HP823R
|
Housing for electrical appliances, TV housing,Monitor housing, PC housing
s
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 7.5 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 9.0 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Density |
ASTM D-792 | 1.03-1.05 | 23 ℃ | g/cm3 |
| Tensile Strength |
ASTM D-638 | |
| 220 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 400 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 21000 | 23 ℃ | kg/cm² |
|
| Vicat Softening Point |
ASTM D-1525 | |
|
|
| 97 | Annealed，10N， 50℃/h | ℃ |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
|
|
|
| 89 | 1.8 MPa, 1/8”bar Unannealed | ℃ |
|
| Molding Shrinkage |
ASTM D-955 | |
|
| 0.46 ~
0.6 | 23℃ | ％ |
| Relative Temp Index |
UL746B | 50 | Elec | ℃ |
| 50 | Imp | ℃ |
| 50 | Str | ℃ |
| Combustibility |
UL-94 |
HB 1.5 ~ 2.99 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 ~ 2.99 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High flow |
|
|
|
HP828R
|
Housing for electrical appliances, TV housing,Monitor housing, PC housing
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 6.5 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 7.00 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Density |
ASTM D-792 | 1.03-1.05 | 23 ℃ | g/cm3 |
| Tensile Strength |
ASTM D-638 | |
| 210 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 370 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 18000 | 23 ℃ | kg/cm² |
|
| Vicat Softening Point |
ASTM D-1525 | |
|
|
| 100 | Annealed，10N， 50℃/h | ℃ |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
|
|
|
| 88 | 1.8 MPa, 1/8”bar Unannealed | ℃ |
|
| Molding Shrinkage |
ASTM D-955 | |
|
| 0.4 ~
0.6 | 23℃ | ％ |
| Relative Temp Index |
UL746B | 50 | Elec | ℃ |
| 50 | Imp | ℃ |
| 50 | Str | ℃ |
| Combustibility |
UL-94 |
HB 1.5 ~ 2.99 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 ~ 2.99 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High flow |
|
|
|
HP8250
|
Housing for electrical appliances, TV housing,Monitor housing, PC housing
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 7.2 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 8.5 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Density |
ASTM D-792 | 1.03-1.05 | 23 ℃ | g/cm3 |
| Tensile Strength |
ASTM D-638 | |
| 215 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 380 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 20000 | 23 ℃ | kg/cm² |
|
| Vicat Softening Point |
ASTM D-1525 | |
|
|
| 96 | Annealed，10N， 50℃/h | ℃ |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
|
|
|
| 88 | 1.8 MPa, 1/8”bar Unannealed | ℃ |
|
| Molding Shrinkage |
ASTM D-955 | |
|
| 0.4 ~
0.6 | 23℃ | ％ |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High flow |
|
|
HP835G
PS RESIN
High Impact Grade
|
Housing for electrical appliances, Baby car parts,Housings of LCD Monitor,Exercise appliances
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 3.7 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 11 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 280 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 22000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 55 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 550 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 23000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 101 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 89 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Combustibility |
UL-94 |
HB 1 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 3.7 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 10.8 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 8 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 28 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 2400 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 38 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 54 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2300 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 101 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 94 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact, Normal flow |
|
|
HQ2200
PC RESIN
Clean grade (Film grade)
|
For high-quality film/sheet of LCD or other printing applications. |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(ISO 1133):11
Charpy (ISO 179-1):80 kJ/m2
FM(ISO 179):2.3 GPa
TS(ISO 527-1,2):65 MPa
Clean PC with low-level contamination.
|
|
|
AG15AB
ABS RESIN
Jet Black General Grade
|
Black purpose parts, LED-TV housing,All-in-one PC housing
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 22 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 2.2 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 19 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 470 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 830 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 25000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-109 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 96 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 86 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 2.4 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 24 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 21 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 47 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 69 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-109 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 96 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 94 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Jet black, High gloss |
|
|
|
HP825S
|
Fridge liner, Door liner of fridge |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(200℃×5kg):2.7
Izod (ASTM,1/4"):10
FM(ASTM):15000
TS(ASTM):240
Environmental stress cracking resistance, extrusion with |
|
|
|
HP825G
|
Housing electronics (Air- Conditioner) Housing |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(200℃×5kg):3.5
Izod (ASTM,1/4"):11
FM(ASTM):20000
TS(ASTM):300
High Gloss, High impact |
|
|
|
NX3200
|
Blade of fan, Batteries housing |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 15 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 1.5 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | <2 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.06 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 800 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 1200 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 37000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | M-79 | 23℃ | M-scale |
| Vicat Softening Point |
ASTM D-1525 | 102 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
| 96 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 1.5 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 15 | 220℃ × 10kg | g/10 min |
| CHARPY IMPACT STRENGTH |
ISO 179 | <2 | 23℃, 4mm, Notched | kJ/m2 |
| Specific Gravity |
ISO 1183 | | 1.06 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 82 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 118 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3600 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-79 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 102 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 103 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High heat,
Chemical resistance |
|
|
|
NF2100
|
Cassettes, Trash cans, Toothbrush handles, Lamp covers, Pen tube,
Cup with cover, Cosmetic cases |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| <2 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.06 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | |
| 700 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 35000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | M-78 | 23℃ | M-scale |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 5 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 50 | 220℃ × 10kg | g/10 min |
| CHARPY IMPACT STRENGTH |
ISO 179 | <2 | 23℃, 4mm, Notched | kJ/m2 |
| Specific Gravity |
ISO 1183 | | 1.06 | 23℃/23℃ | - |
| Flexural Strength |
ISO 178 | | 118 | 23 ℃ | Mpa |
| Flexural Modulus |
ISO 178 | | 69 | 23 ℃ | Mpa |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(220℃×10kg):50
Izod (ASTM,1/4"):1.5
FM(ASTM):35000
TS(ASTM):700
High flow,
Injection grade |
|
|
AC3100
PC/ABS Alloy
Self Extinguishing Grade
|
Household appliances, 3C electronic products, notebook computers,
Netcom products, computer peripheral products
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 25 | 230℃ × 2.16kg | g/10 min |
| 17 | 240℃ × 5kg | g/10 min |
|
|
|
| IZOD Impact Strength |
ASTM D-256 | |
|
| 65 | 23℃, 3.2mm, Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.18 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | |
| 650 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 1000 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 25000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-118 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | |
|
| 107 | VICAT(10N ℃) | ℃ |
|
| Heat Deflection Temperature |
ASTM D-648 | |
| 90 | Unannealed 18.6 kg/cm² (1.8Mpa)(6.4mm) | ℃ |
|
|
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.6 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
v-0 1 ~ 3 mm
5VA 3 mm
5VB 2.3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
| 25 | 240℃ × 5kg | g/10 min |
| 17 | 260℃ × 2.16kg | g/10 min |
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
| 635 | 23 ℃ 3.2mm | J/m |
|
|
|
|
| Charpy Impact Strength |
ISO 179 | |
| 44 | 23 ℃ 4mm | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 1.18 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | | 60 | 23 ℃ | Mpa |
|
| Flexural Strength |
ISO 178 | | 94 | 23 ℃ | Mpa |
| Flexural Modulus |
ISO 178 | | 2438 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-118 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | |
|
| 107 | VICAT(10N ℃) | ℃ |
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
| 0 | Unannealed 18.6 kg/cm² (1.8MPa)(6.4mm) | ℃ |
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.6 | 3.2mm | % |
| Symbol |
ISO 1043 | >PC+ABS-FR(40)< | - | - |
| Combustibility |
UL-94 |
v-0 1 ~ 3 mm
5VA 3 mm
5VB 2.3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Flame retardant,
Halogen free
|
|
|
K1011
Homopolymer PP RESIN
Injection Molding Grade
|
General purpose, Foodcontainers, Electrical appliances, Housewares meets the requirements of USP Plastic Class VI
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 15 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 2.8 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 2.8 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 350 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 14500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 15 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 27 | 23 ℃，1/8"，Notched | kJ/m² |
| 27 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 34 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1421 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-100 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Good stiffness,
Good luster
|
|
|
|
HP8250
|
Housing for electrical appliances, Baby car parts,Housings of LCD Monitor,Exercise appliances
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 5.5 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 13 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 240 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 22000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 53 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 450 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 23000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 101 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 89 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 0.8mm HB
1.0mm HB
1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 0.8 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 5.5 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 11 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 8.5 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 24 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 2200 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 33 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 41 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2200 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 98 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 96 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 0.8 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact, Normal flow |
|
|
GP5000
PS RESIN
General Purpose Grade
|
TRP blending, Thin sheet injection
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 10 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 1.6 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 410 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 33000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 780 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 31000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 94 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 83 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 10 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 8.7 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 42 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3400 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 72 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3000 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 94 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 89 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High flow Injection molding |
|
|
|
AG100H
|
Helmets,
Shoe heels,
Pipe fittings,
Products of low-temp usage
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 8 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 41 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | | 370 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 620 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 19000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-95 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 95 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 93 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 83 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 8 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 40 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | 1.04 | 23℃ | - |
|
| Tensile Strength |
ISO 527 | 38 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 55 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1800 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-95 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 95 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 87 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Super high impact
|
|
|
|
A1900
|
For injection molding or compounding. |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(ISO 1133):19
Charpy (ISO 179-1):70 kJ/m2
FM(ISO 179):2.3 GPa
TS(ISO 527-1,2):65 MPa
Basic PC with natural color。 |
|
|
HP8250
PS RESIN
High Impact Grade
|
Housing for electrical appliances, Baby car parts,Housings of LCD Monitor,Exercise appliances
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 5.5 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 13 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 240 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 22000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 53 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 450 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 21000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 101 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 89 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 0.8mm HB
1.0mm HB
1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 5.5 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 11 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 8.5 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 24 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 2200 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 33 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 41 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2200 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 98 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 96 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact, Normal flow |
|
|
|
AG15E1
|
Toys, Calculators, Phone,Clock housing,Stereo housing, Suitcase
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 25 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 2.4 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 19 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 480 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 840 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 26000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-111 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 95 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 86 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 2.4 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 25 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 16 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Tensile Strength |
ISO 527 | 46 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 70 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2500 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-111 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 95 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 91 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.6 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High gloss,
High rigid
|
|
|
|
WG1800
|
Fans of air-conditioner,
Housings of motorbike,
Outside applications |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 19 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 18 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 430 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 710 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 21000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
| 86 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 18 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 23 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 40 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 57 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1900 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-100 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 90 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Weather resistance is excellent,
Color stable, Suitable for outdoor use
|
|
|
ANC160
ABS RESIN
Self Extinguishing Grade
|
Flame retardant materials;Housing of LCD monitor, LCD-TVcomputers & OA machine
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
v-0 2.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
v-0 2.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(200℃×5kg):4.3
Izod (ASTM,1/4"):28
FM(ASTM):21000
TS(ASTM):396
Flame retardant |
|
|
|
GP560N
|
TV & illumination diffusion plate |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(200℃×5kg):1.9
Izod (ASTM,1/4"):1.8
FM(ASTM):32000
TS(ASTM):510
High transparency, High heat, Extrusion |
|
|
|
NX3400
|
Blade of fan,
Batteries housing |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 10 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 1.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | <2 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.06 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 820 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 1200 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 37000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | M-79 | 23℃ | M-scale |
| Vicat Softening Point |
ASTM D-1525 | 102 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
| 97 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Flammability |
UL-94 | 1.6-1.8mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.6 ~ 1.8 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 1 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 10 | 220℃ × 10kg | g/10 min |
| CHARPY IMPACT STRENGTH |
ISO 179 | <2 | 23℃, 4mm, Notched | kJ/m2 |
| Specific Gravity |
ISO 1183 | | 1.06 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 83 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 121 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3600 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-79 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 102 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 104 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.6 ~ 1.8 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High heat,
Chemical resistance |
|
|
|
NF2200
|
Trash cans,
Toothbrush handles,
Lamp covers, Pen tube,
Cup with cover,
Cosmetic cases
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 29 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 2.9 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | <2 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.06 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 720 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 1200 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 35000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | M-78 | 23℃ | M-scale |
| Vicat Softening Point |
ASTM D-1525 | 101 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
| 94 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Flammability |
UL-94 | 1.5mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 2.9 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 29 | 220℃ × 10kg | g/10 min |
| CHARPY IMPACT STRENGTH |
ISO 179 | <2 | 23℃, 4mm, Notched | kJ/m2 |
| Specific Gravity |
ISO 1183 | | 1.06 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 73 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 117 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3600 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-78 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 101 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 102 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High flow , Injection grade |
|
|
IR1700
PC RESIN
General Purpose Grade
|
Relay cases, Timer cases, Packs, Decorative lighting covers, Cups and
glasses, Dishes, Electrical equipment, Safety lamps, Explosion-proof gloves,
Contact lens cases.
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(ISO 1133):26
Charpy (ISO 179-1):40 kJ/m2
FM(ISO 179):2.3 GPa
TS(ISO 527-1,2):65 MPa
Viscosity:Lowest
1. Highest impact strength among plastics
2. High transparency
3. Wide usable temperature rang
4. Excellent dimensional accuracy and stability
5. Excellent electrical properties
6. Meets UL standard
|
|
|
GP5250
PS RESIN
General Purpose Grade
|
Food containers, Stationery, Toys, Clothing hangers, Lamp decoration, CD, Cosmetic cases
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 6.7 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 1.7 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 430 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 31000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 850 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 31000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 95 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 86 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 6.7 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 7.4 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 41 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3300 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 70 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3200 | 23 ℃，2mm/min | Mpa |
|
| Vicat Softening Point |
ISO 306 | |
| 95 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 91 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Injection molding
|
|
|
|
AG15E3
|
Toys, Calculators, Phone,Clock housing,Stereo housing, Suitcase
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 18 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 1.6 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 18 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | 0 | 23℃ | - |
|
|
| Tensile Strength |
ASTM D-638 | | 500 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 860 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 26000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-111 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 95 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 85 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 1.6 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 18 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 18 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Tensile Strength |
ISO 527 | 49 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 72 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2500 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-111 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High gloss, High rigid |
|
|
|
AG15A3
|
Toys, Calculators, Phone,Clock housing,Stereo housing, Suitcase
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 22 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 2.2 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 24 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 470 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 820 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 25000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-109 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 95 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 85 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1 ~ 1.65 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 2.2 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 22 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 26 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 41 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 60 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1 ~ 1.65 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High gloss, Medium impact |
|
|
|
AG15A1-H
|
Toys, Calculators, Phone,Clock housing,Stereo housing, Suitcase
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 21 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 2.2 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 24 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 460 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 810 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 26000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-110 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 95 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 85 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Combustibility |
UL-94 |
HB 1 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 2.2 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 21 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 23 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 45 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 68 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-110 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High gloss, Medium impact |
|
|
|
AG12A3
|
Shoe heels, Toys, Clock housing,
Stereo housing, Suitcase,
The plate-like products
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 18 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 1.6 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 32 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 430 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 730 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 23000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-106 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 94 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 84 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 1.6 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 18 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 31 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 44 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 64 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2200 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-106 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 88 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact |
|
|
|
AG12A0
|
Helmets,
Shoe heels,
Pipe fittings,
Products of low-temp usage
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 19 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 1.6 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 30 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 420 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 740 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 24000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-105 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 95 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 94 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 84 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 1.6 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 19 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 30 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 44 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 66 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2300 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-105 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Super high impact |
|
|
|
AG12A1-H
|
Shoe heels, Toys, Clock housing,Stereo housing, Suitcase, The plate-like products |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(220℃×10kg):21
Izod (ASTM,1/4"):30
FM(ASTM):23000
TS(ASTM):420
High impact, High gloss
|
|
|
|
A2200
|
for injection molding or compounding. |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(ISO 1133):11
Charpy (ISO 179-1):80 kJ/m2
FM(ISO 179):2.3 GPa
TS(ISO 527-1,2):65 MPa
Basic PC with natural color。 |
|
|
HP825F
PS RESIN
High Impact Grade
|
Housing for electrical appliances, Baby car parts,Housings of LCD Monitor,Exercise appliances
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 9.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 12 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 250 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 24000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 45 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 460 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 23000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 100 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 90 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 9 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 10 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 9.6 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 26 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 2300 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 33 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 46 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 99 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 96 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High flow |
|
|
ANC180
ABS RESIN
Self Extinguishing Grade
|
Flame retardant materials;Housing of LCD monitor, LCD-TVcomputers & OA machine
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
v-0 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
v-0 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(200℃×5kg):5.4
Izod (ASTM,1/4"):16
FM(ASTM):22000
TS(ASTM):424
Flame retardant |
|
|
AG15AJ
ABS RESIN
Jet Black General Grade
|
Black purpose parts, LED-TV housing,All-in-one PC housing
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 220℃ × 10kg | g/10 min |
|
|
|
|
| 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 23 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 440 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 770 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 25000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-108 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 95 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
|
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 2.4 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 25 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 24 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 44 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 66 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2300 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-108 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 95 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 92 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Jet black |
|
|
|
WF3301
|
Fans of air-conditioner,
Parts of car,
Outside pipes
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 26 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 20 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 410 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 670 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 21000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-96 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 89 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
| 83 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 30 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 24 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 38 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 53 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1700 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-96 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 89 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Weather resistance is excellent,
Color stable, Suitable for outdoor use
|
|
|
GP535N
PS RESIN
General Purpose Grade
|
Kitchen ware, Lamp covers, Decorated sheets, Toys |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 3.5 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 1.8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 450 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 32000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 890 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 32000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 98 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 93 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 4.5 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 10.8 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 44 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3300 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 76 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3100 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 100 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 95 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Heat resistance |
|
|
IR1900
PC RESIN
General Purpose Grade
|
Relay cases, Timer cases, Packs, Decorative lighting covers, Cups and
glasses, Dishes, Electrical equipment, Safety lamps, Explosion-proof gloves,
Contact lens cases.
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(ISO 1133):19
Charpy (ISO 179-1):70 kJ/m2
FM(ISO 179):2.3 GPa
TS(ISO 527-1,2):65 MPa
Viscosity:Low
1. Highest impact strength among plastics
2. High transparency
3. Wide usable temperature rang
4. Excellent dimensional accuracy and stability
5. Excellent electrical properties
6. Meets UL standard |
|
|
|
HP9450
|
HP sheets, Disposable dishware,Electronic Packaging, Cable reels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 3.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 15 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 250 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 22000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 52 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 470 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 22000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 100 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 90 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 3 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 12.2 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 9.8 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 25 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 2200 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 39 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 44 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 99 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 94 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Super high impact |
|
|
GP525N
PS RESIN
General Purpose Grade
|
Food containers, Stationery, Toys, Clothing hangers, Lamp decoration, CD, Cosmetic cases
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 6.7 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 430 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 31000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 870 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 31000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 95 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 87 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 6.7 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 7.4 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 41 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3300 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 70 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3200 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 7000 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 95 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 91 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Injection molding
|
|
|
AF3538
ABS RESIN
Jet Black General Grade
|
Housing of stereos, Large toys, Chairs, Motorcycles, OA machines, Black purpose parts, LED-TV housing,All-in-one PC housing |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(220℃×10kg):35
Izod (ASTM,1/4"):18
FM(ASTM):23000
TS(ASTM):440
Black purpose parts, LED-TV housing,All-in-one PC housing, monitor shell, computer chassis main panel, Sound shell
|
|
|
AG15AB
ABS RESIN
Jet Black General Grade
|
Black purpose parts, LED-TV housing,All-in-one PC housing
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 220℃ × 10kg | g/10 min |
|
|
|
|
| 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 19 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
| 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 470 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 830 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 25000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-109 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 96 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 86 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 2.4 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 24 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 21 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 47 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 69 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-109 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 96 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 94 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Jet black, High gloss |
|
|
AG12AJ
ABS RESIN
Jet Black General Grade
|
Black purpose parts, LED-TV housing,All-in-one PC housing
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 220℃ × 10kg | g/10 min |
|
|
|
|
| 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 34 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 400 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 680 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 21000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-103 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 95 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 84 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.6 ~ 1.76 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 1.9 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 20 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 34 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 40 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 58 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2000 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-103 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 95 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 91 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.6 ~ 1.76 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Jet black |
|
|
|
AG15A1-H
|
Toys, Caculators, Phone, Clock housing, Stereo housing, Suitcase
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 22 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 2.2 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 24 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 460 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 810 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 26000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-110 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 95 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 85 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Combustibility |
UL-94 |
HB 1 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 2.2 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 21 | 220℃ × 10kg | g/10 min |
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 45 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 68 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-110 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 94 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High gloss,
Medium impact
|
|
|
AC3830
PC RESIN
Self Extinguishing Grade
|
Diffusion board, Diffusion lamp, Diffusion injection lampshade, Diffusion injection-blow bulb |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | 12 | 300℃×1.2kg | g/10 min |
|
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | |
|
| 5 | 23℃, 3.2mm, Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | 1.2 | 23℃ | - |
|
|
| Tensile Strength |
ASTM D-638 | | 710 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | | 1100 | 23 ℃, 2mm/min | kg/cm² |
|
|
| Flexural Modulus |
ASTM D-790 | | 22000 | 23 ℃, 2mm/min | kg/cm² |
|
|
| Rockwell Hardness |
ASTM D-785 | R-122 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | 128 | Unannealed, 18.6kg/cm², 3.2mm, 120℃/h | ℃ |
|
|
|
|
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | | 0.5 ~
0.7 | - | % |
|
|
| Transmissin |
ASTM D-1003 | 90~60 | 3.2mm | % |
| Haze |
ASTM D-1003 | 91~40 | 3.2mm | % |
| Flammability |
UL94 / UL746B / UL746C | 1.0mm V0
3.0mm 5VA
RTI 130℃, f1
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
v-0 1 mm
5VA 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | | 12 | 300℃ × 1.2kg | g/10 min |
|
|
|
|
|
|
| Charpy Impact Strength |
ISO 179 | |
|
| 70 | 23℃, 4mm, Notched | kJ/m² |
| Specific Gravity |
ISO 1183 | 1.2 | 23℃ | - |
|
| Tensile Strength |
ISO 527 | 70 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 108 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2155 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-122 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
|
| 128 | Unannealed, 1.8Mpa, 4mm, 120℃/h | ℃ |
|
|
|
|
| Molding Shrinkage |
ISO 2577 | 0.5 ~
0.7 | - | % |
|
| Transmissin |
ISO 13468/1 | 90~60 | 3.2mm | % |
| Haze |
ISO 14782 | 91~40 | 3.2mm | % |
| Combustibility |
UL-94 |
v-0 1 mm
5VA 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Light diffusion, Mid flow,
UV resistance, Halogen free
|
|
|
HP9450
PS RESIN
High Impact Grade
|
HP sheets, Disposable dishware,Electronic Packaging, Cable reels
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 3.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 15 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 250 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 22000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 52 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 470 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 22000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 100 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 90 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 3 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 12.2 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Tensile Strength |
ISO 527 | |
| 25 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 2200 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 39 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 44 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 99 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 94 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Super high impact |
|
|
AC3250
PC/ABS Alloy
Self Extinguishing Grade
|
Notebook casings,
3C products,
Electrical equipment,
Dashboard
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
| 25 | 240℃ × 5kg | g/10 min |
| 12 | 260℃ × 2.16kg | g/10 min |
|
|
| IZOD Impact Strength |
ASTM D-256 | |
|
| 6.5 | 23℃, 3.2mm, Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.3 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | |
| 640 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 1110 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 41600 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-115 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | |
|
| 103 | VICAT(10N ℃) | ℃ |
|
| Heat Deflection Temperature |
ASTM D-648 | |
| 89 | Unannealed 18.6 kg/cm² (1.8Mpa)(6.4mm) | ℃ |
|
|
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.3 ~
0.5 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
v-0 1.2 ~ 3 mm
5VA 3 mm
5VB 2 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
| 25 | 240℃ × 5kg | g/10 min |
| 12 | 260℃ × 2.16kg | g/10 min |
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
| 64 | 23 ℃ 3.2mm | J/m |
|
|
|
|
| Charpy Impact Strength |
ISO 179 | |
| 5 | 23 ℃ 4mm | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 1.3 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | | 640 | 23 ℃ | Mpa |
|
| Flexural Strength |
ISO 178 | | 1110 | 23 ℃ | Mpa |
| Flexural Modulus |
ISO 178 | | 41600 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-115 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | |
|
| 103 | VICAT(10N ℃) | ℃ |
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
| 0 | Unannealed 18.6 kg/cm² (1.8MPa)(6.4mm) | ℃ |
|
|
| Molding Shrinkage |
ISO 2577 | | 0.3 ~
0.5 | 3.2mm | % |
| Symbol |
ISO 1043 | >PC+ABS-MD15-FR(40)< | - | - |
| Combustibility |
UL-94 |
v-0 1.2 ~ 3 mm
5VA 3 mm
5VB 2 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Flame retardant,
Halogen free
|
|
|
IR2200
PC RESIN
General Purpose Grade
|
Relay cases, Timer cases, Packs, Decorative lighting covers, Cups and
glasses, Dishes, Electrical equipment, Safety lamps, Explosion-proof gloves,
Contact lens cases.
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(ISO 1133):11
Charpy (ISO 179-1):80 kJ/m2
FM(ISO 179):2.3 GPa
TS(ISO 527-1,2):65 MPa
Viscosity:Medium
1. Highest impact strength among plastics
2. High transparency
3. Wide usable temperature rang
4. Excellent dimensional accuracy
and stability
5. Excellent electrical properties
6. Meets UL
standard
|
|
|
|
MP6500
|
Stationery, Toys,Parts for home electrical appliances, Clothing hangers, Clock housing, FRP blending
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 3.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 290 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 24000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 40 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 560 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 25000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 100 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 91 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 7 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 5.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 5.8 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 30 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 2600 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 27 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 51 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 98 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 94 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Medium impact |
|
|
|
AF3535
|
Housing of stereos, Large toys, Chairs, Motorcycles, OA machines |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 40 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 4.2 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 23 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 440 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 750 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 23000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-105 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 94 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 86 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Combustibility |
UL-94 |
HB 0.8 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 4.2 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 40 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 26 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 42 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 56 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1700 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-105 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 92 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 0.8 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High flow,High impact
|
|
|
AF3560
ABS RESIN
High Flow Grade
|
Housing of stereos, Large toys, Chairs, Motorcycles, OA machines |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 53 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 5.2 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 12 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 460 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 790 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 24000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-109 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 96 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 84 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 5.2 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 53 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 14 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Tensile Strength |
ISO 527 | 43 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 58 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1700 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-109 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 93 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 91 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High flow,High impact
|
|
|
AF3500
ABS RESIN
High Flow Grade
|
Housing of stereos, Large toys, Chairs, Motorcycles, OA machines |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 47 | 220℃ × 10kg | g/10 min |
|
|
|
|
| 5.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 32 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.04 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 390 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 670 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 20000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-102 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 92 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 94 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 83 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.4 ~
0.7 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 5 | 200℃ × 5kg | g/10 min |
|
|
|
|
| 47 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 31 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.04 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 38 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 50 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 1500 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-102 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 92 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 90 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.4 ~
0.7 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High flow,High impact
|
|
|
MP6500
PS RESIN
High Impact Grade
|
Stationery, Toys,Parts for home electrical appliances, Clothing hangers, Clock housing, FRP blending
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 7.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 290 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 24000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 40 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 560 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 23000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 100 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 91 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 7 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 5.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 5.8 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 30 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 2600 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 27 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 51 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2400 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 98 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 94 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Medium impact |
|
|
IR2500
PC RESIN
General Purpose Grade
|
Relay cases, Timer cases, Packs, Decorative lighting covers, Cups and
glasses, Dishes, Electrical equipment, Safety lamps, Explosion-proof gloves,
Contact lens cases.
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
MI(ISO 1133):7
Charpy (ISO 179-1):80 kJ/m2
FM(ISO 179):2.2 GPa
TS(ISO 527-1,2):65 MPa
Viscosity:High
1. Highest impact strength among plastics
2. High transparency
3. Wide usable temperature rang
4. Excellent dimensional accuracy
and stability
5. Excellent electrical properties
6. Meets UL
standard
|
|
|
GP535A
PS RESIN
General Purpose Grade
|
Kitchen ware, Lamp covers, Decorated sheets, Toys |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 4.3 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | |
|
|
|
| 1.8 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
| Tensile Strength |
ASTM D-638 | 480 | 23 ℃，5mm/min | kg/cm² |
|
|
|
| Tensile Modulus |
ASTM D-638 | 32000 | 23 ℃，1mm/min | kg/cm² |
| Tensile Elongation |
ASTM D-638 | 2 | 23 ℃，5mm/min | % |
|
| Flexural Strength |
ASTM D-790 | |
|
| 930 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | |
|
| 31000 | 23 ℃，1.2mm/min | kg/cm² |
| Vicat Softening Point |
ASTM D-1525 | |
| 96 | Annealed 80℃*2hr 1/8" ，10N 50℃/h | ℃ |
|
|
| Reidual Monomer |
| 700 | - | ppm max |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
|
| 89 | Annealed 80℃*2hr，120℃/h 1.8Mpa 1/8" | ℃ |
|
|
|
|
| Flammability |
UL-94 | 1.5-1.7mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | 4.3 | 200℃ × 5kg 49N | g/10min |
|
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
|
| 1.6 | 23 ℃，4mm，Unnotched | kJ/m² |
|
|
|
| Charpy Impact Strength |
ISO 179 | | 7.2 | 23℃，4mm GPPS無缺口，HIPS有缺口 | kJ/m² |
|
|
| Tensile Strength |
ISO 527 | |
| 43 | 23 ℃，20mm/min | Mpa |
| Tensile Modulus |
ISO 527 | 3300 | 23 ℃，1mm/min | Mpa |
| Tensile Elongation |
ISO 527 | 3 | 23 ℃，20mm/min | % |
| Flexural Strength |
ISO 178 | 74 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 3100 | 23 ℃，2mm/min | Mpa |
|
| Reidual Monomer |
| 700 | - | ppm max |
| Vicat Softening Point |
ISO 306 | |
| 98 | Annealed 80℃*2hr， 4mm，10N 50℃/h | ℃ |
|
| Heat Deflection Temperature |
ISO 75/A | |
|
|
|
|
| 94 | Annealed 80℃*2hr，120℃/h，1.8Mpa 4mm | ℃ |
|
| Combustibility |
UL-94 |
HB 1.5 ~ 1.7 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High heat resistance |
|
|
AX4300
ABS RESIN
Heat Resistant Grade
|
Parts of cars, Electrical appliances, Hair dryer, Heat resistant parts |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 4.0 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 29 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 450 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 780 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 22000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-106 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 99 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 104 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 94 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.3 ~
0.6 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 4 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 28 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 42 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 62 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2000 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-106 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 99 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 96 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.3 ~
0.6 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Medium high heat, Extrusion blow molding |
|
|
AX4100
ABS RESIN
Heat Resistant Grade
|
Parts of cars, Electrical appliances, Hair dryer, Heat resistant parts |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 4.5 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 15 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 400 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 740 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 24000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-110 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 106 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 112 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 102 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.3 ~
0.6 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 4.5 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 16 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 38 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 61 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2100 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-110 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 106 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 102 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.3 ~
0.6 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Super high heat |
|
|
AX4000
ABS RESIN
Heat Resistant Grade
|
Parts of cars, Electrical appliances, Hair dryer, Heat resistant parts |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | | 9.0 | 220℃ × 10kg | g/10 min |
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | 20 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.05 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 420 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 770 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 24000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-109 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 100 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 104 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 93 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.3 ~
0.6 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
|
| 9 | 220℃ × 10kg | g/10 min |
| Charpy Impact Strength |
ISO 179 | 21 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.05 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 41 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 63 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2100 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-109 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 100 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 96 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.3 ~
0.6 | 3.2mm | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Medium high heat |
|
|
K1108
Homopolymer PP RESIN
Injection Molding Grade
|
General purpose, Foodcontainers, Electrical appliances, Housewares
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 10 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 3 | 23 ℃，1/8"，Notched | kg-cm/cm |
| 3 | 23 ℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 360 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 15000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 115 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 10 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | | 29 | 23 ℃，1/8"，Notched | kJ/m² |
| 29 | 23 ℃，4mm，Notched | kJ/m² |
|
|
|
|
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 35 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1470 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-100 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 115 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Good stiffness, Good luster
|
|
|
ANC120
ABS RESIN
Self Extinguishing Grade
|
Flame retardant materials;Housing of LCD monitor, LCD-TVcomputers & OA machine
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 5.5 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 26 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.19 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 400 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 690 | 23 ℃，15mm/min | kg/cm² |
|
|
| 0 | 23 ℃，1.2mm/min | kg/cm² |
| Flexural Modulus |
ASTM D-790 | 23000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-100 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 83 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 84 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 74 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Combustibility |
UL-94 |
v-0 2.3 ~ 3 mm
5VB 2.3 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 5.5 | 200℃ × 5kg | g/10 min |
|
|
|
|
|
| Charpy Impact Strength |
ISO 179 | 18 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.19 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 39 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 59 | 23 ℃，2mm/min | Mpa |
|
| Flexural Modulus |
ISO 178 | 2000 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-100 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 83 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 79 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.3 ~
0.6 | 3.2mm | % |
| Combustibility |
UL-94 |
v-0 2.3 ~ 3 mm
5VB 2.3 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Flame retardant |
|
|
ANC100
ABS RESIN
Heat Resistant Grade
|
Flame retardant materials;Housing of LCD monitor, LCD-TV,computers & OA machine
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
|
|
|
|
| 6.0 | 200℃ × 5kg | g/10 min |
| IZOD Impact Strength |
ASTM D-256 | 22 | 23 ℃，1/4"，Notched | kg-cm/cm |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | 0 | 23℃ | - |
|
|
| Tensile Strength |
ASTM D-638 | | 420 | 23 ℃，50mm/min | kg/cm² |
|
|
| Flexural Strength |
ASTM D-790 | 720 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Flexural Modulus |
ASTM D-790 | 24000 | 23 ℃，15mm/min | kg/cm² |
|
|
|
| Rockwell Hardness |
ASTM D-785 | R-101 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | 80 | Annealed，50N，50℃/h | ℃ |
|
|
|
|
| Heat Deflection Temperature |
ASTM D-648 | |
|
| 90 | Annealed，1.8Mpa 1/4"厚，120℃/h | ℃ |
| 76 | Unannealed，1.8Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.3 ~
0.6 | 3.2mm | % |
|
|
|
| Combustibility |
UL-94 |
v-0 1.5 ~ 3 mm
5VA 2.3 ~ 2.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
| 6 | 200℃ × 5kg | g/10 min |
|
|
|
|
|
| Charpy Impact Strength |
ISO 179 | 17 | 23 ℃，4mm厚，Notched | kJ/m² |
|
|
|
| Specific Gravity |
ISO 1183 | | 1.21 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 40 | 23 ℃，50mm/min | Mpa |
|
|
| Flexural Strength |
ISO 178 | 59 | 23 ℃，2mm/min | Mpa |
| 0 | 23 ℃ | Mpa |
| Flexural Modulus |
ISO 178 | 2000 | 23 ℃，2mm/min | Mpa |
|
| Rockwell Hardness |
ISO 2039-2 | R-101 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | 80 | Annealed，50N，50℃/h | ℃ |
|
|
|
| Heat Deflection Temperature |
ISO 75/A | | 76 | Annealed，1.8Mpa 4mm厚，120℃/h | ℃ |
|
|
|
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.3 ~
0.6 | 3.2mm | % |
| Combustibility |
UL-94 |
v-0 1.5 ~ 3 mm
5VA 2.3 ~ 2.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Flame retardant |
|
|
K7009AH
Impact Copolymer PP RESIN
Injection Molding Grade
|
Electric appliance parts, Automotive parts,RTI=125℃ |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 11 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 4.6 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 260 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 13500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-94 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 120 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 9 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 45 | 0℉，4mm，Notched | kJ/m² |
| 108 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 25 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1323 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-94 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 120 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Long term thermal aging, High stiffness, Good impact strength
|
|
|
K7025
Impact Copolymer PP RESIN
Injection Molding Grade
|
Washing machine cylinder, Appliances |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 8 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 4.5 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 270 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 14000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-93 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 120 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
3.0mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 27 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 44 | 0℉，4mm，Notched | kJ/m² |
| 78 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 26 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1372 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-93 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 120 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High fluidity, High impact strength,
|
|
|
K8009
Impact Copolymer PP RESIN
Injection Molding Grade
|
Automotive parts, Battery case,Electrical appliances, Furniture
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 40 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 7.4 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 230 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-80 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 9 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 73 | 0℉，4mm，Notched | kJ/m² |
| 392 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 22 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1078 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-80 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact strength, Good fluidity
|
|
|
|
K8009
|
Automotive parts, Battery case,Electrical appliances, Furniture
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 9 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 40 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 7.4 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 230 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-80 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 9 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 73 | 0℉，4mm，Notched | kJ/m² |
| 392 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 22 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1078 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-80 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact strength, Good fluidity
|
|
|
K8025
Impact Copolymer PP RESIN
Injection Molding Grade
|
Automotive parts, Washing machine parts, Tool boxes,
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 25 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 12.5 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 6.2 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 230 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 11000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-80 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 28 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 61 | 0℉，4mm，Notched | kJ/m² |
| 123 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 22 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1078 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-80 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact strength, High fluidity
|
|
|
|
K8025
|
Automotive parts, Washing machine parts, Tool boxes,
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 25 | 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 12.5 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 6.2 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 230 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >200 | 23 ℃，50mm/min | % |
|
| Rockwell Hardness |
ASTM D-785 | R-80 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 110 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | |
|
| 1.4 ~
1.8 | 23℃ | ％ |
| Flammability |
UL-94 | HB 1.5 mm | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 28 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 61 | 0℉，4mm，Notched | kJ/m² |
| 123 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 22 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >200 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1078 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-80 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 110 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Combustibility |
UL-94 |
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High impact strength, High fluidity
|
|
|
K8050
Impact Copolymer PP RESIN
Injection Molding Grade
|
Washing machine,Storage boxes,Thin wall products
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | |
| 230℃ × 2.16kg | g/10 min |
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | | 10 | 23 ℃，1/8"，Notched | kg-cm/cm |
|
|
|
|
| 5 | -20℃，4mm，Notched | kg-cm/cm |
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 0.9 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | | 240 | 23 ℃，50mm/min | kg/cm² |
|
|
| Tensile Elongation at break |
ASTM D-638 | >100 | 23 ℃，50mm/min | % |
|
| Flexural Modulus |
ASTM D-790 | |
| 12500 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-85 | 23 ℃ | R-scale |
| Heat Deflection Temperature |
ASTM D-648 | |
|
|
|
| 115 | Unannealed，1/4" bar | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Flammability |
UL-94 | 1.5-1.65mm HB
All Color | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | |
|
|
|
|
| 50 | 230℃ × 2.16kg | g/10 min |
|
| IZOD Impact Strength |
ISO 180 | |
|
|
|
| 49 | 0℉，4mm，Notched | kJ/m² |
| 98 | 73℉，1/8"，Notched | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 0.9 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | 23 | 23 ℃，50mm/min | Mpa |
|
|
| Tensile Elongation at break |
ISO 527 | >100 | 23 ℃，50mm/min | % |
| Flexural Modulus |
ISO 178 | | 1225 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-85 | 23℃ | R-scale |
| Heat Deflection Temperature |
ISO 75/A | |
| 115 | Unannealed，0.455Mpa 1/4" 厚，120℃/h | ℃ |
|
|
|
|
|
| Molding Shrinkage |
FCFC Method | 1.4 ~
1.8 | 23 ℃ | % |
| Combustibility |
UL-94 |
HB 1.5 ~ 1.65 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
High fluidity, Good impact strength, High Stiffness,Low warpage
|
|
|
AC3900
PC RESIN
Self Extinguishing Grade
|
Home lighting, electronics
touch panel module
internal accessories such as LED lamp cap, lamp holder, panel white frame
|
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ASTM D-1238 | 26 | 300℃×1.2kg | g/10 min |
|
|
|
|
|
|
| IZOD Impact Strength |
ASTM D-256 | |
|
|
| 60 | 23 ℃ 3.2mm | kg-cm/cm |
|
|
|
|
|
|
|
|
|
| Specific Gravity |
ASTM D-792 | | 1.28 | 23℃/23℃ | - |
|
| Tensile Strength |
ASTM D-638 | |
| 610 | 23 ℃ | kg/cm² |
|
| Flexural Strength |
ASTM D-790 | |
| 1060 | 23 ℃ | kg/cm² |
|
| Flexural Modulus |
ASTM D-790 | |
| 24000 | 23 ℃ | kg/cm² |
|
| Rockwell Hardness |
ASTM D-785 | R-121 | 23 ℃ | R-scale |
| Vicat Softening Point |
ASTM D-1525 | |
|
| 146 | VICAT(10N ℃) | ℃ |
|
| Heat Deflection Temperature |
ASTM D-648 | | 124 | Unannealed 18.6 kg/cm² (1.8MPa)(3.2mm) | ℃ |
|
|
|
|
|
|
|
|
|
| Molding Shrinkage |
ASTM D-955 | 0.5 ~
0.7 | 3.2mm | % |
|
|
|
| Flammability |
UL-94 | 1.5mm V-0
3.0mm V-0
NC | FILE NO. E162823 | - |
| Combustibility |
UL-94 |
v-0 1.5 ~ 3 mm
|
File No. E162823 |
- |
| Property |
Test Method |
Value |
Test Condition |
Unit |
| Melt Flow Index |
ISO 1133 | | 26 | 300℃ × 1.2kg | g/10 min |
|
|
|
|
|
|
| IZOD Impact Strength |
ISO 180 | |
|
| 585 | 23 ℃ 3.2mm | J/m |
|
|
|
|
| Charpy Impact Strength |
ISO 179 | |
| 45 | 23 ℃ 4mm | kJ/m² |
|
| Specific Gravity |
ISO 1183 | | 1.28 | 23℃/23℃ | - |
| Tensile Strength |
ISO 527 | | 60 | 23 ℃ | Mpa |
|
| Flexural Strength |
ISO 178 | | 104 | 23 ℃ | Mpa |
| Flexural Modulus |
ISO 178 | | 2350 | 23 ℃ | Mpa |
| Rockwell Hardness |
ISO 2039-2 | R-121 | 23℃ | R-scale |
| Vicat Softening Point |
ISO 306 | |
|
| 146 | VICAT(10N ℃) | ℃ |
| Heat Deflection Temperature |
ISO 75/A | |
|
|
| 124 | Unannealed 18.6 kg/cm² (1.8MPa)(3.2mm) | ℃ |
|
|
|
| Molding Shrinkage |
ISO 2577 | | 0.5 ~
0.7 | 3.2mm | % |
| Symbol |
ISO 1043 | >PC< | - | - |
| Combustibility |
UL-94 |
v-0 1.5 ~ 3 mm
|
File No. E162823 |
- |
To print, please click on the attached standard physical properties table.
|
Halogen free,
Flame retardant,
White color,
Non-transparency,
High gloss reflection
|
|
|