-static, Good Transparency
|
|
|
S1019
Homopolymer PP RESIN
Multi-Filament Grade
|
Staple fiber, ES fiber & PP staple fiber |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 19 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 2.8 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 2.8 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 340 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 14000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 19 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 27 | 23 ℃，1/8"，Notched | kJ/m² |
| 27 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 33 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1372 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-100 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Controlled rheology, Good softness, Anti gas fading
|
|
|
K1011
Homopolymer PP RESIN
Injection Molding Grade
|
General purpose, Foodcontainers, Electrical appliances, Housewares meets the requirements of USP Plastic Class VI
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 15 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 2.8 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 2.8 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 350 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 14500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 15 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 27 | 23 ℃，1/8"，Notched | kJ/m² |
| 27 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 34 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1421 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-100 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Good stiffness,
Good luster
|
|
|
|
GP550N
|
PSP sheets, XPS sheets, OPS,Medicine containers
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 1.9 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 1.8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 510 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 32000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 1060 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 33000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 104 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 95 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 2.6 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 9.5 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 48 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3400 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 84 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3000 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 103 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 98 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High molecular weight |
|
|
T3002
Random Copolymer PP RESIN
Extrusion & Blow Molding
|
Blow Molding, USP CLASS VI Approved
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 2 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 8 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 8 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 260 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 8500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-85 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 85 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 1.6 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 78 | 23 ℃，1/8"，Notched | kJ/m² |
| 78 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 25 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 833 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-85 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | 0 | Unannealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
| 85 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Good transparency, Good resistance to chemical
|
|
|
IV2200R(<380 nm cut)
PC RESIN
Weatherability Grade
|
IV-R grade is listed in AMECA, can used for car headlamp, lighting equipment and various outdoor applications. |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(ISO 1133):11
Charpy (ISO 179-1):80 kJ/m2
FM(ISO 179):2.3 GPa
TS(ISO 527-1,2):65 MPa
UV-stabilized PC with UV cut-off under 380 nm, iced-clear color, and good mold release property. |
|
|
|
AG15E1
|
Toys, Calculators, Phone,Clock housing,Stereo housing, Suitcase
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 25 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 2.4 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 19 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 480 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 840 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 26000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-111 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 95 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 86 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 2.4 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 25 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 16 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Tensile Strength |
ISO 527 | 46 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 70 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2500 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-111 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 95 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 91 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High gloss,
High rigid
|
|
|
T4002
Random Copolymer PP RESIN
Extrusion & Blow Molding
|
Blow molding, sheet
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 2 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 8 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 8 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 260 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 8500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-85 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 85 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 1.6 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 78 | 23 ℃，1/8"，Notched | kJ/m² |
| 78 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 25 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 833 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-85 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 85 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Good transparency, Good resistance to chemical
|
|
|
|
WG1800
|
Fans of air-conditioner,
Housings of motorbike,
Outside applications |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 19 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 18 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 430 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 710 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 21000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
| 86 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 18 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 23 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 40 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 57 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1900 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-100 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 90 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Weather resistance is excellent,
Color stable, Suitable for outdoor use
|
|
|
AG23AT
ABS RESIN
Metal Plating Grade
|
Wheel cover, Knobs, Tags,Door handle, Plating products
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 22 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 2.3 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 32 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 440 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 740 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 23000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-106 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 86 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 2 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 20 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 33 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | 1.04 | 23℃ | - |
|
| Tensile Strength |
ISO 527 | 44 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 62 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2000 | 23 ℃，2mm/min | Mpa |
|
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 93 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact,Electro plating
|
|
|
|
NX3400
|
Blade of fan,
Batteries housing |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 10 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 1.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | <2 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.06 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 820 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 1200 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 37000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | M-79 | 23℃ | M-scale |
| Vicat Softening Point |
ASTM D-1525 | 102 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
| 97 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Flammability |
UL-94 | 1.6-1.8mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.6 ~ 1.8 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 1 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 10 | 220℃ × 10kg | g/10 min |
| CHARPY IMPACT STRENGTH |
ISO 179 | <2 | 23℃, 4mm, Notched | kJ/m2 |
| Specific Gravity |
ISO 1183 | | 1.06 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 83 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 121 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3600 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-79 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 102 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 104 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.6 ~ 1.8 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High heat,
Chemical resistance |
|
|
|
NF2200
|
Trash cans,
Toothbrush handles,
Lamp covers, Pen tube,
Cup with cover,
Cosmetic cases
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 29 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 2.9 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | <2 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.06 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 720 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 1200 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 35000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | M-78 | 23℃ | M-scale |
| Vicat Softening Point |
ASTM D-1525 | 101 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
| 94 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Flammability |
UL-94 | 1.5mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 2.9 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 29 | 220℃ × 10kg | g/10 min |
| CHARPY IMPACT STRENGTH |
ISO 179 | <2 | 23℃, 4mm, Notched | kJ/m2 |
| Specific Gravity |
ISO 1183 | | 1.06 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 73 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 117 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3600 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-78 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 101 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 102 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High flow , Injection grade |
|
|
IR1700
PC RESIN
General Purpose Grade
|
Relay cases, Timer cases, Packs, Decorative lighting covers, Cups and
glasses, Dishes, Electrical equipment, Safety lamps, Explosion-proof gloves,
Contact lens cases.
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(ISO 1133):26
Charpy (ISO 179-1):40 kJ/m2
FM(ISO 179):2.3 GPa
TS(ISO 527-1,2):65 MPa
Viscosity:Lowest
1. Highest impact strength among plastics
2. High transparency
3. Wide usable temperature rang
4. Excellent dimensional accuracy and stability
5. Excellent electrical properties
6. Meets UL standard
|
|
|
K4515
Random Copolymer PP RESIN
Injection Molding Grade
|
High transparency container, Transparency housewares, USP Class VI approved |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 6 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 6 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 310 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-95 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 95 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5-1.65mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 18 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 59 | 23 ℃，1/8"，Notched | kJ/m² |
| 59 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 30 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1127 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-95 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 95 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High Clarity, Anti-static,Good resistance to chemical
|
|
|
S1003
Homopolymer PP RESIN
Flat Yarn Grade
|
Portfolio, Yarn: Woven bag, Carpet, Backing, Ropes, Monofilament: Brushes, Ropes, Nettings |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 3 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 3.8 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 3.8 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 340 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 14000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 3 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 37 | 23 ℃，1/8"，Notched | kJ/m² |
| 37 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 33 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1372 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-100 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Good stretchability
|
|
|
B1101
Homopolymer PP RESIN
Extrusion & Blow Molding
|
Thermoforming Sheet, PP-H pipe, Tray, Blow molding |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 0.5 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 7 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 7 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 360 | 23 ℃，50mm/min | kg/cm² |
| 0 | 23 ℃ | kg/cm² |
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 14500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-102 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
1.9 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 0.5 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 69 | 23 ℃，1/8"，Notched | kJ/m² |
| 69 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 35 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1421 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-102 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Excellent melt strength,
Deep drawing
|
|
|
GP5250
PS RESIN
General Purpose Grade
|
Food containers, Stationery, Toys, Clothing hangers, Lamp decoration, CD, Cosmetic cases
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 6.7 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 1.7 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 430 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 31000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 850 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 32000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 95 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 86 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 6.7 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 7.4 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 41 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3300 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 70 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3200 | 23 ℃，2mm/min | Mpa |
|
| Vicat Softening Point |
ISO 306 | |
| 95 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 91 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Injection molding
|
|
|
|
AG15E3
|
Toys, Calculators, Phone,Clock housing,Stereo housing, Suitcase
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 18 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 1.6 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 18 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | 0 | 23℃ | - |
|
|
| Tensile Strength |
ASTM D-638 | | 500 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 860 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 26000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-111 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 95 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 85 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 1.6 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 18 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 18 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Tensile Strength |
ISO 527 | 49 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 72 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2500 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-111 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High gloss, High rigid |
|
|
|
AG15A3
|
Toys, Calculators, Phone,Clock housing,Stereo housing, Suitcase
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 22 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 2.2 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 24 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 470 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 820 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 25000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-109 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 95 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 85 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1 ~ 1.65 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 2.2 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 22 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 26 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 41 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 60 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1 ~ 1.65 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High gloss, Medium impact |
|
|
|
AG15A1-H
|
Toys, Calculators, Phone,Clock housing,Stereo housing, Suitcase
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 21 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 2.2 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 24 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 460 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 810 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 26000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-110 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 95 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 85 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Combustibility |
UL-94 |
HB 1 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 2.2 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 21 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 23 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 45 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 68 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-110 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High gloss, Medium impact |
|
|
|
AG12A3
|
Shoe heels, Toys, Clock housing,
Stereo housing, Suitcase,
The plate-like products
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 18 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 1.6 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 32 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 430 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 730 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 23000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-106 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 94 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 84 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 1.6 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 18 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 31 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 44 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 64 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2200 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-106 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 88 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact |
|
|
|
AG12A0
|
Helmets,
Shoe heels,
Pipe fittings,
Products of low-temp usage
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 19 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 1.6 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 30 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 420 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 740 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 24000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-105 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 95 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 94 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 84 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 1.6 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 19 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 30 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 44 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 66 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2300 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-105 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Super high impact |
|
|
|
AG12A1-H
|
Shoe heels, Toys, Clock housing,Stereo housing, Suitcase, The plate-like products |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(220℃×10kg):21
Izod (ASTM,1/4"):30
FM(ASTM):23000
TS(ASTM):420
High impact, High gloss
|
|
|
IV2500(<380 nm cut)
PC RESIN
Weatherability Grade
|
IV grade is mainly used for safety glasses, sun glasses and daylight roof. |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(ISO 1133):7
Charpy (ISO 179-1):80 kJ/m2
FM(ISO 179):2.2 GPa
TS(ISO 527-1,2):65 MPa
UV-stabilized PC with UV cut-off under 380 nm, iced-clear color.
|
|
|
|
WF3301
|
Fans of air-conditioner,
Parts of car,
Outside pipes
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 26 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 20 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 410 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 670 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 21000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-96 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 89 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
| 83 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 30 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 24 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 38 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 53 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1700 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-96 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 89 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Weather resistance is excellent,
Color stable, Suitable for outdoor use
|
|
|
GP535N
PS RESIN
General Purpose Grade
|
Kitchen ware, Lamp covers, Decorated sheets, Toys |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 3.5 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 1.8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 450 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 32000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 890 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 32000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 98 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 93 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 4.5 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 10.8 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 44 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3300 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 76 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3100 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 100 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 95 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Heat resistance |
|
|
IR1900
PC RESIN
General Purpose Grade
|
Relay cases, Timer cases, Packs, Decorative lighting covers, Cups and
glasses, Dishes, Electrical equipment, Safety lamps, Explosion-proof gloves,
Contact lens cases.
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(ISO 1133):19
Charpy (ISO 179-1):70 kJ/m2
FM(ISO 179):2.3 GPa
TS(ISO 527-1,2):65 MPa
Viscosity:Low
1. Highest impact strength among plastics
2. High transparency
3. Wide usable temperature rang
4. Excellent dimensional accuracy and stability
5. Excellent electrical properties
6. Meets UL standard |
|
|
K4535
Random Copolymer PP RESIN
Injection Molding Grade
|
High transparency container, Transparency housewares, USP Class VI approved |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 5 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 5 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 310 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-95 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 95 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5-1.65mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 35 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 49 | 23 ℃，1/8"，Notched | kJ/m² |
| 49 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 30 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1127 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-95 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 95 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High fluidity, High Clarity, Anti-static, Good resistance to chemical
|
|
|
F4007
Random Copolymer PP RESIN
Film Grade
|
Blow Molding, USP CLASS VI Approved
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 7 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 6.5 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 6.5 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 260 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
| 0 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 8500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-85 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 85 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 7.5 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 64 | 23 ℃，1/8"，Notched | kJ/m² |
| 64 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 25 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 833 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-85 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 85 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Good transparency
|
|
|
K1023
Homopolymer PP RESIN
Injection Molding Grade
|
Thin wall parts,Housewares,Toys,meets the requirements of USP Plastic Class VI
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 23 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 2.6 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 2.6 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 340 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 14000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 25 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 25 | 23 ℃，1/8"，Notched | kJ/m² |
| 25 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 33 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1372 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-100 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High fluidity,
Good Stiffness,
Good luster
|
|
|
S1005
Homopolymer PP RESIN
Flat Yarn Grade
|
Portfolio, Straw |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 5 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 3.6 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 3.6 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 340 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 14000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 5 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 35 | 23 ℃，1/8"，Notched | kJ/m² |
| 35 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 33 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1372 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-100 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Good stretchability, Good processability
|
|
|
T1002
Homopolymer PP RESIN
Extrusion & Blow Molding
|
Corrugated sheet, Strapping, Bottles |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 1.7 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 5 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 5 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 360 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Strength |
ASTM D-790 | | 0 | 23 ℃, 2mm/min | kg/cm² |
|
|
| Flexural Modulus |
ASTM D-790 | |
| 15000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
1.9 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5-1.65mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 1.7 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 49 | 23 ℃，1/8"，Notched | kJ/m² |
| 49 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 35 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1470 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-100 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
1.9 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Excellent tensile strength
|
|
|
|
HP9450
|
HP sheets, Disposable dishware,Electronic Packaging, Cable reels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 3.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 15 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 250 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 22000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 52 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 470 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 22000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 100 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 90 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 3 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 12.2 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 9.8 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 25 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 2200 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 39 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 44 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 99 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 94 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Super high impact |
|
|
GP525N
PS RESIN
General Purpose Grade
|
Food containers, Stationery, Toys, Clothing hangers, Lamp decoration, CD, Cosmetic cases
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 6.7 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 430 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 31000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 870 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 32000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 95 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 87 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 6.7 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 7.4 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 41 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3300 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 70 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3200 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 7000 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 95 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 91 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Injection molding
|
|
|
|
AG15A1-H
|
Toys, Caculators, Phone, Clock housing, Stereo housing, Suitcase
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 22 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 2.2 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 24 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 460 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 810 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 26000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-110 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 95 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 85 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Combustibility |
UL-94 |
HB 1 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 2.2 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 21 | 220℃ × 10kg | g/10 min |
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 45 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 68 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-110 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High gloss,
Medium impact
|
|
|
|
AC2856
|
Diffusion injection lampshade, Diffusion injection-blow bulb
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | 27 | 300℃×1.2kg | g/10 min |
|
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | |
|
| 6 | 23℃, 3.2mm, Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | 1.2 | 23℃ | - |
|
|
| Tensile Strength |
ASTM D-638 | | 600 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | | 1020 | 23 ℃, 2mm/min | kg/cm² |
|
|
| Flexural Modulus |
ASTM D-790 | | 22800 | 23 ℃, 2mm/min | kg/cm² |
|
|
| Rockwell Hardness |
ASTM D-785 | R-122 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | 125 | Unannealed, 18.6kg/cm², 3.2mm, 120℃/h | ℃ |
|
|
|
|
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | | 0.5 ~
0.7 | - | % |
|
|
| Transmissin |
ASTM D-1003 | 99~60 | 3.2mm | % |
| Haze |
ASTM D-1003 | 91~88 | 3.2mm | % |
| Flammability |
UL94 / UL746B / UL746C | 0.75mm V2
RTI 120~130℃
f1
WT,RD,BK | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
v-2 0.75 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | | 27 | 300℃ × 1.2kg | g/10 min |
|
|
|
|
|
|
| Specific Gravity |
ISO 1183 | 1.2 | 23℃ | - |
|
| Tensile Strength |
ISO 527 | 60 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 100 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2230 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-122 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
|
| 125 | Unannealed, 1.8Mpa, 4mm, 120℃/h | ℃ |
|
|
|
|
| Molding Shrinkage |
ISO 2577 | 0.5 ~
0.7 | - | % |
|
| Transmissin |
ISO 13468/1 | 1.0mm | 3.2mm | % |
| Haze |
ISO 14782 | 1.0mm | 3.2mm | % |
| Combustibility |
UL-94 |
v-2 0.75 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Light diffusion, Mid-high flow, UV resistanc
|
|
|
|
AC2854
|
Diffusion board, Diffusion lamp(LED tube shell)
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | 12 | 300℃×1.2kg | g/10 min |
|
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | |
|
| 75 | 23℃, 3.2mm, Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | 1.2 | 23℃ | - |
|
|
| Tensile Strength |
ASTM D-638 | | 710 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | | 1100 | 23 ℃, 2mm/min | kg/cm² |
|
|
| Flexural Modulus |
ASTM D-790 | | 22000 | 23 ℃, 2mm/min | kg/cm² |
|
|
| Rockwell Hardness |
ASTM D-785 | R-122 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | 128 | Unannealed, 18.6kg/cm², 3.2mm, 120℃/h | ℃ |
|
|
|
|
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | | 0.5 ~
0.7 | - | % |
|
|
| Transmissin |
ASTM D-1003 | 80~45 | 3.2mm | % |
| Haze |
ASTM D-1003 | 91~88 | 3.2mm | % |
| Flammability |
UL94 / UL746B / UL746C | 0.75mm V2
RTI 120~130℃
f1
WT,RD,BK | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
v-2 0.75 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | | 12 | 300℃ × 1.2kg | g/10 min |
|
|
|
|
|
|
| Charpy Impact Strength |
ISO 179 | |
|
| 70 | 23℃, 4mm, Notched | kJ/m² |
| Specific Gravity |
ISO 1183 | 1.2 | 23℃ | - |
|
| Tensile Strength |
ISO 527 | 70 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 108 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2155 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-122 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
|
| 128 | Unannealed, 1.8Mpa, 4mm, 120℃/h | ℃ |
|
|
|
|
| Transmissin |
ISO 13468/1 | 1.0mm | 3.2mm | % |
| Haze |
ISO 14782 | 1.0mm | 3.2mm | % |
| Combustibility |
UL-94 |
v-2 0.75 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Light diffusion, Mid flow,
UV resistance
|
|
|
VT2500(<400 nm cut)
PC RESIN
Weatherability Grade
|
VT grade is also mainly used for safety glasses, sun glasses and daylight roof. |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(ISO 1133):7
Charpy (ISO 179-1):80 kJ/m2
FM(ISO 179):2.2 GPa
TS(ISO 527-1,2):65 MPa
UV-stabilized PC with UV cut-off under 400 nm, iced-clear color and good mold release property.
|
|
|
AG26AT
ABS RESIN
Metal Plating Grade
|
Parts of cars, Tags, Door handle of refrigirator,
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact,High flow, Metal plating
|
|
|
HP9450
PS RESIN
High Impact Grade
|
HP sheets, Disposable dishware,Electronic Packaging, Cable reels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 3.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 15 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 250 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 22000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 52 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 470 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 22000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 100 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 90 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 3 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 12.2 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Tensile Strength |
ISO 527 | |
| 25 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 2200 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 39 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 44 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 99 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 94 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Super high impact |
|
|
IR2200
PC RESIN
General Purpose Grade
|
Relay cases, Timer cases, Packs, Decorative lighting covers, Cups and
glasses, Dishes, Electrical equipment, Safety lamps, Explosion-proof gloves,
Contact lens cases.
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(ISO 1133):11
Charpy (ISO 179-1):80 kJ/m2
FM(ISO 179):2.3 GPa
TS(ISO 527-1,2):65 MPa
Viscosity:Medium
1. Highest impact strength among plastics
2. High transparency
3. Wide usable temperature rang
4. Excellent dimensional accuracy
and stability
5. Excellent electrical properties
6. Meets UL
standard
|
|
|
K3029
Impact Copolymer PP RESIN
Injection Molding Grade
|
Bumper, Automotive parts, Thin wall products |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 15 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 7 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 210 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >100 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 10000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-75 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 108 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 32 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 69 | 0℉，4mm，Notched | kJ/m² |
| 147 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 21 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >100 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 980 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-75 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 108 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High fluidity, High impact strength
|
|
|
T8002
Impact Copolymer PP RESIN
Extrusion Grade
|
Corrugated sheet, Bottles, Thermo-forming sheet
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 2 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 75 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 10.8 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 270 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-80 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 105 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
1.9 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 1 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 106 | 0℉，4mm，Notched | kJ/m² |
| 735 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 26 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1078 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-80 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 105 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
1.9 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Hight impact strength,
Excellent resistance to low temp. Brittleness,
Good luster
|
|
|
K4650
Random Copolymer PP RESIN
Injection Molding Grade
|
High transparency container& housewares,
meets the requirements of USP Plastic Class VI
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 50 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 4.5 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 4.5 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 310 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-95 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 95 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 50 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 44 | 23 ℃，1/8"，Notched | kJ/m² |
| 44 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 30 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1127 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-95 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 95 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High fluidity, High clarity, anti-static
|
|
|
S1040
Homopolymer PP RESIN
Multi-Filament Grade
|
Nonwoven, Fine Denier staple fiber |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 40 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 2.3 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 2.3 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 350 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >50 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 15000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-103 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 34 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 23 | 23 ℃，1/8"，Notched | kJ/m² |
| 23 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 34 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >50 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1470 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-103 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Controlled rheology, Compact Spinning, Anti gas fading
|
|
|
K1035
Homopolymer PP RESIN
Injection Molding Grade
|
Thin wall parts , Housewares , Toys
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 38 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 2 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 2 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 340 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >50 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 14000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-102 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | | 0 | 300℃ × 1.2kg | g/10 min |
|
|
|
|
| 38 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 2 | 23 ℃，1/8"，Notched | kJ/m² |
| 2 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 33 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >50 | 23 ℃，50mm/min | % |
| Flexural Strength |
ISO 178 | 0 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | | 14000 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-102 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High fluidity,
Good Stiffness,
Good luster
|
|
|
T1202
Homopolymer PP RESIN
Extrusion & Blow Molding
|
Blow molding
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 1.6 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 4.5 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 4.5 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | |
| 380 | 23 ℃ | kg/cm² |
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 18000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-108 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 135 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
1.9 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 1.6 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 44 | 23 ℃，1/8"，Notched | kJ/m² |
| 44 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
high stiffness, heat resistance, clarity
MI(230℃×2.16kg):1.6
Izod(ASTM,1/8"):4.5
FM(ASTM):18000
TS(ASTM):380
|
|
|
|
MP6500
|
Stationery, Toys,Parts for home electrical appliances, Clothing hangers, Clock housing, FRP blending
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 3.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 290 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 24000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 40 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 560 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 25000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 100 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 91 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 7 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 5.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 5.8 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 30 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 2600 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 27 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 51 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 98 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 94 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Medium impact |
|
|
GP5350
PS RESIN
General Purpose Grade
|
Kitchen ware, Lamp covers, Decorated sheets, Toys |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 4.5 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 1.8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 450 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 32000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 900 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 32000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 98 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 90 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 4.5 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 10.8 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 44 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3300 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 76 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3100 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 100 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 95 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High heat resistance |
|
|
AE8000-H
ABS RESIN
Extrusion Grade
|
Extrusion products,Crash helmets,Pipes, Shoe heels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 6.0 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 45 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | 1.04 | 23℃ | - |
|
|
| Tensile Strength |
ASTM D-638 | | 440 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 740 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 22000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-103 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 87 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(220℃×10kg):5.4
Izod (ASTM,1/4"):42
FM(ASTM):21000
TS(ASTM):434
Extrusion molding, Super high impact, High rigid |
|
|
|
AF3535
|
Housing of stereos, Large toys, Chairs, Motorcycles, OA machines |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 40 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 4.2 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 23 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 440 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 750 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 23000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-105 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 94 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 86 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Combustibility |
UL-94 |
HB 0.8 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 4.2 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 40 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 26 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 42 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 56 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1700 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-105 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 92 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 0.8 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High flow,High impact
|
|
|
AF3560
ABS RESIN
High Flow Grade
|
Housing of stereos, Large toys, Chairs, Motorcycles, OA machines |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 53 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 5.2 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 12 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 460 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 790 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 24000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-109 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 84 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 5.2 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 53 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 14 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Tensile Strength |
ISO 527 | 43 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 58 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1700 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-109 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 91 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High flow,High impact
|
|
|
AF3500
ABS RESIN
High Flow Grade
|
Housing of stereos, Large toys, Chairs, Motorcycles, OA machines |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 47 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 5.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 32 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 390 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 670 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 20000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-102 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 92 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 94 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 83 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 5 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 47 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 31 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 38 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 50 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1500 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-102 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 92 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High flow,High impact
|
|
|
MP6500
PS RESIN
High Impact Grade
|
Stationery, Toys,Parts for home electrical appliances, Clothing hangers, Clock housing, FRP blending
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 7.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 290 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 24000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 40 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 560 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 25000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 100 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 91 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 7 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 5.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 5.8 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 30 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 2600 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 27 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 51 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 98 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 94 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Medium impact |
|
|
IR2500
PC RESIN
General Purpose Grade
|
Relay cases, Timer cases, Packs, Decorative lighting covers, Cups and
glasses, Dishes, Electrical equipment, Safety lamps, Explosion-proof gloves,
Contact lens cases.
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(ISO 1133):7
Charpy (ISO 179-1):80 kJ/m2
FM(ISO 179):2.2 GPa
TS(ISO 527-1,2):65 MPa
Viscosity:High
1. Highest impact strength among plastics
2. High transparency
3. Wide usable temperature rang
4. Excellent dimensional accuracy
and stability
5. Excellent electrical properties
6. Meets UL
standard
|
|
|
K4715
Random Copolymer PP RESIN
Injection Molding Grade
|
Super high transparency container& housewares,
meets the requirements of USP Plastic Class VI
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 15 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 6 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 6 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 310 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-95 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 95 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 18 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 59 | 23 ℃，1/8"，Notched | kJ/m² |
| 59 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 30 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1127 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-95 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 95 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Super High Clarity, Anti-static
|
|
|
T2502
Homopolymer PP RESIN
Extrusion & Blow Molding
|
Transparency pressure forming sheet,Portfolio, Bottles |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 1.8 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 6 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 6 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 360 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 15500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 117 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
1.9 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 1.8 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 59 | 23 ℃，1/8"，Notched | kJ/m² |
| 59 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 35 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1519 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-100 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 117 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
1.9 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High stiffiness, Good transparency, Good heat resistance
|
|
|
GP535A
PS RESIN
General Purpose Grade
|
Kitchen ware, Lamp covers, Decorated sheets, Toys |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 4.3 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 1.8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 480 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 35000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 930 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 32000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 100 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 89 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 4.3 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 7.2 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 43 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3300 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 74 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3100 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 98 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 94 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High heat resistance |
|
|
K4750
Random Copolymer PP RESIN
Injection Molding Grade
|
Super high transparency container& housewares |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 50 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 4.5 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 4.5 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 310 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 1127 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-95 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 95 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 50 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 44 | 23 ℃，1/8"，Notched | kJ/m² |
| 44 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 30 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1127 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-95 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 95 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
2 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Super High Clarity, Anti-static
|
|
|
AG10NP
ABS RESIN
Extrusion Grade
|
Extrusion products,Crash helmets,Pipes, Shoe heels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 5.5 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 44 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 430 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 730 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 22000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-102 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 98 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 88 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 ~ 1.76 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 5.5 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 45 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 42 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 58 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1900 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-102 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 93 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.6 ~ 1.76 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Extrusion molding, Super high impact, High rigid |
|
|
AE8000
ABS RESIN
Extrusion Grade
|
Extrusion products,Crash helmets,Pipes, Shoe heels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 4.5 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 45 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 440 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 740 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 22000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-103 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 87 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 4.5 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 47 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 42 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 51 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1500 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-103 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 92 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Extrusion molding, Super high impact, High rigid |
|
|
K1080
Homopolymer PP RESIN
Injection Molding Grade
|
Thin wall parts , Housewares , Toys
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 80 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 2 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 2 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 350 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >50 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 14000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-102 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 80 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 20 | 23 ℃，1/8"，Notched | kJ/m² |
| 20 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 34 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >50 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1372 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-102 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Ultra high fluidity, Good stiffness, Good luster
|
|
|
AG10AP
ABS RESIN
Extrusion Grade
|
Extrusion products,Crash helmets,Pipes, Shoe heels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 4.0 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 51 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 370 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 640 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 19000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-93 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 91 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 94 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 84 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 4 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 50 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 37 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 46 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1500 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-93 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 91 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 92 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Extrusion molding, Super high impact, High rigid |
|
|
K1108
Homopolymer PP RESIN
Injection Molding Grade
|
General purpose, Foodcontainers, Electrical appliances, Housewares
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 10 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 3 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 3 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 360 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 15000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 115 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 10 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 29 | 23 ℃，1/8"，Notched | kJ/m² |
| 29 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 35 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1470 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-100 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 115 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Good stiffness, Good luster
|
|
|
GP5500
PS RESIN
General Purpose Grade
|
PSP sheets, OPS,Medicine containers
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 2.6 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 1.8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 500 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 32000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 1050 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 34000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 104 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 95 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 2.6 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 9.5 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 47 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3400 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 85 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3100 | 23 ℃，2mm/min | Mpa |
|
| Vicat Softening Point |
ISO 306 | |
| 103 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 98 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High molecular weight |
|
|
|
K8003
|
Baby-car parts, Paint drum,Sport appliances, Base of Luggage
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 25 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
|
|
|
| 2.6 | 23℃ 1/8"bar | kg-cm/cm |
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | |
| 343 | 23 ℃ | kg/cm² |
|
| Tensile Elongation at break |
ASTM D-638 | | >200 | 23℃ | % |
| Flexural Modulus |
ASTM D-790 | |
| 14500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.52 ~
| 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Hight impact strength, Good Stiffness
|
|
|
GP550N
PS RESIN
General Purpose Grade
|
PSP sheets, XPS sheets, OPS,Medicine containers
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 2.6 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 1.8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 510 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 32000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 1060 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 33000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 104 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 95 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 2.6 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 9.5 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 48 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3400 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 84 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3000 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 103 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 98 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High molecular weight |
|
|
AG23AT
ABS RESIN
Metal Plating Grade
|
Wheel cover, Knobs, Tags,Door handle, Plating products
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 20 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 2.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 32 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 440 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Modulus |
ASTM D-790 | 23000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-106 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 86 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 2 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 20 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 33 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 44 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 62 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2000 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-106 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 93 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact,Electro plating
|
|
|
K1525
Homopolymer PP RESIN
Injection Molding Grade
|
microwave containers, Food containers |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 25 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 2.6 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 2.6 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 360 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >50 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 18000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-108 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 125 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 25 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 25 | 23 ℃，1/8"，Notched | kJ/m² |
| 25 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 35 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >50 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1764 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-108 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 125 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High fluidity, High Stiffness , Good luster, Good
Transparency
|
|
|
|
K8003
|
Baby-car parts, Paint drum,Sport appliances, Base of Luggage
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 31-37 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
|
|
|
| 4.0 | 23℃ 1/8"bar | kg-cm/cm |
|
|
|
| 4.0(38) | 23℃ 1/8"bar | kg-cm/cm (J/m) |
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Elongation at break |
ASTM D-638 | | >200 | 23℃ | % |
| Flexural Modulus |
ASTM D-790 | |
| 18000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-105 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 125 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | |
|
| 1.4 ~
1.8 | 23℃ | ％ |
| Tensile Strength at Yield |
ASTM D-638 | 380(37) | 23℃ | kg/cm2 (Mpa) |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Hight impact strength, Good Stiffness
|
|
|
K2051
Homopolymer PP RESIN
Injection Molding Grade
|
Thinner Wall Parts, Microwave containers, House wares,Toys |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 51 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 4 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 4 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 400 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >50 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 20000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-110 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 135 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 50 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 39 | 23 ℃，1/8"，Notched | kJ/m² |
| 39 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 39 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >50 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1960 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-110 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 135 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Super high fluidity,
High stiffness, Good luster, Nucleating Agent, Low warpage
|
|
|
K8003
Impact Copolymer PP RESIN
Injection Molding Grade
|
Baby-car parts, Paint drum,Sport appliances, Base of Luggage
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 60 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 9.5 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 260 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-80 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 3 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 93 | 0℉，4mm，Notched | kJ/m² |
| 588 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 25 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1078 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-80 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Hight impact strength, Good Stiffness
|
|
|
K8003AN
Impact Copolymer PP RESIN
Injection Molding Grade
|
Paint drum,Sport appliances, Base of Luggage |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 60 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 9 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 260 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 12000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-83 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 115 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Excellent impact strength, High stiffness, Excellent anti-static
|
|
|
K8050
Impact Copolymer PP RESIN
Injection Molding Grade
|
Washing machine,Storage boxes,Thin wall products
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 10 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 5 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 240 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >100 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 12500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-85 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 115 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5-1.65mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 50 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 49 | 0℉，4mm，Notched | kJ/m² |
| 98 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 23 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >100 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1225 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-85 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 115 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High fluidity, Good impact strength, High Stiffness,Low warpage
|
|
|
K8802
Impact Copolymer PP RESIN
Injection Molding Grade
|
Suitcase Parts |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 70 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 10 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 270 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-80 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 105 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
1.9 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 2 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 98 | 0℉，4mm，Notched | kJ/m² |
| 686 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 26 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1078 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-80 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 105 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
1.9 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Hight impact strength,
Excellent resistance to low temp. Brittleness,
Good luster
|
|
|
K9010
Impact Copolymer PP RESIN
Injection Molding Grade
|
Automotive parts
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 50 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 8.5 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 220 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 10000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-78 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 9 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 83 | 0℉，4mm，Notched | kJ/m² |
| 490 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 22 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Strength |
ISO 178 | 0 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | | 980 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-78 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact strength, Good fluidity
|
|
|
K9017
Impact Copolymer PP RESIN
Injection Molding Grade
|
Automotive parts
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 45 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 8.3 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 210 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 9000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-76 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 98 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.3 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 17 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 81 | 0℉，4mm，Notched | kJ/m² |
| 441 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 21 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 882 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-76 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 98 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.3 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact strength, Good fluidity, Anti-UV added,
|
|
|
KP03B
Impact Copolymer PP RESIN
Injection Molding Grade
|
Automotive parts, Storage boxes, Thin wall products |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 5 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 3.7 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 260 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >100 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 13500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-94 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 115 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 30 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 0 | 23 ℃，4mm，Unnotched | kJ/m² |
| 36 | 0℉，4mm，Notched | kJ/m² |
| 49 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 25 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >100 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1323 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-94 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 115 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High fluidity, Good impact strength
|
|
|