AC2300
|
Auto parts, household appliances, 3C electronic products and household goods casings such as wheel covers, handles, Portable storage device
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
| 7 | 240℃ × 5kg | g/10 min |
|
| 17 | 260℃ × 5kg | g/10 min |
|
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
|
|
|
|
| 60 | 23 ℃ | kg-cm/cm |
|
|
|
|
| Specific Gravity |
ASTM D-792 | |
| 1.14 | 23 ℃ | g/cm3 |
| Tensile Strength |
ASTM D-638 | |
| 560 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 920 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 23000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-116 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
|
|
| 112 | Unannealed 6.4mm, 1.8 MPa | ℃ |
|
|
| Molding Shrinkage |
ASTM D-955 | |
| 0.4 ~
0.6 | Flow dir.料流方向 | % |
|
| Flammability |
UL-94 | 1.5mm HB | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Metal plating
|
|
|
|
AC2300
|
Auto parts, household appliances, 3C electronic products and household goods casings such as wheel covers, handles, Portable storage device
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
| 37 | 240℃ × 5kg | g/10 min |
| 27 | 260℃ × 2.16kg | g/10 min |
|
|
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
|
|
|
|
| 45 | 23 ℃ | kg-cm/cm |
| 15 | -30 ℃ | kg-cm/cm |
|
|
|
| Specific Gravity |
ASTM D-792 | |
| 1.18 | 23 ℃ | g/cm3 |
| Tensile Elongation |
ASTM D-638 | | 600 | 23 ℃ | kg/cm2 |
| Flexural Strength |
ASTM D-790 | |
| 1000 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 26000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-117 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
|
|
| 87 | Unannealed 6.4mm, 1.8 MPa | ℃ |
|
|
| Molding Shrinkage |
ASTM D-955 | |
| 0.4 ~
0.6 | Flow dir.料流方向 | % |
|
| Flammability |
UL-94 | 1.5mm V-0
1.5mm 5V-B | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Metal plating
|
|
|
|
AC2300
|
Auto parts, household appliances, 3C electronic products and household goods casings such as wheel covers, handles, Portable storage device
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
| 25 | 240℃ × 5kg | g/10 min |
|
|
|
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
|
|
|
|
| 60 | 23 ℃ | kg-cm/cm |
| -- | -30 ℃ | kg-cm/cm |
|
|
|
| Specific Gravity |
ASTM D-792 | |
| 1.18 | 23 ℃ | g/cm3 |
| Tensile Strength |
ASTM D-638 | |
| 600 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 1000 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 25000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-116 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
|
|
| 88 | Unannealed 6.4mm, 1.8 MPa | ℃ |
|
|
| Molding Shrinkage |
ASTM D-955 | |
| 0.4 ~
0.6 | Flow dir.料流方向 | % |
|
| Flammability |
UL-94 | 1.5mm V0 | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Metal plating
|
|
|
|
AC2300
|
Auto parts, household appliances, 3C electronic products and household goods casings such as wheel covers, handles, Portable storage device
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
| 9 | 240℃ × 5kg | g/10 min |
|
| 21 | 260℃ × 5kg | g/10 min |
|
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
|
|
|
|
| 50 | 23 ℃ | kg-cm/cm |
|
|
|
|
| Specific Gravity |
ASTM D-792 | 1.08 | 23℃ | - |
|
|
| Tensile Strength |
ASTM D-638 | |
| 480 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 840 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 23000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-107 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
|
|
| 95 | Unannealed 6.4mm, 1.8 MPa | ℃ |
|
|
| Molding Shrinkage |
ASTM D-955 | | 0.4 ~
0.6 | - | % |
|
|
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
| 27 | 260℃ × 2.16kg | g/10 min |
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
| 510 | 23 ℃ 3.2mm | J/m |
|
|
|
|
| Charpy Impact Strength |
ISO 179 | |
| 35 | 23 ℃ 4mm | kJ/m² |
|
| Tensile Strength |
ISO 527 | | 47 | 23 ℃ | Mpa |
|
| Flexural Strength |
ISO 178 | | 82 | 23 ℃ | Mpa |
| Flexural Modulus |
ISO 178 | | 2250 | 23 ℃ | Mpa |
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
| 84 | Unannealed 18.6 kg/cm² (1.8MPa)(6.4mm) | ℃ |
|
|
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Metal plating
|
|
|
IV1900R(<380 nm cut)
PC RESIN
Weatherability Grade
|
IV-R grade is listed in AMECA, can used for car headlamp, lighting equipment and various outdoor applications. |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(ISO 1133):19
Charpy (ISO 179-1):70 kJ/m2
FM(ISO 179):2.3 GPa
TS(ISO 527-1,2):65 MPa
UV-stabilized PC with UV cut-off under 380 nm, iced-clear color, and good mold release property.
|
|
|
LC1500
PC RESIN
Light Guide Grade
|
For light guide panel and daytime running light. |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(ISO 1133):65
Charpy (ISO 179-1):15 kJ/m2
FM(ISO 179):2.3 GPa
TS(ISO 527-1,2):65 MPa
Light-conduct PC with high flow and low-level contamination.
|
|
|
AG10NP-N
ABS RESIN
Extrusion Grade
|
MI(220℃×10kg):6
Izod (ASTM,1/4"):47
FM(ASTM):18000
TS(ASTM):355
Extrusion products,Crash helmets,Pipes, Shoe heels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Extrusion molding, Super high impact, High rigid |
|
|
AC2000
PC/ABS Alloy
General Grade
|
Auto parts, household appliances, 3C electronic products and houseware shells such as tail lights, cameras, helmets, tablet PC
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
| 7.0 | 240℃ × 5kg | g/10 min |
| 17 | 260℃ × 2.16kg | g/10 min |
|
|
| IZOD Impact Strength |
ASTM D-256 | |
|
| 65 | 23℃, 3.2mm, Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.14 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | |
| 600 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 960 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 24000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-116 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | |
|
| 136 | VICAT(10N ℃) | ℃ |
|
| Heat Deflection Temperature |
ASTM D-648 | |
| 112 | Unannealed 18.6 kg/cm² (1.8Mpa)(6.4mm) | ℃ |
|
|
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.6 | 3.2mm | % |
|
|
|
| Flammability |
UL-94 | 1.5-1.65mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
| 7 | 240℃ × 5kg | g/10 min |
|
| 17 | 260℃ × 5kg | g/10 min |
|
|
| Charpy Impact Strength |
ISO 179 | |
| 55 | 23 ℃ 4mm | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 1.14 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | | 59 | 23 ℃ | Mpa |
|
| Flexural Strength |
ISO 178 | | 94 | 23 ℃ | Mpa |
| Flexural Modulus |
ISO 178 | | 2350 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-116 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | |
|
| 136 | VICAT(10N ℃) | ℃ |
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
| 0 | Unannealed 18.6 kg/cm² (1.8MPa)(6.4mm) | ℃ |
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.6 | 3.2mm | % |
| Symbol |
ISO 1043 | >PC+ABS< | - | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact
|
|
|
|
AG100H
|
Helmets,
Shoe heels,
Pipe fittings,
Products of low-temp usage
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 8 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 41 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | | 370 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 620 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 19000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-95 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 95 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 93 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 83 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 8 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 40 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | 1.04 | 23℃ | - |
|
| Tensile Strength |
ISO 527 | 38 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 55 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1800 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-95 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 95 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 87 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Super high impact
|
|
|
IV2200R(<380 nm cut)
PC RESIN
Weatherability Grade
|
IV-R grade is listed in AMECA, can used for car headlamp, lighting equipment and various outdoor applications. |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(ISO 1133):11
Charpy (ISO 179-1):80 kJ/m2
FM(ISO 179):2.3 GPa
TS(ISO 527-1,2):65 MPa
UV-stabilized PC with UV cut-off under 380 nm, iced-clear color, and good mold release property. |
|
|
AC2916
PC RESIN
High Transparency Grade
|
Light guide bar,
Daytime running lights for car lamp,
LED condenser lens.
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | 35 | 300℃×1.2kg | g/10 min |
|
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | |
|
| 60 | 23℃, 3.2mm, Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | 1.2 | 23℃ | - |
|
|
| Tensile Strength |
ASTM D-638 | | 650 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | | 1200 | 23 ℃, 2mm/min | kg/cm² |
|
|
| Flexural Modulus |
ASTM D-790 | | 24000 | 23 ℃, 2mm/min | kg/cm² |
|
|
| Rockwell Hardness |
ASTM D-785 | R-123 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | 126 | Unannealed, 18.6kg/cm², 3.2mm, 120℃/h | ℃ |
|
|
|
|
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | | 0.5 ~
0.7 | - | % |
|
|
| Transmissin |
ASTM D-1003 | > 90 | 3.2mm | % |
| Haze |
ASTM D-1003 | < 0.5 | 3.2mm | % |
| Flammability |
UL94 / UL746B / UL746C | 1.0mm V2
RTI 80℃
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
v-2 1 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | | 35 | 300℃ × 1.2kg | g/10 min |
|
|
|
|
|
|
| Charpy Impact Strength |
ISO 179 | 55 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | 1.2 | 23℃ | - |
|
| Tensile Strength |
ISO 527 | 65 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 118 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2350 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-123 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
|
| 126 | Unannealed, 1.8Mpa, 4mm, 120℃/h | ℃ |
|
|
|
|
| Molding Shrinkage |
ISO 2577 | 0.5 ~
0.7 | - | % |
|
| Transmissin |
ISO 13468/1 | > 90 | 3.2mm | % |
| Haze |
ISO 14782 | < 0.5 | 3.2mm | % |
| Combustibility |
UL-94 |
v-2 1 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High Transparency, High flow
|
|
|
|
WG1800
|
Fans of air-conditioner,
Housings of motorbike,
Outside applications |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 19 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 18 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 430 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 710 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 21000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
| 86 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 18 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 23 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 40 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 57 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1900 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-100 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 90 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Weather resistance is excellent,
Color stable, Suitable for outdoor use
|
|
|
AG23AT
ABS RESIN
Metal Plating Grade
|
Wheel cover, Knobs, Tags,Door handle, Plating products
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 22 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 2.3 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 32 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 440 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 740 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 23000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-106 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 86 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 2 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 20 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 33 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | 1.04 | 23℃ | - |
|
| Tensile Strength |
ISO 527 | 44 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 62 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2000 | 23 ℃，2mm/min | Mpa |
|
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 93 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact,Electro plating
|
|
|
AC2300
PC/ABS Alloy
General Grade
|
Auto parts, household appliances, 3C electronic products and household goods casings such as wheel covers, handles, Portable storage device
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
| 9.0 | 240℃ × 5kg | g/10 min |
|
| 21 | 260℃ × 5kg | g/10 min |
|
| IZOD Impact Strength |
ASTM D-256 | |
|
| 55 | 23℃, 3.2mm, Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.08 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | |
| 510 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 880 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 24000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-110 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | |
|
| 117 | VICAT(10N ℃) | ℃ |
|
| Heat Deflection Temperature |
ASTM D-648 | |
| 96 | Unannealed 18.6 kg/cm² (1.8Mpa)(6.4mm) | ℃ |
|
|
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.6 | 3.2mm | % |
|
|
|
| Flammability |
UL-94 | 1.5-1.65mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
| 9 | 240℃ × 5kg | g/10 min |
|
| 21 | 260℃ × 5kg | g/10 min |
|
|
| IZOD Impact Strength |
ISO 180 | |
|
| 540 | 23 ℃ 3.2mm | J/m |
|
|
|
|
| Charpy Impact Strength |
ISO 179 | |
| 40 | 23 ℃ 4mm | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 1.08 | 23℃/23℃ | - |
| Flexural Strength |
ISO 178 | | 86 | 23 ℃ | Mpa |
| Flexural Modulus |
ISO 178 | | 2350 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-110 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | |
|
| 117 | VICAT(10N ℃) | ℃ |
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
| 0 | Unannealed 18.6 kg/cm² (1.8MPa)(6.4mm) | ℃ |
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.6 | 3.2mm | % |
| Symbol |
ISO 1043 | >ABS+PC< | - | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Metal plating
|
|
|
AC25BM
PC/ABS Alloy
Extrusion Grade
|
Spoiler |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Extrusion & Blow Molding
MI(260℃×5kg):3.3
Izod(ASTM,1/8"):60
FM(ASTM):20000
TS(ASTM):550
|
|
|
|
WF3301
|
Fans of air-conditioner,
Parts of car,
Outside pipes
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 26 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 20 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 410 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 670 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 21000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-96 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 89 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
| 83 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 30 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 24 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 38 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 53 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1700 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-96 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 89 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Weather resistance is excellent,
Color stable, Suitable for outdoor use
|
|
|
AG26AT
ABS RESIN
Metal Plating Grade
|
Parts of cars, Tags, Door handle of refrigirator,
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact,High flow, Metal plating
|
|
|
AC3250
PC/ABS Alloy
Self Extinguishing Grade
|
Notebook casings,
3C products,
Electrical equipment,
Dashboard
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
| 25 | 240℃ × 5kg | g/10 min |
| 12 | 260℃ × 2.16kg | g/10 min |
|
|
| IZOD Impact Strength |
ASTM D-256 | |
|
| 6.5 | 23℃, 3.2mm, Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.3 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | |
| 640 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 1110 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 41600 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-115 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | |
|
| 103 | VICAT(10N ℃) | ℃ |
|
| Heat Deflection Temperature |
ASTM D-648 | |
| 89 | Unannealed 18.6 kg/cm² (1.8Mpa)(6.4mm) | ℃ |
|
|
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.3 ~
0.5 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
v-0 1.2 ~ 3 mm
5VA 3 mm
5VB 2 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
| 25 | 240℃ × 5kg | g/10 min |
| 12 | 260℃ × 2.16kg | g/10 min |
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
| 64 | 23 ℃ 3.2mm | J/m |
|
|
|
|
| Charpy Impact Strength |
ISO 179 | |
| 5 | 23 ℃ 4mm | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 1.3 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | | 640 | 23 ℃ | Mpa |
|
| Flexural Strength |
ISO 178 | | 1110 | 23 ℃ | Mpa |
| Flexural Modulus |
ISO 178 | | 41600 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-115 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | |
|
| 103 | VICAT(10N ℃) | ℃ |
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
| 0 | Unannealed 18.6 kg/cm² (1.8MPa)(6.4mm) | ℃ |
|
|
| Molding Shrinkage |
ISO 2577 | | 0.3 ~
0.5 | 3.2mm | % |
| Symbol |
ISO 1043 | >PC+ABS-MD15-FR(40)< | - | - |
| Combustibility |
UL-94 |
v-0 1.2 ~ 3 mm
5VA 3 mm
5VB 2 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Flame retardant,
Halogen free
|
|
|
AC2500
PC/ABS Alloy
General Grade
|
Auto parts, household appliances, 3C electronic products,instrument panel.
grill ,bathroom accessories, electrical control knobs
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
| 8.0 | 240℃ × 5kg | g/10 min |
|
| 19 | 260℃ × 5kg | g/10 min |
|
| IZOD Impact Strength |
ASTM D-256 | |
|
| 60 | 23℃, 3.2mm, Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.12 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | |
| 550 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 950 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 25000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-114 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | |
|
| 130 | VICAT(10N ℃) | ℃ |
|
| Heat Deflection Temperature |
ASTM D-648 | |
| 106 | Unannealed 18.6 kg/cm² (1.8Mpa)(6.4mm) | ℃ |
|
|
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.6 | 3.2mm | % |
|
|
|
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
| 8 | 240℃ × 5kg | g/10 min |
|
| 19 | 260℃ × 5kg | g/10 min |
|
|
| IZOD Impact Strength |
ISO 180 | |
|
| 585 | 23 ℃ 3.2mm | J/m |
|
|
|
|
| Charpy Impact Strength |
ISO 179 | |
| 50 | 23 ℃ 4mm | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 1.12 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | | 54 | 23 ℃ | Mpa |
|
| Flexural Strength |
ISO 178 | | 93 | 23 ℃ | Mpa |
| Flexural Modulus |
ISO 178 | | 2450 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-114 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | |
|
| 130 | VICAT(10N ℃) | ℃ |
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
| 0 | Unannealed 18.6 kg/cm² (1.8MPa)(6.4mm) | ℃ |
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.6 | 3.2mm | % |
| Symbol |
ISO 1043 | >PC+ABS< | - | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Heat resistant
|
|
|
K3029
Impact Copolymer PP RESIN
Injection Molding Grade
|
Bumper, Automotive parts, Thin wall products |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 15 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 7 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 210 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >100 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 10000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-75 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 108 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 32 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 69 | 0℉，4mm，Notched | kJ/m² |
| 147 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 21 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >100 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 980 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-75 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 108 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High fluidity, High impact strength
|
|
|
AE8000-H
ABS RESIN
Extrusion Grade
|
Extrusion products,Crash helmets,Pipes, Shoe heels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 6.0 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 45 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | 1.04 | 23℃ | - |
|
|
| Tensile Strength |
ASTM D-638 | | 440 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 740 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 22000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-103 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 87 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(220℃×10kg):5.4
Izod (ASTM,1/4"):42
FM(ASTM):21000
TS(ASTM):434
Extrusion molding, Super high impact, High rigid |
|
|
|
AF3535
|
Housing of stereos, Large toys, Chairs, Motorcycles, OA machines |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 40 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 4.2 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 23 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 440 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 750 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 23000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-105 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 94 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 86 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Combustibility |
UL-94 |
HB 0.8 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 4.2 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 40 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 26 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 42 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 56 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1700 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-105 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 92 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 0.8 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High flow,High impact
|
|
|
AF3560
ABS RESIN
High Flow Grade
|
Housing of stereos, Large toys, Chairs, Motorcycles, OA machines |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 53 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 5.2 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 12 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 460 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 790 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 24000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-109 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 84 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 5.2 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 53 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 14 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Tensile Strength |
ISO 527 | 43 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 58 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1700 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-109 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 91 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High flow,High impact
|
|
|
AF3500
ABS RESIN
High Flow Grade
|
Housing of stereos, Large toys, Chairs, Motorcycles, OA machines |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 47 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 5.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 32 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 390 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 670 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 20000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-102 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 92 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 94 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 83 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 5 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 47 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 31 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 38 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 50 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1500 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-102 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 92 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High flow,High impact
|
|
|
AX4300
ABS RESIN
Heat Resistant Grade
|
Parts of cars, Electrical appliances, Hair dryer, Heat resistant parts |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 4.0 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 29 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 450 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 780 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 22000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-106 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 99 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 104 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 94 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.3 ~
0.6 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 4 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 28 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 42 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 62 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2000 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-106 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 99 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 96 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.3 ~
0.6 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Medium high heat, Extrusion blow molding |
|
|
AX4100
ABS RESIN
Heat Resistant Grade
|
Parts of cars, Electrical appliances, Hair dryer, Heat resistant parts |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 4.5 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 15 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 400 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 740 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 24000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-110 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 106 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 112 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 102 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.3 ~
0.6 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 4.5 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 16 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 38 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 61 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2100 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-110 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 106 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 102 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.3 ~
0.6 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Super high heat |
|
|
AX4000
ABS RESIN
Heat Resistant Grade
|
Parts of cars, Electrical appliances, Hair dryer, Heat resistant parts |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 9.0 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 20 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 420 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 770 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 24000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-109 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 100 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 104 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 93 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.3 ~
0.6 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 9 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 21 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 41 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 63 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2100 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-109 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 100 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 96 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.3 ~
0.6 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Medium high heat |
|
|
AG10NP
ABS RESIN
Extrusion Grade
|
Extrusion products,Crash helmets,Pipes, Shoe heels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 5.5 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 44 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 430 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 730 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 22000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-102 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 98 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 88 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 ~ 1.76 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 5.5 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 45 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 42 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 58 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1900 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-102 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 93 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.6 ~ 1.76 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Extrusion molding, Super high impact, High rigid |
|
|
AE8000
ABS RESIN
Extrusion Grade
|
Extrusion products,Crash helmets,Pipes, Shoe heels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 4.5 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 45 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 440 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 740 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 22000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-103 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 87 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 4.5 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 47 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 42 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 51 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1500 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-103 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 92 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Extrusion molding, Super high impact, High rigid |
|
|
AG10AP
ABS RESIN
Extrusion Grade
|
Extrusion products,Crash helmets,Pipes, Shoe heels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 4.0 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 51 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 370 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 640 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 19000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-93 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 91 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 94 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 84 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 4 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 50 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 37 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 46 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1500 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-93 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 91 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 92 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Extrusion molding, Super high impact, High rigid |
|
|
AG23AT
ABS RESIN
Metal Plating Grade
|
Wheel cover, Knobs, Tags,Door handle, Plating products
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 20 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 2.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 32 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 440 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Modulus |
ASTM D-790 | 23000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-106 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 86 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 2 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 20 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 33 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 44 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 62 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2000 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-106 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 93 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact,Electro plating
|
|
|
K7009AH
Impact Copolymer PP RESIN
Injection Molding Grade
|
Electric appliance parts, Automotive parts,RTI=125℃ |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 11 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 4.6 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 260 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 13500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-94 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 120 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 9 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 45 | 0℉，4mm，Notched | kJ/m² |
| 108 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 25 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1323 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-94 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 120 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Long term thermal aging, High stiffness, Good impact strength
|
|
|
K8009
Impact Copolymer PP RESIN
Injection Molding Grade
|
Automotive parts, Battery case,Electrical appliances, Furniture
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 40 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 7.4 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 230 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-80 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 9 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 73 | 0℉，4mm，Notched | kJ/m² |
| 392 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 22 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1078 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-80 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact strength, Good fluidity
|
|
|
|
K8009
|
Automotive parts, Battery case,Electrical appliances, Furniture
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 9 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 40 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 7.4 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 230 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-80 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 9 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 73 | 0℉，4mm，Notched | kJ/m² |
| 392 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 22 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1078 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-80 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact strength, Good fluidity
|
|
|
K8025
Impact Copolymer PP RESIN
Injection Molding Grade
|
Automotive parts, Washing machine parts, Tool boxes,
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 25 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 12.5 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 6.2 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 230 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-80 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 28 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 61 | 0℉，4mm，Notched | kJ/m² |
| 123 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 22 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1078 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-80 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact strength, High fluidity
|
|
|
|
K8025
|
Automotive parts, Washing machine parts, Tool boxes,
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 25 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 12.5 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 6.2 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 230 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Rockwell Hardness |
ASTM D-785 | R-80 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | |
|
| 1.4 ~
1.8 | 23℃ | ％ |
| Flammability |
UL-94 | HB 1.5 mm | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 28 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 61 | 0℉，4mm，Notched | kJ/m² |
| 123 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 22 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1078 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-80 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact strength, High fluidity
|
|
|
K8802
Impact Copolymer PP RESIN
Injection Molding Grade
|
Suitcase Parts |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 70 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 10 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 270 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-80 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 105 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
1.9 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 2 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 98 | 0℉，4mm，Notched | kJ/m² |
| 686 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 26 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1078 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-80 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 105 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.5 ~
1.9 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Hight impact strength,
Excellent resistance to low temp. Brittleness,
Good luster
|
|
|
K9010
Impact Copolymer PP RESIN
Injection Molding Grade
|
Automotive parts
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 9.0 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 50 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 8.5 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 220 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 10000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-78 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 9 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 83 | 0℉，4mm，Notched | kJ/m² |
| 490 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 22 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Strength |
ISO 178 | 0 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | | 980 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-78 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact strength, Good fluidity
|
|
|
K9017
Impact Copolymer PP RESIN
Injection Molding Grade
|
Automotive parts
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 17 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 45 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 8.3 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 210 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 9000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-76 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 98 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.3 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 17 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 81 | 0℉，4mm，Notched | kJ/m² |
| 441 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 21 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 882 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-76 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 98 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.3 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact strength, Good fluidity, Anti-UV added,
|
|
|
KP03B
Impact Copolymer PP RESIN
Injection Molding Grade
|
Automotive parts, Storage boxes, Thin wall products |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 5 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 3.7 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 260 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >100 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 13500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-94 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 115 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 30 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 0 | 23 ℃，4mm，Unnotched | kJ/m² |
| 36 | 0℉，4mm，Notched | kJ/m² |
| 49 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 25 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >100 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1323 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-94 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 115 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High fluidity, Good impact strength
|
|
|